Steel pretreatment solution and method for enhanced corrosion and cathodic disbondment resistance
A pretreatment solution and process for pretreating steel substrates with an aqueous solution to form a thin partially crosslinked layer that passivates the steel surface and inhibits the formation of flash rust, in which the thin partially crosslinked layer is dried in ambient air, and the dried layer enhances the cathodic disbondment resistance of the overlying paint system. In the process an aqueous precursor solution (A) containing at least one amino-functional silane, at least one of a dissolved silicate or a dissolved aluminate and at least a metal salt; is mixed with an aqueous precursor solution (B) containing at least an epoxy resin. The molar amount of amino-functional silane in precursor solution (A) is at considerably lower than the stoichiometric amount that is needed for completing the crosslinking reaction with the epoxy resin in precursor solution (B) so that unreacted epoxy groups are made available for further crosslinking with the overlying paint.
1. A pretreatment composition for steel surfaces to improve corrosion resistance, paint adhesion and cathodic disbondment resistance, consisting essentially of: water; at least one amino-functional silane; at least one of a dissolved silicate and a dissolved aluminate; a metal salt; and an epoxy resin dispersed in the form of particles; wherein:
a molar amount of amino-functional silane is at least two times lower than a stoichiometric amount that is needed for completing a crosslinking reaction with the epoxy resin and the concentration of the epoxy resin has a range of 0.25-2.5 wt %.
2. The pretreatment composition of claim 1 wherein the molar amount of amino-functional silane in the composition is at least ten times lower than the stoichiometric amount that is needed for completing the crosslinking reaction with the epoxy resin.
3. The pretreatment composition of claim 1 wherein the amino-functional silane has a general formula of R 1 —R 2 —Si(OR 3 ) 3 where R 1 is an amino functional group, R 2 is an aliphatic or aromatic hydrocarbon group and R 3 is an alkyl group.
4. The pretreatment composition of claim 3 wherein the amino-functional silane is selected from a group consisting of 3-aminopropyltriethoxysilane and N-(2-aminoethyl)-3-aminopropyltrimethoxysilane.
5. The pretreatment composition of claim 1 wherein the concentration of the amino-functional silane in the composition is in a range of 0.005-0.5 wt %.
6. The pretreatment composition of claim 1 wherein the concentration of the amino-functional silane in the composition is in a range of 0.015-0.15 wt %.
7. The pretreatment composition of claim 1 wherein the aluminate is selected from a group consisting of sodium aluminate, potassium aluminate and lithium aluminate.
8. The pretreatment composition of claim 1 wherein the concentration of the dissolved silicate or aluminate in the composition is in a range of 0.0025-0.05 M.
9. The pretreatment composition of claim 1 wherein the metal salt is selected from a group consisting of Ba(NO 3 ) 2 , Ca(NO 3 ) 2 , Sr(NO 3 ) 2 , and Fe(NO 3 ) 3 .
10. The pretreatment composition of claim 1 wherein the concentration of metal salt in the composition is in a range of 0.005-0.05 M.
11. The pretreatment composition of claim 1 wherein the particle size of the epoxy resin has a range of 0.05-20 μm.
12. A method of pretreating steel to improve corrosion resistance, paint adhesion and cathodic disbondment resistance, comprising the steps of:
(1) providing an aqueous precursor composition (A) containing at least one amino-functional silane, at least one of a dissolved silicate or a dissolved aluminate and at least a metal salt;
(2) providing an aqueous precursor composition (B) containing at least an epoxy resin dispersed in the form of particles;
(3) mixing precursor compositions (A) and (B) in a predetermined mixing ratio to make a pretreatment composition such that a molar amount of amino-functional silane in the pretreatment composition is at least two times lower than a stoichiometric amount that is needed for completing a crosslinking reaction with the epoxy resin in the pretreatment composition, the concentration of the epoxy resin in the pretreatment composition having a range of 0.25-2.5 wt %;
(4) wetting a steel surface with the pretreatment composition; and
(5) drying the wetted steel surface to form a partially crosslinked thin-film coating.
13. The method of claim 12 wherein the molar amount of amino-functional silane in the mixed composition is at least ten times lower than the stoichiometric amount that is needed for completing the crosslinking reaction with the epoxy resin in the mixed composition.
14. The method of claim 12 wherein the amino-functional silane in precursor composition (A) has a general formula of R 1 —R 2 —Si(OR 3 ) 3 where R 1 is an amino functional group, R 2 is an aliphatic or aromatic hydrocarbon group and R 3 is an alkyl group.
15. The method of claim 12 wherein the amino-functional silane in precursor composition (A) is selected from a group consisting of 3-aminopropyltriethoxysilane and N-(2-aminoethyl)-3-aminopropyltrimethoxysilane.
16. The method of claim 12 wherein either step (4) or step (5) is carried out at ambient conditions.