Powder coating composition useful as a finish
A chemical resistant powder coating composition comprising a urethane-polyester powder coating resin, a styrene-free hydroxyl functional acrylic resin, and a hardener. The composition may contain a flow aid that is a combination of a polyester hydroxyl resin, polyethylene resin, and spherical glass flakes and having introduced silica type carriers.
1. A chemical resistant powder coating composition comprising:
a urethane-polyester powder coating resin;
a styrene-free hydroxyl functional acrylic resin;
a hardener or a curative; and
glass flakes;
wherein, upon curing, the chemical resistant powder coating composition has a gloss of less than 2.0 at an angle of 85 degrees.
2. The powder coating of claim 1 wherein the urethane-polyester resin is a thermosetting powder urethane polyester resin having hydroxyl or carboxyl functionality.
3. The powder coating of claim 2 wherein the hardener is selected from the group consisting of tetramethoxy glycoluril, a blocked cycloaliphatic polyisocyanate, triglycidylisocyanurate, an imidazole adduct, aliphatic and cycloaliphatic amine curing agent, a phenolic hardener, and mixtures thereof.
4. The powder coating of claim 2 wherein the urethane-polyester resin is present in an amount of about 45 to 90 parts by weight and the styrene-free hydroxyl functional acrylic resin is present in an amount of about 3 to 10 parts by weight relative to the polyester-urethane.
5. The powder coating composition of claim 1 wherein the composition additionally includes a flow aid.
6. The powder coating composition of claim 1 wherein the composition additionally includes a thermosetting powder coating resin.
7. The powder coating of claim 6 wherein the thermosetting powder coating resin is selected from the group consisting of epoxy, epoxy-polyester, and TGIC-free polyester resins.
8. A chemical resistant powder coating composition comprising a composition shown in the following table:
Amounts
(wt.%)
Constituents Control Component
(approx.)
Styrene-free hydroxyl functional acrylic
3.1-9.5
Polyester urethane powder binder
44-90
Polymeric curative
25-45
Degassing agent
.25-2.0
Flow additive
.5-3.0
Glass Flake
20-50
Tin Catayst
0.5-2.0
Precipitated Silica
1.0-3.0.
9. The powder coating composition of claim 8 wherein the coating has the composition shown in the following table:
Amounts
(wt %)
Constituents Control Component
(approx.)
Styrene-free hydroxyl functional acrylic
2.5
Polyester urethane powder binder
81.17
Polymeric curative
31.37
Degassing agent
1.02
Flow additive
1.79
Glass Flake
10.0
Tin Catayst
1.0
Magnesium Ferrite
2.81
Chromite
10.28
Iron Red Oxide
.046
Cinquasia violet L 5120
0.05
Precipitated Silica
1.49
Chrome Green Oxide
14.76.
10. A chemical resistant powder coating composition comprising:
a urethane-polyester powder coating resin present in an amount of about 45 to about 90 parts by weight, the urethane-polyester powder coating resin having hydroxyl or carboxyl functionality;
a styrene-free hydroxyl functional acrylic resin present in an amount of about 3 to about 10 parts by weight relative to the polyester-urethane powder coating resin;
a hardener or a curative; and
glass flakes.
11. The powder coating of claim 10 wherein the hardener is selected from the group consisting of tetramethoxy glycoluril, a blocked cycloaliphatic polyisocyanate, triglycidylisocyanurate, an imidazole adduct, aliphatic and cycloaliphatic amine curing agent, a phenolic hardener, and mixtures thereof.
12. The powder coating of claim 10 wherein the composition additionally includes a flow aid.
13. The powder coating composition of claim 10 wherein the composition additionally includes a thermosetting powder coating resin.
14. The powder coating of claim 10 wherein the thermosetting powder coating resin is selected from the group consisting of epoxy, epoxy-polyester, and TGIC-free polyester resins.