Substrate with a corrosion resistant coating and method of production thereof

1. A substrate with a corrosion-resistant coating, the corrosion-resistant coating comprising at least one nickel layer, a chromium layer as an outermost metal finish layer, and at least one tin-nickel alloy layer deposited between the at least one nickel layer and the chromium finish layer for suppression of corrosion reactions, wherein the chromium finish layer comprises chromium and from 1 to 25 wt. % carbon, from 1 to 30 wt. % oxygen, from 0 to 10 wt. % sulfur, from 0 to 10 wt. % nitrogen, and from 0 to 30 wt. % iron, wherein the at least one tin-nickel alloy layer is produced by deposition from an electrolyte having a temperature of from 40° C. to 60° C., and wherein the produced substrate passes a corrosion test according to UNI EN ISO 9227 CASS standard procedure for a test duration of at least 96 hours.

2. The substrate according to claim 1 , wherein the at least one tin-nickel alloy layer comprises 55 to 75 weight-% tin and 25 to 45 weight % nickel.

3. The substrate according to claim 1 , wherein the at least one tin-nickel alloy layer has a thickness of 0.1 to 10 μm.

4. The substrate according to claim 1 , wherein the at least one nickel layer has a thickness of 1 to 50 μm.

5. The substrate according to claim 1 , wherein the chromium finish layer has a thickness of 0.05 to 2 μm.

6. The substrate according to claim 1 , wherein the corrosion-resistant coating comprises a bright nickel layer or a further metallic layer deposited on the substrate.

7. The substrate according to claim 6 , wherein the further metallic layer consists essentially of copper.

8. The substrate according to claim 6 , further comprising a semi-bright nickel layer arranged between the bright nickel layer and the substrate or the further metallic layer.

9. The substrate according to claim 1 , wherein the substrate comprises a metal, a metal alloy, or a plastic.

10. The substrate according to claim 1 , wherein the produced substrate passes a corrosion test according to Volkswagen VW PV1067 standard procedure for a test duration of at least 48 hours.

11. A method for producing a corrosion resistant coating for a substrate, the method comprising:

a) electroplating at least one nickel layer on the substrate,

b) electroplating at least one tin-nickel alloy layer from an electrolyte having a temperature of from 40° C. to 60° C., and

c) electroplating a chromium layer as an outermost metal finish layer, wherein electroplating the chromium layer comprises electro-plating chromium that includes from 1 to 25 wt. % carbon, from 1 to 30 wt. % oxygen, from 0 to 10 wt. % sulfur, from 0 to 10 wt. % nitrogen, and from 0 to 30 wt. % iron, so that the at least one tin-nickel alloy layer is deposited between the at least one nickel layer and the at least one chromium finish layer,

wherein corrosion reactions are suppressed by the tin-nickel alloy layer such that the produced substrate passes a corrosion test according to UNI EN ISO 9227 CASS standard procedure for a test duration of at least 96 hours.

12. The method according to claim 11 , wherein electroplating the at least one tin-nickel alloy layer comprises electroplating the at least one tin-nickel alloy layer from an acidic aqueous electrolyte with a pH in the range of 2 to 6, wherein the electrolyte comprises additives comprising at least one of chlorides, fluorides, fluoroborates apart from at least one tin salt and at least one nickel salt.

13. The method according to claim 12 , wherein the electrolyte comprises second additives selected from the group consisting of complexing agents;

wetting agents; and

mixtures thereof.

14. The method according to claim 11 , wherein electroplating the at least one tin-nickel alloy layer comprises electroplating the at least one tin-nickel alloy layer from an alkaline aqueous electrolyte, wherein the electrolyte comprises at least one tin salt and at least one nickel salt, wherein the salts are selected from the group consisting of sulfates, sulfamates, phosphates, pyrophosphates, glycine, and mixtures thereof.

15. The method according to claim 11 , wherein electroplating the at least one tin-nickel alloy layer comprises electroplating the at least one tin-nickel alloy layer from a cyanide-containing aqueous electrolyte, wherein the electrolyte comprises at least one tin salt and at least one nickel salt, wherein the salts are selected from the group consisting of sulfates, sulfamates, phosphates, pyrophosphates, glycine, and mixtures thereof.

16. The method according to claim 11 , wherein electroplating the at least one tin-nickel alloy layer comprises electroplating the at least one tin-nickel alloy layer from a neutral or weakly alkaline aqueous electrolyte with a pH in the range of 6 to 10, wherein the electrolyte comprises at least one tin salt and at least one nickel salt, wherein the salts are selected from the group consisting of sulfates, sulfamates, phosphates, pyrophosphates, glycine, and mixtures thereof.

17. The method according to claim 11 , wherein the tin salt is selected from the group consisting of chlorides, fluorides, fluoroborates, sulfates, methane sulfonates and mixtures thereof, and the nickel salt is selected from the group consisting of chlorides, fluorides, fluoroborates, sulfates, sulfamates, pyrophosphates, methane sulfonates, and mixtures thereof.

18. The method according to claim 11 , wherein electroplating the chromium finish layer comprises electroplating the chromium layer from an acidic aqueous electrolyte, wherein the electrolyte comprises at least one chromium(VI)-salt.

19. The method according to claim 11 , wherein electroplating the chromium finish layer comprises electroplating the chromium layer from an acidic aqueous electrolyte with a pH in the range of 2 to 6, wherein the electrolyte comprises at least one chromium(III)-salt.

20. The method according to claim 19 , wherein the electrolyte comprises additives selected from the group consisting of:

organic acids or salts thereof;

inorganic acids or salts thereof;

conducting salts;

blackening agents; and

wetting agents.