Anion binder for solid alkaline fuel cell, method of preparing the same and membrane-electrode assembly
The present invention concerns the preparation of an anion binder for a solid alkaline fuel cell which enhances durability to electrochemical reactions and makes the production of electrode slurry easy. A method of preparing an anion binder for a solid alkaline fuel cell includes: (A) mixing an electrolytic monomer of quaternary ammonium salts having a cation group, a bisacrylicamide crosslinking agent having a tertiary amino group, and water together by stirring; (B) mixing the mixture with a photoinitiator; (C) interposing the solution between polyethylene terephthalate films and irradiating the solution with ultraviolet light for crosslinking and polymerization; and (D) pulverizing crosslinked polymerized resin to a nano size.
1. A method of preparing an anion binder for a solid alkaline fuel cell, the method comprising:
(A) mixing an electrolytic monomer of quaternary ammonium salts having a cation group, a bisacrylicamide crosslinking agent having a tertiary amino group, and water together by stirring;
(B) mixing the mixture with a photoinitiator;
(C) interposing the solution between polyethylene terephthalate films and irradiating the solution with ultraviolet light for crosslinking and polymerization; and
(D) pulverizing crosslinked polymerized resin to a nano size, wherein (D) comprises:
(D1) primarily pulverizing the crosslinked polymerized resin to a size of 40 to 60 μm by a grinding pulverizer; and
(D2) dispersing and secondarily pulverizing the powder obtained in the primary pulverization to a size of 150 to 250 nm by a wet pulverizer.
2. The method of claim 1 , wherein the electrolytic monomer of quaternary ammonium salts having a cation group is vinybenzyl trimethylammonium chloride.
3. The method of claim 1 , wherein the bisacrylicamide crosslinking agent having a tertiary amino group is N,N′-bisacryloylpiperazine.
4. The method of claim 1 , wherein the electrolytic monomer of quaternary ammonium salts, the bisacrylicamide crosslinking agent having a tertiary amino group, and the water are mixed together by stirring at a weight ratio of 60˜75:5˜16:20˜25.
5. The method of claim 1 , wherein the photoinitiator is 2-hydroxy-2-methyl-1-phenyl-1-one.
6. The method of claim 1 , wherein the solution is irradiated with ultraviolet light having an energy of 30 to 150 mJ/cm 2 for crosslinking.
7. The method of claim 1 , wherein 5% by weight of the powder obtained in the primary pulverization is dispersed in a mixed solution of 1-propanol and water at a weight ratio of 9:1 and pulverized.
8. A membrane-electrode assembly which is formed by the binder prepared according to claim 1 .