Positive electrode active material for lithium ion battery, method of producing the same, electrode for lithium ion battery, and lithium ion battery
Provided is a positive electrode active material for lithium ion batteries, which may be in the form of fine particles with good crystallinity and high purity by suppressing grain growth, and which is capable of improving the charge and discharge capacity and high-rate characteristics, a production method thereof, an electrode for lithium ion batteries, and a lithium ion battery. The positive electrode active material for lithium ion batteries of the invention is a positive electrode active material for lithium ion batteries which are formed from LiMPO 4 (provided that, M represents one or more kinds selected from a group consisting of Mn, Co, and Ni). In an X-ray diffraction pattern, a ratio I(020)/I(200) of the X-ray intensity I(020) of a (020) plane around a diffraction angle 2θ of 29° to the X-ray intensity I(200) of a (200) plane around a diffraction angle 2θ of 17° is 3.00 to 5.00, and a specific surface area is 15 m 2 /g to 50 m 2 /g.
1. A positive electrode active material for lithium ion batteries which is formed from LiMPO 4 , provided that, M represents one or more kinds selected from a group consisting of Mn, Co, and Ni,
wherein in an X-ray diffraction pattern, a ratio I(020)/I(200) of the X-ray intensity I(020) of a (020) plane around a diffraction angle 2θ of 29° to the X-ray intensity I(200) of a (200) plane around a diffraction angle 2θ of 17° is 3.21 to 4.31, wherein a specific surface area of the active material is 15 m 2 /g to 50 m 2 /g.
2. An electrode for lithium ion batteries, containing:
the positive electrode active material for lithium ion batteries according to claim 1 .
3. A lithium ion battery, comprising:
the electrode for lithium ion batteries according to claim 2 .
4. An electrode for lithium ion batteries, containing:
the positive electrode active material for lithium ion batteries according to claim 1 .
5. The positive electrode active material for lithium ion batteries according to claim 1 , wherein the positive electrode active material is generated by a method comprising:
preparing a raw material slurry obtained by mixing a Li source, a P source, and an M source with a solvent containing water as a main component, provided that M represents one or more kinds selected from the group consisting of Mn, Co, and Ni;
adding one kind or two kinds selected from the group consisting of ammonia and amine-type compounds to the raw material slurry in such a manner that % by mole of an ammonia group of the ammonia or the amine-type compounds with respect to the M source becomes 1% by mole to 12% by mole to obtain a mixture; and
heating the mixture to a temperature equal to or higher than a boiling point of the raw material slurry to generate the positive electrode active material using a hydrothermal synthesis method.
6. The positive electrode active material for lithium ion batteries according to claim 5 , wherein one kind or two kinds selected from the group consisting of ammonia and amine-type compounds is added to the raw material slurry in such a manner that % by mole of an ammonia group of the ammonia or the amine-type compounds with respect to the M source becomes 5% by mole to 12% by mole.