Ternary blends of terephthalate or isophthalate polyesters containing EG, CHDM and TMCD
Disclosed are ternary polyester blends that contain at least one polyester comprising terephthalic or isophthalic acid, ethylene glycol, and 1,4-cyclohexanedimethanol residues, and at least one polyester comprising terephthalic or isophthalic acid, 2,2,4,4-tetramethyl-1,3-cyclobutanediol, and 1,4-cyclohexanedimethanol residues. The ternary polyester blends have improved clarity, toughness, and fabrication characteristics and are useful for the preparation of flat or shaped articles. Of special interest are ternary blends where one of the three components compatibilizes the blend of two otherwise immiscible polyesters.
1. A ternary polyester blend comprising:
(a) a polyester (PCTT) comprising:
(i) a diacid component comprising at least 95 mole percent of the residues of terephthalic acid, isophthalic acid, or mixtures thereof; and
(ii) a diol component comprising from 15 to 45 mole percent of the residues of 2,2,4,4-tetramethyl-1,3-cyclobutanediol and from 55 to 85 mole percent of the residues of 1,4-cyclohexanedimethanol;
(b) a polyester (PETG) comprising:
(i) a diacid component comprising at least 95 mole percent of the residues of terephthalic acid, isophthalic acid, or mixtures thereof; and
(ii) a diol component comprising from 25 to 55 mole percent of the residues of 1,4-cyclohexanedimethanol and from 45 to 75 mole percent of the residues of ethylene glycol; and
(c) a polyester (PCTG) comprising:
(i) a diacid component comprising at least 95 mole percent of the residues of terephthalic acid, isophthalic acid, or mixtures thereof; and
(ii) a diol component comprising from 60 to 85 mole percent of the residues of 1,4-cyclohexanedimethanol and from 15 to 40 mole percent of the residues of ethylene glycol,
wherein said blend has a haze value of 5% or less when measured on a 0.010-inch thick film.
2. The blend according to claim 1 , having a haze value of 1.5% or less when measured on a 0.010-inch thick film.
3. The blend according to claim 1 , which comprises:
(a) 40 to 90 weight percent of the polyester PCTT;
(b) 1 to 20 weight percent of the polyester PETG; and
(c) 15 to 45 weight percent of the polyester PCTG,
wherein the weight percentages are based on the total amount of the polyesters PCTT, PETG, and PCTG in the blend, and the sum of the weight percentages equals 100.
4. The blend according to claim 1 , wherein
(a) the diol component of the polyester PCTT comprises from 15 to 30 mole percent of the residues of 2,2,4,4-tetramethyl-1,3-cyclobutanediol and from 70 to 85 mole percent of the residues of 1,4-cyclohexanedimethanol,
(b) the diol component of the polyester PETG comprises from 25 to 35 mole percent of the residues of 1,4-cyclohexanedimethanol and from 65 to 75 mole percent of the residues of ethylene glycol
(c) the diol component of the polyester PCTG comprises from 60 to 70 mole percent of the residues of 1,4-cyclohexanedimethanol and from 30 to 40 mole percent of the residues of ethylene glycol.
5. The blend according to claim 1 , wherein
(a) the diol component of the polyester PCTT comprises from 30 to 45 mole percent of the residues of 2,2,4,4-tetramethyl-1,3-cyclobutanediol and from 55 to 70 mole percent of the residues of 1,4-cyclohexanedimethanol,
(b) the diol component of the polyester PETG comprises from 45 to 55 mole percent of the residues of 1,4-cyclohexanedimethanol and from 45 to 55 mole percent of the residues of ethylene glycol
(c) the diol component of the polyester PCTG comprises from 60 to 85 mole percent of the residues of 1,4-cyclohexanedimethanol and from 15 to 40 mole percent of the residues of ethylene glycol.
6. The blend according to claim 1 , wherein the polyesters PCTT, PETG, and PCTG have an inherent viscosity of 0.45 to 1.2 dL/g.
7. The blend according to claim 1 , wherein the polyesters PCTT, PETG, and PCTG have an inherent viscosity of 0.55 to 0.76 dL/g.
8. The blend according to claim 1 , wherein the polyesters PCTT, PETG, and PCTG have an inherent viscosity of 0.65 to 0.78 dL/g.
