Positive electrode active material for lithium ion battery, method of producing the same, electrode for lithium ion battery, and lithium ion battery
Provided is a positive electrode active material for lithium ion batteries, which is capable of realizing stability and safety at a high voltage, a high energy density, high load characteristics, and long-term cycle characteristics by controlling a crystal shape of LiMnPO 4 particles having a crystal structure very suitable for Li diffusion or controlling an average primary particle size, a production method thereof, an electrode for lithium ion batteries, and a lithium ion battery. The positive electrode active material for lithium ion batteries of the invention is a positive electrode active material for lithium ion batteries, which is formed from LiMnPO 4 . Values of lattice constants a, b, and c, which are calculated from an X-ray diffraction pattern, satisfy 10.41 Å<a≦10.43 Å, 6.070 Å<b≦6.095 Å, and 4.730 Å<C≦4.745 Å, and an average particle size is 10 to 100 nm.
1. A positive electrode active material for lithium ion batteries, which is formed from LiMnPO 4 particles,
wherein lattice constants a, b, and c, which are calculated from an X-ray diffraction pattern of the LiMnPO 4 particles, have values satisfying 10.41 Å<a≦10.43 Å, 6.070 Å<b≦6.086 Å, and 4.730 Å<c≦4.745 Å;
an average particle diameter of the LiMnPO4 particles is 10 to 100 nm,
wherein the LiMnPO 4 particles are obtained by a hydrothermal synthesis method, the method comprising: a step of heating raw material slurry obtained by mixing a Li source, a P source, and a Mn source with a solvent containing water as a main component to a maximum temperature within a range of 100 to 130° C., and performing synthesis under compression at a temperature below or equal to the maximum temperature, and
wherein the maximum temperature of the hydrothermal synthesis is the highest temperature to which the LiMnPO 4 particles are heated during the production of the positive electrode active material.
2. The positive electrode active material for lithium ion batteries according to claim 1 , wherein an average particle diameter of the LiMnPO 4 particles is 15 to 60 nm.
3. The positive electrode active material for lithium ion batteries according to claim 1 , wherein the hydrothermal synthesis method comprises performing hydrothermal synthesis under compression for 1 to 48 hours.
4. An electrode for lithium ion batteries, containing: the positive electrode active material for lithium ion batteries according to claim 1 .
5. A lithium ion battery, comprising: the electrode for lithium ion batteries according to claim 4 .
6. A method of producing a positive electrode active material comprising LiMnPO 4 particles for lithium ion batteries, the method comprising:
producing LiMnPO 4 particles having an average particle diameter of 10 to 100 nm and lattice constants a, b, and c, which satisfy 10.41 Å<a 10.43 Å, 6.070 Å<b≦6.086 Å, and 4.730 Å<c≦4.745 Å by a hydrothermal synthesis process,
wherein the hydrothermal synthesis includes a step of heating raw material slurry obtained by mixing a Li source, a P source, and a Mn source with a solvent containing water as a main component to a maximum temperature within a range of 100 to 130° C., and performing synthesis under compression at a temperature at or below the maximum temperature, and
wherein the maximum temperature of the hydrothermal synthesis is the highest temperature to which the LiMnPO 4 particles are heated during the production of the positive electrode active material.