Low density foam, midsole, footwear, and methods for making low density foam
Foamed thermoplastic elastomeric polyurethane and ethylene-vinyl acetate copolymer articles are made with a combination of a supercritical fluid and a non-supercritical fluid blowing agent.
1. A method for making a low density foamed article, comprising:
combining in an extruder a molten thermoplastic polyurethane elastomer with
(a) a chemical blowing agent and
(b) a supercritical fluid,
to form a mixture, wherein the chemical blowing agent (a) is present in an amount up to about 15 wt % based on total polymer weight in the mixture and the supercritical fluid (b) comprises one of about 0.1 to about 5 weight percent of supercritical CO 2 based on the total polymer weight in the mixture or about 0.1 to about 4 weight percent of supercritical N 2 based on the total polymer weight in the mixture, and
injecting the mixture into a mold at an injection pressure of from 110 MPa to about 207 MPa, and molding the mixture to form the low density foamed article, wherein the mold comprises a porous tool;
wherein the low density foamed article has a density of less than 0.3 g/cm 3 .
2. A method according to claim 1 , wherein the molten thermoplastic polyurethane elastomer comprises a thermoplastic polyurethane elastomer having a solid Shore A hardness of from about 35 A to about 85 A.
3. A method according to claim 2 , wherein the solid Shore A hardness is from about 50 A to about 80 A.
4. A method according to claim 1 , wherein the chemical blowing agent is present in an amount from about 3 to about 12 wt % based on the total polymer weight in the mixture.
5. A method according to claim 1 , wherein the supercritical fluid is one of from about 0.5 to about 3 weight percent of supercritical CO 2 based on the total polymer weight in the mixture or from about 0.4 to about 2.5 weight percent of supercritical N 2 based on the total polymer weight in the mixture.
6. A method according to claim 1 , wherein the mixture further comprises a crosslinker.
7. A method according to claim 1 , wherein the porous tool has a pore size of from about 3 micrometers to about 20 micrometers.
8. A method according to claim 1 , wherein the porous tool is a porous metal or metal alloy.
9. A method according to claim 1 , wherein the porous tool is an insert having dimensions of the mold cavity.
10. A method according to claim 1 , wherein the porous tool comprises a plurality of inserts spaced within the mold cavity.
11. A method for making a low density foamed article, comprising:
combining in an extruder a molten thermoplastic polyurethane elastomer having a solid Shore A hardness of from about 35 A to about 85 A and a melt index of from about 5 to about 100 grams/10 min. as measured according to ASTM D1238 using an 8.7 kg weight and a temperature of 190° C. or from about 180 to about 300 grams/10 min. as measured according to ASTM D1238 using a 21.6 kg weight and a temperature of 200° C. with
(a) a chemical blowing agent and
(b) a supercritical fluid
to form a mixture, wherein the chemical blowing agent (a) is present in an amount up to 15 wt % based on total polymer weight in the mixture and the supercritical fluid (b) comprises one of about 0.1 to about 5 weight percent of supercritical CO 2 based on the total polymer weight in the mixture or about 0.1 to about 4 weight percent of supercritical N 2 based on the total polymer weight in the mixture, and
injecting the mixture into a mold at an injection pressure of from 110 MPa to about 207 MPa, and molding the mixture to form the low density foamed article.
12. A method according to claim 11 , wherein the Shore A hardness is from about 50 A to about 80 A.
13. A method according to claim 11 , wherein the or chemical blowing agent is present in an amount from about 3 to about 12 wt % based on the total polymer weight in the mixture.
14. A method according to claim 11 , wherein the supercritical fluid is one of from about 0.5 to about 3 weight percent of supercritical CO 2 based on the total polymer weight in the mixture or from about 0.4 to about 2.5 weight percent of supercritical N 2 based on the total polymer weight in the mixture.
15. A method for making a low density foamed article, comprising:
combining in an extruder a molten polymer thermoplastic polyurethane elastomer having a melt index of from about 5 to about 100 grams/10 min. as measured according to ASTM D1238 using an 8.7 kg weight and a temperature of 190° C., or from about 180 to about 300 grams/10 min. as measured according to ASTM D1238 using a 21.6 kg weight and a temperature of 200° C. with
(a) a chemical blowing agent and
(b) a supercritical fluid
to form a mixture, wherein the chemical blowing agent is present in an amount up to 15 wt % based on total polymer weight in the mixture and the supercritical fluid comprises one of about 0.1 to about 5 weight percent of supercritical CO 2 based on the total polymer weight in the mixture or about 0.1 to about 4 weight percent of supercritical N 2 based on the total polymer weight in the mixture, and
injecting the mixture into a mold at an injection pressure of from 110 MPa to about 207 MPa, and molding the mixture to form the low density foamed article; wherein the mold comprises a porous tool;
wherein the low density foamed article has a density of less than 0.3 g/cm 3 .
16. A method according to claim 15 , wherein the molten polymer comprises a thermoplastic polyurethane elastomer having a solid Shore A hardness of from about 35 A to about 85 A.
17. A method according to claim 15 , wherein the chemical blowing agent is present in an amount from about 3 to about 12 wt % based on the total polymer weight.
18. A method according to claim 15 , wherein the supercritical fluid is one of from about 1 to about 3 weight percent of supercritical CO 2 based on the total polymer weight in the mixture or from about 0.4 to about 2.5 weight percent of supercritical N 2 based on the total polymer weight in the mixture.
19. A method according to claim 15 , wherein the porous tool has a pore size of from about 3 micrometers to about 20 micrometers.
20. A method according to claim 15 , wherein the porous tool is a porous metal or metal alloy.
21. A method according to claim 15 , wherein the porous tool is an insert that is generally the dimensions of the mold cavity.
22. A low density foamed article made by the method of claim 1 .
23. The low density foamed article according to claim 22 , wherein the article has a density of from about 0.15 to less than 0.3 g/cm 3 .
24. The low density foamed article according to claim 22 , wherein the article is a cushion or cushioning element for an article of footwear, protective equipment, or clothing.