Adhesive tape made of silicone intended for medical applications

1. An adhesive tape ( 1 ) for medical applications, comprising:

a nonwoven sheet material ( 12 ) having an internal face ( 12 a ) and an external face ( 12 b ), the nonwoven sheet material comprising an internal layer ( 13 a ) that carries the internal face ( 12 a ) and an external layer ( 13 b ) that carries the external face ( 12 b ), the external layer ( 13 b ) having a density greater than a density of the internal layer ( 13 a ),

the internal face carrying a barrier membrane ( 14 ) which adheres to the sheet material, the barrier membrane comprising a crosslinked silicone polymer, the barrier membrane carrying an atraumatic and biocompatible silicone adhesive gel layer ( 16 ),

the external face ( 12 b ) carrying a nonstick and waterproof polymer layer ( 18 ) comprising a fluorosilicone or fluorocarbon polymer;

wherein the sheet material ( 12 ) includes a profusion of small folds ( 15 ) in a transverse direction, thereby providing a capacity for elongation under low stress in the longitudinal direction.

2. An adhesive tape ( 1 ) for medical applications, comprising:

a nonwoven sheet material ( 12 ) having an internal face ( 12 a ) and an external face ( 12 b ), the nonwoven sheet material comprising an internal layer ( 13 a ) that carries the internal face ( 12 a ) and an external layer ( 13 b ) that carries the external face ( 12 b ), the external layer ( 13 b ) having a density greater than a density of the internal layer ( 13 a ),

the internal face carrying a barrier membrane ( 14 ) which adheres to the sheet material, the barrier membrane comprising a crosslinked silicone polymer, the barrier membrane carrying an atraumatic and biocompatible silicone adhesive gel layer ( 16 ),

the external face ( 12 b ) carrying a nonstick and waterproof polymer layer ( 18 ) comprising a fluorosilicone or fluorocarbon polymer.

3. The tape of claim 2 , wherein the sheet material ( 12 ) is composed of a mixture of fibers and having a low resistance to tearing and easily tearable by hand, wherein the sheet material includes a mixture of short cellulose fibers and of medium length polyethylene terephthalate (PET) fibers bonded to one another by calendering under hot pressure and/or by a chemical bonding agent.

4. The tape of claim 3 , wherein the sheet material includes a ratio of 10 to 40% of PET for 90 to 60% of cellulose, wherein the sheet material has a weight of 30 to 70 g/m 2 and a thickness of 0.10 to 0.30 mm, wherein the cellulose fibers have a length of the order of 1 mm to 20 mm, and the PET fibers exhibit cylindrical fiber structures with a linear density of between 0.1 dtex and 5 dtex, and with a length of the order of 2 mm to 20 mm.

5. The tape of claim 2 , wherein the tape is perforated with small orifices ( 20 ) to provide high permeability to vapor resulting from the exudation of the skin and to prevent maceration of wet skin.

6. The tape of claim 2 , wherein the sheet of nonwoven fibers is perforated with orifices ( 20 ) with a diameter of 0.05 to 0.5 mm, so as to provide the final material with an appearance of a woven or knitted textile structure, in order to improve the permeability to water vapor resulting from the exudation of the skin, to improve the tearability, and/or to provide the external surface of the material with properties of low friction and of high comfort of wearing, on contact with any textile or item of clothing, and/or in order to provide, for the patient, great comfort of wearing, on contact with a region of the skin capable of deforming, of folding, or of comprising hollow regions and regions possessing relief.

7. The tape of claim 2 , wherein edges ( 5 ) of the tape are cut over their entire length according to a repeating geometrical design ( 6 ) to provide the tape ( 1 ) with an ease of transverse manual tearing (F).

8. The tape of claim 2 , wherein permeability of the water vapor of the layer of the adhesive silicone gel ( 16 ) is between approximately 500 and 2000 g/m 2 /24 h, measured with water according to the inverted cup method (standard EN 13 726-2).

9. The tape of claim 2 , wherein the nonwoven fibers ( 12 ) are dyed, and/or the chemical agent for bonding the fibers is pigmented and coated with a barrier layer of crosslinked silicone and with a layer of an adhesive of crosslinked silicone gel in which the silicone polymers are pigmented.

10. An adhesive tape ( 1 ) for medical applications, comprising:

a nonwoven sheet material ( 12 ) having an internal face ( 12 a ) and an external face ( 12 b ), the nonwoven sheet material comprising an internal layer ( 13 a ) that carries the internal face ( 12 a ) and an external layer ( 13 b ) that carries the external face ( 12 b ), the external layer ( 13 b ) having a density greater than a density of the internal layer ( 13 a ),

the internal face carrying a barrier membrane ( 14 ) which adheres to the sheet material, the barrier membrane comprising a crosslinked silicone polymer, the barrier membrane carrying an atraumatic and biocompatible silicone adhesive gel layer ( 16 ),

the external face ( 12 b ) carrying a nonstick and waterproof polymer layer ( 18 ) comprising a fluorosilicone or fluorocarbon polymer;

wherein the sheet material ( 12 ) is composed of a mixture of fibers and having a low resistance to tearing and easily tearable by hand, wherein the sheet material includes a mixture of short cellulose fibers and of medium length polyethylene terephthalate (PET) fibers bonded to one another by calendering under hot pressure and/or by a chemical bonding agent, wherein the sheet material includes a ratio of 10 to 40% of PET for 90 to 60% of cellulose, wherein the sheet material has a weight of 30 to 70 g/m 2 and a thickness of 0.10 to 0.30 mm, wherein the cellulose fibers have a length of the order of 1 mm to 20 mm, and the PET fibers exhibit cylindrical fiber structures with a linear density of between 0.1 dtex and 5 dtex, and with a length of the order of 2 mm to 20 mm; and

wherein the sheet material ( 12 ) includes a profusion of small folds ( 15 ) in a transverse direction, thereby providing a low elongation stress in the longitudinal direction.

11. The tape of claim 10 , wherein the barrier membrane is a thin continuous barrier membrane or a noncontinuous barrier membrane, and wherein the barrier membrane is made of crosslinked silicone polymer ( 14 ) laminated to the fibers of the internal face ( 12 a ).

12. The tape of claim 11 , wherein the atraumatic and biocompatible silicone adhesive gel layer ( 16 ) is adhered by a copolymerization reaction to the barrier membrane.