9. The blend according to claim 1 , which has an inherent viscosity of 0.45 to 1.2 dL/g.
10. The blend according to claim 1 , wherein the polyesters PCTT, PETG, and PCTG are present in an amount sufficient to satisfy equations (1a) or (1b):
(−0.02276 *X )+(−0.02273 *Y )+(−0.01537 *Z )+(0.003789 *X*Y )+(6.52×10 −5 *X*Z )+(5.7×10 −5 *Y*Z )+(−6.7×10 −5 *X*Y*Z )≦0.41 (1a)
(0.005331 *X )+(0.005345 *Y )+(0.00507 *Z )+(0.002287 *X*Y )+(−4.9×10 −5 *X*Z )+(−5.3×10 −5 *Y*Z )+(−3.1×10 −5 *X*Y*Z )≦1.22 (1b)
wherein X is the weight percent of the polyester PCTT, Y is the weight percent of the polyester PETG, and Z is the weight percent of the polyester PCTG in the polyester blend.
11. The blend according to claim 1 , wherein the polyesters PCTT, PETG, and PCTG are present in an amount sufficient to satisfy equations (2a) or (2b):
(−0.02276 *X )+(−0.02273 *Y )+(−0.01537 *Z )+(0.003789 *X*Y )+(6.52×10 −5 *X*Z )+(5.7×10 −5 *Y*Z )+(−6.7×10 −5 *X*Y*Z )≦0 (2a)
(0.005331 *X )+(0.005345 *Y )+(0.00507 *Z )+(0.002287 *X*Y )+(−4.9×10 −5 *X*Z )+(−5.3×10 −5 *Y*Z )+(−3.1×10 −5 *X*Y*Z )≦1 (2b)
wherein X is the weight percent of the polyester PCTT, Y is the weight percent of the polyester PETG, and Z is the weight percent of the polyester PCTG in the polyester blend.
12. The blend according to claim 1 , wherein the polyesters PCTT, PETG, and PCTG are present in an amount sufficient to satisfy equations (3a) or (3b):
(−0.02276 *X )+(−0.02273 *Y )+(−0.01537 *Z )+(0.003789 *X*Y )+(6.52×10 −5 *X*Z )+(5.7×10 −5 *Y*Z )+(−6.7×10 −5 *X*Y*Z )≦0.7 (3a)
(0.005331 *X )+(0.005345 *Y )+(0.00507 *Z )+(0.002287 *X*Y )+(−4.9×10 −5 *X*Z )+(−5.3×10 −5 *Y*Z )+(−3.1×10 −5 *X*Y*Z )≦0.7 (3b)
wherein X is the weight percent of the polyester PCTT, Y is the weight percent of the polyester PETG, and Z is the weight percent of the polyester PCTG in the polyester blend.
13. A shaped article comprising the polyester blend according to claim 1 .
14. The shaped article according to claim 13 , which is a film, sheet, fiber, tube, preform, container, or bottle.
15. The shaped article according to claim 13 , which is a laminate, multi-layered film, multi-layered sheet, or multi-component fiber.
16. A ternary polyester blend comprising:
(a) from 50 to 80 weight percent of a polyester (PCTT) comprising:
(i) a diacid component comprising at least 95 mole percent of the residues of terephthalic acid; and
(ii) a diol component comprising from 15 to 40 mole percent of the residues of 2,2,4,4-tetramethyl-1,3-cyclobutanediol and from 60 to 85 mole percent of the residues of 1,4-cyclohexanedimethanol;
(b) from 5 to 15 weight percent of a polyester (PETG) comprising:
(i) a diacid component comprising at least 95 mole percent of the residues of terephthalic acid; and
(ii) a diol component comprising from 25 to 35 mole percent of the residues of 1,4-cyclohexanedimethanol and from 65 to 75 mole percent of the residues of ethylene glycol; and
(c) from 15 to 45 weight percent of a polyester (PCTG) comprising:
(i) a diacid component comprising at least 95 mole percent of the residues of terephthalic acid; and
(ii) a diol component comprising from 50 to 85 mole percent of the residues of 1,4-cyclohexanedimethanol and from 15 to 50 mole percent of the residues of ethylene glycol,
wherein the weight percentages are based on the total amount of the polyesters PCTT, PETG, and PCTG in the blend, and the sum of the weight percentages equals 100, and
wherein the blend has a haze value of 1.5% or less when measured on a 0.010-inch thick film.
