Post irradiation shelf-stable dual paste direct injectable bone cement precursor systems and methods of making same
The present invention relates to a bone cement precursor system that is presented in the form of two shelf-stable pastes which have been terminally sterilized and are held in separate containers during product transport and storage. When the product is used during surgery, these pastes inject to a site of application through a static mixing device by the action of applied injection force. When the two pastes are mixed, they start to react to each other while injecting out. The resulting composition is highly biocompatible, osteoconductive, injectable, rapid setting and bioresorbable, and is useful in connection with bone repair procedures, for example, in the craniomaxillofacial, trauma and orthopedic areas.
1. A bone cement precursor system comprising:
a first container containing an acidic aqueous paste comprising monocalcium phosphate monohydrate (MCPM) and dicalcium phosphate anhydrous (DCPA), citric acid, water, glycerol, polyvinyl pyrrolidone (PVP) and polyethylene glycol (PEG), and
a second container containing an alkaline non-aqueous paste comprising at least one basic calcium phosphate mineral, at least one paste stabilizing agent, a surfactant and a solvent.
2. The bone cement precursor system of claim 1 , wherein the mean particle size of said monocalcium phosphate monohydrate (MCPM) and dicalcium phosphate anhydrous (DCPA) is between about 1 μm to about 90 μm.
3. The bone cement precursor system of claim 1 , wherein the amount of said monocalcium phosphate monohydrate (MCPM) and dicalcium phosphate anhydrous (DCPA) present in said acidic aqueous paste is between about 5% w/w to about 65% w/w based on the total weight of said acidic aqueous paste.
4. The bone cement precursor system of claim 2 , wherein the mean particle size of said monocalcium phosphate monohydrate (MCPM) is about 30 μm to about 90 μm.
5. The bone cement precursor system of claim 2 , wherein the mean particle size of said dicalcium phosphate anhydrous (DCPA) is about 1 μm to about 20 μm.
6. The bone cement precursor system of claim 1 , wherein the amount of said polyvinyl pyrrolidone (PVP) and polyethylene glycol (PEG) is 1% w/w and about 10% w/w based on the total weight of said acidic aqueous paste.
7. The bone cement precursor system of claim 1 , wherein the amount of said citric acid present in said acidic aqueous paste is between about 5% w/w and about 8% w/w based on the total weight of said acidic aqueous paste.
8. The bone cement precursor system of claim 1 , wherein the amount of said glycerol present in said acidic aqueous paste is between about 0.5% w/w and about 2% w/w based on the total weight of said acidic aqueous paste.
9. The bone cement precursor system of claim 1 , wherein the amount of said water present in said acidic aqueous paste is between about 15 w/w % to about 25 w/w % based on the total weight of said acidic aqueous paste.
10. The bone cement precursor system of claim 1 , wherein said system further comprises an additive.
11. The bone cement precursor system of claim 10 , wherein said additive is selected from the group consisting of a protein, osteoinductive material, osteoconductive material, x-ray opacifying agent, medicament, supporting or strengthening filler material, crystal growth adjuster, viscosity modifier, pore forming agent, radiopaque filler and mixtures thereof.
12. A calcium phosphate composition produced by mixing said acidic aqueous paste and said alkaline non-aqueous paste of claim 1 .
13. The bone cement precursor system of claim 1 , wherein the mean molecular weight (Mw) of PEG in the acidic aqueous paste is between about 1,000 Mw to about 60,000 Mw.
14. The bone cement precursor system of claim 1 , wherein the mean molecular weight (Mw) of PVP in the acidic aqueous paste is between about 10,000 Mw to about 100,000 Mw.
15. A bone cement precursor system comprising:
a first container containing an acidic aqueous paste comprising at least one acidic calcium phosphate mineral, at least one synthetic polymer-based paste stabilizing agent, a pH buffering agent and a humectant, and
a second container containing an alkaline non-aqueous paste comprising tetracalcium phosphate (TTCP), polyethylene glycol (PEG), polysorbate 80, and propylene glycol.
16. The bone cement precursor system of claim 15 , wherein the mean particle size of TTCP is between about 10 μm to about 60 μm.
17. The bone cement precursor system of claim 15 , wherein the amount of TTCP in said alkaline non-aqueous paste is between about 10 w/w % to about 80 w/w % based on the total weight of said alkaline non-aqueous paste.
18. The bone cement precursor system of claim 15 , wherein said alkaline non-aqueous paste comprises a bimodal mean particle size distribution of the TTCP.
19. The bone cement precursor system of claim 15 , wherein the amount of the PEG present in said alkaline non-aqueous paste is between about 1 w/w % to about 5 w/w % based on the total weight of said alkaline non-aqueous paste.
20. The bone cement precursor system of claim 15 , wherein the amount of the polysorbate 80 in said alkaline non-aqueous paste is between about 0.5 w/w % to about 2 w/w % based on the total weight of said alkaline non-aqueous paste.
21. The bone cement precursor system of claim 15 , wherein the amount of said propylene glycol in said alkaline non-aqueous paste is between about 22 w/w % to about 28 w/w % based on the total weight of said alkaline non-aqueous paste.
22. The bone cement precursor system of claim 15 , wherein said system further comprises an additive.
23. The bone cement precursor system of claim 22 , wherein said additive is selected from the group consisting of a protein, osteoinductive material, osteoconductive material, x-ray opacifying agent, medicament, supporting or strengthening filler material, crystal growth adjuster, viscosity modifier, pore forming agent, radiopaque filler and mixtures thereof.
24. A calcium phosphate composition produced by mixing said acidic aqueous paste and said alkaline non-aqueous paste of claim 15 .
25. The bone cement precursor system of claim 15 , wherein the at least one synthetic polymer-based paste stabilizing agent is polyvinyl pyrrolidone (PVP) and polyethylene glycol (PEG).
26. The bone cement precursor system of claim 25 , wherein the mean molecular weight (Mw) of PEG in the acidic aqueous paste is between about 1,000 Mw to about 60,000 Mw.
27. The bone cement precursor system of claim 25 , wherein the mean molecular weight (Mw) of PVP in the acidic aqueous paste is between about 10,000 Mw to about 100,000 Mw.