Process for the manufacture of tanks having high barrier properties toward fluids
The invention relates to a method for producing a tank having high fluid-barrier properties. According to the invention, a specific polyamide composition containing impact-resistance modifying agents is used in a first step to produce components by means of injection moulding and, subsequently, said components are assembled in order to obtain the tank. The viscosity and gasoline permeability of the polyamide composition are sufficient to allow the production of tanks that provide an excellent trade-off between fluid-barrier properties and mechanical properties.
1. A process for making a tank having high barrier properties toward fluids, comprising:
assembling one or more components made by injection molding of a polyamide composition, optionally with one or more other components, in order to obtain the tank; said polyamide composition comprising a polyamide and from 5% to 40% by weight of an impact strength modifier, wherein the impact strength modifier has a mean particle size of between 0.1 and 1 μm and is defined as having an ASTM D-638 tensile modulus of less than about 500 MPa;
said polyamide composition further comprising a novolac resin; and
said polyamide composition exhibiting the following characteristics:
a melt viscosity of between 50 and 700 Pa·s, measured according to the standard ISO 11443, at a shear gradient of 1000 s −1 and a temperature equal to the melting point of the polyamide +35° C.; and
a permeability to SP95 E10 alcohol-blend gasoline of less than or equal to 10 g·mm/m 2 ·day, as measured at a temperature of 40° C. and a relative humidity of 20%,
wherein:
the polyamide composition is devoid of cyclodextrin and silica;
the polyamide composition is substantially free of plasticizers;
the impact strength modifier comprises at least 20% by weight, based on the total weight of the impact strength modifier, of reactive impact strength modifier that comprises functional groups that are reactive with the polyamide, and/or
the polyamide composition further comprises at least 10% by weight, based on the total weight of the impact strength modifier, of a compatibilizing agent that comprises functional groups that are reactive with the polyamide.
2. The process of claim 1 , wherein the composition exhibits a melt viscosity of between 100 and 500 Pa·s.
3. The process of claim 1 , wherein the composition exhibits a permeability to SP95 E10 alcohol-blend gasoline of less than or equal to 4 g·mm/m 2 ·day.
4. The process of claim 1 , wherein the polyamide is a semicrystalline aliphatic or semiaromatic polyamide.
5. The process of claim 1 , wherein the polyamide composition comprises between 20% and 90% by weight of the polyamide, with respect to the total weight of the polyamide composition.
6. The process of claim 1 , wherein the other components are metal or plastic parts.
7. The process of claim 1 , wherein the step of assembling is carried out by direct or indirect welding.
8. The process of claim 1 , wherein the tank is composed solely of components obtained by injection molding of the polyamide composition.
9. The process of claim 1 , wherein the step of assembling is carried out by bringing the components into contact over at least a portion of their surfaces and then welding the components over at least a portion where the components are in contact, at a temperature greater than the softening.
10. The process of claim 1 , wherein the tank comprises a wall that exhibits a notched Charpy impact at −40° C. (kJ/m 2 ), measured according to the standard ISO 179-1/1 eA, of greater than or equal to 23 kJ/m 2 .
11. The process of claim 10 , wherein the wall exhibits a thickness of less than 4 mm.
12. The process of claim 10 , wherein the wall exhibits a thickness of from 1.5 mm to 3 mm.
13. The process of claim 1 , wherein the polyamide composition further comprises the impact strength modifier and/or compatibilizing agent, wherein the impact strength modifier and/or compatibilizing agent comprise one or more reactive functional groups selected from a group consisting of maleic anhydride, glycidyl groups, (meth)acrylic ester groups, and mixtures thereof.
14. The process as of claim 1 , wherein the composition comprises greater than or equal to 25% by weight of the impact strength modifier, with respect to the total weight of the composition, and further comprises from 1% to 7% by weight of the novolac resin, with respect to the total weight of the composition.
15. The process of claim 1 , wherein the impact strength modifier is added within a range of 4 to 10 times that of the novolac resin.
16. The process of claim 1 , wherein the polyamide composition is free of plasticizers.