Method for producing a thin film made of lead zirconate titanate
The invention relates to a method for producing the thin film made of lead zirconate titanate in a 111-oriented perovskite structure, comprising the following steps: providing a substrate having a substrate temperature above 450° C. and a lead target, a zirconium target, and a titanium target; applying the thin film by sputtering lead, zirconium, and titanium from the respective targets onto the substrate, wherein the total deposition rate of lead, zirconium, and titanium is greater than 10 nm/min, the deposition rate of zirconium is selected in such a way that the atomic concentration of zirconium with respect to the atomic concentration of zirconium together with titanium in the thin film is between 0.2 and 0.3, and the deposition rate of lead is selected to be sufficiently low, depending on the substrate temperature and the total deposition rate of lead, zirconium, and titanium, for an X-ray diffractometer graph of the 111-oriented lead zirconate titanate to have a significant peak value (19) in a diffraction angle range from 33 to 35.5°; and completing the thin film.
1. A method for producing a thin film made of lead zirconate titanate in a 111-oriented perovskite structure, comprising:
providing a substrate at a temperature of over 450° C. and a lead target, a zirconium target and a titanium target;
applying the thin film by sputtering of lead, zirconium and titanium from the respective targets onto the substrate, wherein
an overall deposition rate of lead, zirconium and titanium is greater than 10 nm/min,
the deposition rate of zirconium is selected such that the atomic concentration of zirconium relative to the atomic concentration of zirconium together with titanium in the thin film lies in the range of 0.2 to 0.3, and
the deposition rate of lead is selected to be sufficiently low, depending on the substrate temperature and the overall deposition rate of lead, zirconium and titanium that an X-ray diffractometer graph for the 111-oriented lead zirconate titanate has a significant peak value in the diffraction angle range from 33° to 35.5°; and
completing the thin film.
2. The method as claimed in claim 1 , wherein the sputtering of lead, zirconium and titanium from the respective targets onto the substrate is carried out confocally and/or simultaneously.
3. The method as claimed in claim 1 , wherein the deposition rate of lead is selected such that the atomic concentration of lead relative to the atomic concentration of zirconium together with titanium in the thin film lies in the range of 1.1 to 1.3.
4. The method as claimed in claim 1 , wherein the overall deposition rate of lead, zirconium and titanium at a substrate temperature in the range of 500° C. to 550° C. is selected to lie in the range between 11 nm/min and 13 nm/min, the deposition rate of lead is selected such that the atomic concentration of lead relative to the atomic concentration of zirconium together with titanium in the thin film lies in the range of 1.24 to 1.29 and the deposition rate of zirconium is selected such that the atomic concentration of zirconium relative to the atomic concentration of zirconium together with titanium in the thin film lies in the range of 0.25 to 0.29.
5. The method as claimed in claim 1 , wherein the significant peak value of an X-ray diffractometer graph for the thin film lies in the diffraction angle range from 34° to 34.5°.
6. The method as claimed in claim 1 , wherein the significant peak value in the X-ray diffractometer graph of the thin film is caused by crystals of a zirconium dioxide in the thin film.
7. The method as claimed in claim 1 , wherein the thin film is applied such that the thin film is self-polarized.
8. The method as claimed in claim 1 , further comprising:
polarizing the thin film such that the pyroelectric coefficient of the thin film is greater than 10 −4 C/m 2 .
9. The method as claimed in claim 1 , wherein the thin film has a thickness in the range of 0.2 μm to 3 μm.