Release film having a rough surface structure
Release film having at least one layer based on at least one thermoplastic polymer as matrix polymer, in which solid microparticles having a melting point which is at least 10° C. higher than that of the matrix polymer are dispersed therein and surfaces of which at least one is provided with a release layer as outer layer based on at least one cured polysiloxane.
1. A release film having a nonplanar but unembossed surface structure which is not caused by a foam structure, comprising at least one layer (s) based on at least one thermoplastic matrix polymer selected from the group consisting of olefin homopolymers or copolymers and polyamides or copolyamides and comprising distributed solid microparticles having a particle size of at least 50 μm and having a melting point at least 10° C. higher than that of the matrix polymer, and at least one of the surfaces of the release film is covered by a release layer (b) as outer layer, based on at least one cured polysiloxane.
2. A release film as claimed in claim 1 , wherein the microparticles have a particle size distribution from 50 μm to 500 μm.
3. A release film as claimed in claim 1 , wherein the microparticles are based on a thermoplastic polymer or on an inorganic compound or an inorganic material.
4. A release film as claimed in claim 1 , wherein the melting point of the microparticles is at least 30° C. higher than that of the matrix polymer.
5. A release film as claimed in claim 1 , wherein one surface of said at least one layer (s) is covered by a release layer (b).
6. A release film as claimed in claim 1 , wherein the nonplanar surface structure has elevations which have a height of up to 300 μm.
7. A release film as claimed in claim 1 , wherein the layer (s) comprises 5-15 wt % based on the total weight of the layer (s), of solid microparticles.
8. A release film as claimed claim 1 , wherein the release layer (b) comprises at least one flow improving auxiliary agent and/or at least one adhesion improving auxiliary agent.
9. A release film as claimed in claim 8 , wherein the release layer (b) contains the flow improving auxiliary agent in an amount of 1-10wt % and/or the adhesion improving auxiliary agent in an amount of 1-5 wt %, based in each case on the total weight of the release layer (b).
10. A release film as claimed in claim 1 , wherein the layer (s) is joined by its free surface to a layer (a) based on at least one olefin homopolymer or copolymer or on a laminate of a layer (a) and a layer (c), which comprises or comprise no solid microparticles.
11. A release film as claimed in claim 1 , wherein the release film has at least one barrier layer (e) adjacent to the layer (a) which layer (e) is bonded to the layer (a) respectively the layer (c) optionally via an adhesion promoting layer (f) respectively (g).
12. A release film as claimed in claim 1 , wherein the barrier layer (e) is based on at least one homopolyamide or copolyamide which is bonded in each case via an adhesion promoting layer (f) or (g) to layer (a) or to layer (c), respectively, which layer (a) respectively (c), is based on a propylene homopolymer or copolymer.
13. A releasable protective or cover film for self-adhesive labels, adhesive tapes, stickers, or self-adhesive roofing comprising the release film of claim 1 .
14. A self-adhesive roofing sheet provided with a release film as releasable protective or cover film as claimed in claims 1 which can be winded up.
15. A winded-up, self-adhesive bitumen roofing sheet provided with a release film of claim 1 as releasable protective or cover film.