Acoustic building material employing chitosan
A cast ceiling tile and method for manufacture incorporates chitosan in an amount sufficient to provide improved strength.
1. A cast ceiling tile formed from an aqueous slurry of ingredients including fiber, filler, binder and chitosan in addition to said binder, said ingredients being homogenously dispersed throughout the aqueous slurry for interacting of the chitosan with the other of said slurry ingredients whereby the cast ceiling tile formed of the aqueous slurry is structurally reinforced by the chitosan as compared with an identically formed ceiling tile of the same slurry ingredients except for the chitosan, said fiber comprising mineral wool, said filler comprising at least one component of perlite, calcium carbonate, clay and stucco, and said binder comprising at least one component of starch and latex.
2. The cast ceiling tile of claim 1 , wherein said chitosan interacts with said ingredients to provide the ceiling tile with increased physical properties including MOR (modulus of rupture) as compared with a ceiling tile identically formed of the same slurry ingredients except for the chitosan.
3. The cast ceiling tile of claim 1 , wherein the chitosan is present in an amount from about 0.5 wt % to about 10 wt % based on the total weight of the solids in the aqueous slurry.
4. The cast ceiling tile of claim 1 , wherein the chitosan is dissolved in acid solution for addition to the slurry.
5. The cast ceiling tile of claim 1 , wherein the slurry includes a reduced amount of binder in accordance with the amount of added chitosan to maintain physical properties and an amount of a recycled cellulose fiber material in accordance with the reduced amount of a binder whereby the postindustrial/postconsumer content of the tile is increased and structural reinforcement is maintained.
6. The ceiling tile of claim 5 , wherein the physical properties include MOR (modulus of rupture) and hardness.
7. The cast ceiling tile of claim 1 , wherein said chitosan tends to improve the mold resistance of the ceiling tile.
8. The cast ceiling tile of claim 1 , wherein said ceiling tile has a composition including on a solids content weight basis:
fiber from about 60% to about 80%,
filler from about 15% to about 70%,
binder from about 3% to about 12%, and
chitosan from about 0.5% to about 10%.
9. A method for making a ceiling tile in a cast process comprising forming an aqueous slurry of ingredients including mineral fiber, filler, binder comprising starch or latex and chitosan in addition to said binder, homogenously dispersing said chitosan in said aqueous slurry, dewatering and drying said slurry to form said acoustical material, said chitosan interacting with the slurry ingredients to structurally reinforce the resulting tile as compared with a cast tile identically formed of the same ingredients except for the chitosan.
10. The method of claim 9 , wherein the chitosan is dissolved in acid solution and then added to the slurry.
11. The method of claim 10 , wherein said chitosan interacts with said ingredients to provide said cast tile with increased MOR (modulus of rupture) and hardness as compared with a cast tile identically formed of the same ingredients except for the chitosan.
12. The method of claim 9 , wherein the chitosan is present in an amount from about 0.5 wt % to about 10 wt % based on the total weight of the solids in the aqueous slurry, and the slurry includes a reduced amount of binder in accordance with the amount of added chitosan to maintain physical properties and an amount of a recycled cellulose fiber material in accordance with the reduced amount of binder whereby the postindustrial/postconsumer content of the building material is increased and structural reinforcement is maintained.