17. The blend according to claim 16 , wherein the diol component of the polyester PCTT comprises from 20 to 30 mole percent of the residues of 2,2,4,4-tetramethyl-1,3-cyclobutanediol and from 70 to 80 mole percent of the residues of 1,4-cyclohexanedimethanol.
18. The blend according to claim 16 , wherein the diol component of the polyester PCTG comprises from 60 to 85 mole percent of the residues of 1,4-cyclohexanedimethanol and from 15 to 40 mole percent of the residues of ethylene glycol.
19. A ternary blend comprising:
(a) 40 to 90 weight percent of a polyester (PCTT) comprising:
(i) a diacid component comprising at least 95 mole percent of the residues of terephthalic acid, isophthalic acid, or mixtures thereof; and
(ii) a diol component comprising from 15 to 45 mole percent of the residues of 2,2,4,4-tetramethyl-1,3-cyclobutanediol and from 55 to 85 mole percent of the residues of 1,4-cyclohexanedimethanol;
(b) 1 to 20 weight percent of a polyester (PETG) comprising:
(i) a diacid component comprising at least 95 mole percent of the residues of terephthalic acid, isophthalic acid, or mixtures thereof; and
(ii) a diol component comprising from 25 to 55 mole percent of the residues of 1,4-cyclohexanedimethanol and from 45 to 75 mole percent of the residues of ethylene glycol; and
(c) 10 to 50 weight percent of a polyester (PCTG) comprising:
(i) a diacid component comprising at least 95 mole percent of the residues of terephthalic acid, isophthalic acid, or mixtures thereof; and
(ii) a diol component comprising from 60 to 85 mole percent of the residues of 1,4-cyclohexanedimethanol and from 15 to 40 mole percent of the residues of ethylene glycol,
wherein the weight percentages are based on the total amount of the polyesters PCTT, PETG, and PCTG in the blend, and the sum of the weight percentages equals 100.
20. The ternary blend of claim 19 comprising:
(a) 50 to 80 weight percent of the polyester PCTT;
(b) 5 to 15 weight percent of the polyester PETG; and
(c) 15 to 45 weight percent of the polyester PCTG,
wherein the weight percentages are based on the total amount of the polyesters PCTT, PETG, and PCTG in the blend, and the sum of the weight percentages equals 100.
21. The ternary blend of claim 19 comprising:
(a) a polyester PCTT comprising from 30 to 45 mole percent of the residues of 2,2,4,4-tetramethyl-1,3-cyclobutanediol and from 55 to 70 mole percent of the residues of 1,4-cyclohexanedimethanol,
(b) a polyester PETG comprises from 45 to 55 mole percent of the residues of 1,4-cyclohexanedimethanol and from 45 to 55 mole percent of the residues of ethylene glycol; and
(c) a polyester PCTG comprises from 60 to 85 mole percent of the residues of 1,4-cyclohexanedimethanol and from 15 to 40 mole percent of the residues of ethylene glycol.
22. The ternary blend of claim 20 comprising:
(a) a polyester PCTT comprising from 30 to 45 mole percent of the residues of 2,2,4,4-tetramethyl-1,3-cyclobutanediol and from 55 to 70 mole percent of the residues of 1,4-cyclohexanedimethanol,
(b) a polyester PETG comprises from 45 to 55 mole percent of the residues of 1,4-cyclohexanedimethanol and from 45 to 55 mole percent of the residues of ethylene glycol; and
(c) a polyester PCTG comprises from 60 to 85 mole percent of the residues of 1,4-cyclohexanedimethanol and from 15 to 40 mole percent of the residues of ethylene glycol.
23. The blend according to claims 16 , 19 , 20 , 21 or 22 , having a haze value of 1% or less when measured on a 0.010-inch thick film.
24. The blend according to claims 16 , 19 , 20 , 21 or 22 , having a haze value of 0.5% or less when measured on a 0.010-inch thick film.
25. The blend according to claims 16 , 19 , 20 , 21 or 22 , wherein the polyesters PCTT, PETG, and PCTG have an inherent viscosity of 0.5 to 0.8 dL/g.
26. The blend according to claims 16 , 19 , 20 , 21 or 22 , wherein the polyesters PCTT, PETG, and PCTG have an inherent viscosity of 0.55 to 0.70 dL/g.
27. A shaped article comprising the polyester blend according to claims 16 , 19 , 20 , 21 or 22 .
28. The shaped article according to claim 27 , which is a film, sheet, fiber, tube, preform, container, or bottle.