Method of forming an MT-propyl siloxane resin
View Patent ↗A method of forming an MT-propyl siloxane resin includes the steps of hydrolyzing propyl trichlorosilane in an excess of water to provide a T-propyl siloxane resin and capping the T-propyl siloxane resin formed from the hydrolysis of the propyl trichlorosilane with a silicon-containing M-group capping agent to form the MT-propyl siloxane resin. The MT-propyl siloxane resin is useful in a variety of personal care applications, and in particular, as an additive to personal care compositions.
1. A method of forming an MT-propyl siloxane resin having at least 0.60 moles of R 1 SiO 3/2 units per mole of silicon, wherein R 1 is a substituted or unsubstituted hydrocarbyl group having from 1 to 10 carbon atoms, an aryl group, a carbinol group, an amino group, or a sulfido group, and with the proviso that at least 0.40 moles of the R 1 groups per mole of silicon are propyl groups, said method comprising:
hydrolyzing propyl trichlorosilane in an excess of water to provide a T-propyl siloxane resin;
capping the T-propyl siloxane resin formed from hydrolyzing propyl trichlorosilane with a silicon-containing M-group capping agent to form the MT-propyl siloxane resin, wherein the silicon-containing M-group capping agent comprises at least 0.50 moles of monofunctional units per mole of silicon, wherein the silicon-containing M-group capping agent is selected from triorganosilanes, halotriorganosilanes, alkoxytriorganosilanes, carboxytriorganosilanes, chlorosilanes, alkoxysilanes, disiloxanes, disilazanes, and compounds having average formula:
wherein Z is Cl, an alkoxy group having from 1 to 10 carbons, or a substituted or unsubstituted hydrocarbyl group having from 1 to 10 carbon atoms, and each R 4 , R 5 , and R 6 is independently a substituted or unsubstituted hydrocarbyl group having from 1 to 10 carbon atoms; X is O or NH, and y ranges from 0 to 10; or hydrolyzate thereof, wherein the MT-propyl siloxane resin has the average formula:
(R 2 3 SiO 1/2 ) a (R 1 SiO 3/2 ) c ,
wherein:
a is less than 0.20, and ‘c’ ranges from 0.80 to less than 1, with the proviso that a+c=1.
2. The method of forming an MT-propyl siloxane resin of claim 1 , wherein the MT-propyl siloxane resin comprises from 0.05 to 0.40 moles of silanol groups per mole of silicon.
3. The method of forming an MT-propyl siloxane resin of claim 1 , wherein the step of hydrolyzing propyl trichlorosilane is conducted in the presence of an organic solvent, and the method further comprises the step of conducting a solvent-exchange between the organic solvent and an alternative carrier solvent.
4. The method of forming an MT-propyl siloxane resin of claim 1 , wherein the silicon-containing M-group capping agent comprises a compound having the following average formula:
wherein Z is Cl, an alkoxy group having from 1 to 10 carbons, or a substituted or unsubstituted hydrocarbyl group having from 1 to 10 carbon atoms, and each R 4 , R 5 , and R 6 is independently a substituted or unsubstituted hydrocarbyl group having from 1 to 10 carbon atoms; X is O or NH, and y ranges from 0 to 10; or hydrolyzate thereof.
5. The method of forming an MT-propyl siloxane resin of claim 1 , wherein the silicon-containing M-group capping agent comprises trimethylchlorosilane or a hydrolyzate thereof.
6. The method of forming an MT-propyl siloxane resin of claim 1 , wherein the silicon-containing M-group capping agent is provided before the step of hydrolyzing propyl trichlorosilane.
7. An MT-propyl siloxane resin, wherein the MT-propyl siloxane resin has the average formula:
(R 2 3 SiO 1/2 ) a (R 1 SiO 3/2 ) c ,
wherein:
a is less than 0.20, and c ranges from 0.80 to less than 1, with the proviso that a+c=1.
8. The MT-propyl siloxane resin of claim 7 , wherein the MT-propyl siloxane resin comprises from 0.05 to 0.40 moles of silanol groups per mole of silicon.