Composite barrier-type Nb3AI superconducting multifilament wire material
A composite barrier-type Nb 3 Al superconducting multifilament wire material comprises Nb barrier filaments, Ta barrier filaments, Nb bulk dummy filaments, and a Nb or Ta covering. In the composite barrier-type Nb 3 Al superconducting multifilament wire material, the Nb barrier filaments and Ta barrier filaments are disposed in the wire material so that the Nb barrier filaments are concentrated in a filament region near a core formed from the Nb bulk dummy filaments and only the Ta barrier filaments are disposed or the Nb barrier filaments are dispersed in the Ta barrier filaments in an outer layer portion formed from a region outside the Nb barrier filaments, excluding the Nb or Ta covering.
1. A composite barrier-type Nb 3 Al superconducting multifilament wire material comprising Nb barrier filaments, Ta barrier filaments, Nb bulk dummy filaments, and a Nb or Ta covering, wherein the Nb barrier filaments and Ta barrier filaments are disposed in the wire material so that the Nb barrier filaments are concentrated in a filament region near a core formed from the Nb bulk dummy filaments and only the Ta barrier filaments are disposed or the Nb barrier filaments are dispersed in the Ta barrier filaments in an outer layer portion formed from a region outside the Nb barrier filaments, excluding the Nb or Ta covering.
2. The composite barrier-type Nb 3 Al superconducting multifilament wire material according to claim 1 , wherein one or a plurality of the Nb barrier filaments are dispersed in a plurality of the Ta barrier filaments in the outer layer portion.
3. The composite barrier-type Nb 3 Al superconducting multifilament wire material according to claim 1 , wherein the Nb barrier filaments are Nb barrier filaments each obtained by rolling a Nb sheet and an Al sheet into a jelly roll and forming a Nb layer around the roll and subjecting the resultant roll to wire drawing processing.
4. The composite barrier-type Nb a Al superconducting multifilament wire material according to claim 1 , wherein the Ta barrier filaments are Ta barrier filaments each obtained by rolling a Nb sheet and an Al sheet into a jelly roll and forming a Ta layer around the roll and subjecting the resultant roll to wire drawing processing.
5. The composite barrier-type Nb 3 Al superconducting multifilament wire material according to claim 1 , wherein the cross-sectional occupancy rate of the Nb bulk dummy filaments is 3 to 20%, the cross-sectional occupancy rate of the Nb barrier filaments disposed in the filament region near the core is 4 to 40%, the cross-sectional occupancy rate of the covering is 5 to 30%, and the remaining cross-sectional area is occupied by the outer layer portion.
6. The composite barrier-type Nb 3 Al superconduating multifilament wire material according to claim 5 , wherein the cross-sectional occupancy rate of the Nb barrier filaments in the outer layer portion is 0 to 80%.