Method and composition for sequestration of arsenic
A method for sequestrating arsenic oxides, comprising forming an insoluble and stable glass incorporating a fully oxidized form of arsenic generated by oxidation of an initial lower oxide of arsenic and stabilization by calcium salt formation. The glass composition for sequestration of arsenic comprises from 50 to 75% silica; from 0.5 to 3% Al 2 O 3 ; from 1 to 15% MnO; from 5 to 15% CaO; from 1 to 20% As 2 O 5 and from 8 to 14% Na 2 O, less than four percent of iron oxides, magnesium oxide and other oxides.
1. A method for sequestrating arsenic oxides, comprising forming an insoluble and stable glass by mixing an initial lower oxide of arsenic with one of: i) glass-forming elements and ii) recycled glass; adding an oxidizing agent, for oxidizing the initial lower oxide of arsenic into a fully oxidized form of arsenic, and at least one of: i) calcium oxide and ii) calcium hydroxide for stabilization of arsenic by calcium salt formation; and a heating cycle.
2. The method of claim 1 , wherein the initial lower oxide of arsenic is arsenious oxide, and the fully oxidized form of arsenic is pentavalent arsenic oxide.
3. The method of claim 1 , wherein the oxidizing a ent is manganese dioxide.
4. The method of claim 1 , wherein said adding the oxidizing agent comprises adding manganese dioxide, in a water slurry and at a temperature in a range between 50° C. and 100° C.
5. The method of claim 1 , wherein the oxidizing agent is pyrolusite.
6. The method of claim 1 , comprising mixing the initial lower oxide of arsenic with glass-forming elements selected in the group consisting of silica, sodium oxide, calcium oxide, alumina, feldspar, sodium carbonate and magnesium oxide.
7. The method of claim 1 , wherein the initial lower oxide of arsenic is arsenious oxide, the oxidizing agent oxidizing the arsenious oxide into arsenic oxide, and the arsenic oxide being thermally stabilized by the at least one of: calcium oxide and calcium hydroxide.
8. The method of claim 1 , wherein said heating cycle comprises increasing the temperature to a range between about 1000° C. and about 1200° C., maintaining the temperature within the range between about 1000° C. and about 1200° C. to allow glass formation, and cooling.
9. A method for sequestrating arsenic oxides, comprising forming an insoluble and stable glass having a composition by weight of from 50 to 75% silica; from 0.5 to 3% alumina; from 1 to 15% manganese oxide; from 5 to 15% calcium oxide; from 1 to 20% arsenic calculated as arsenic oxide and from 8 to 14% of sodium oxide, and less than four percent of iron oxides, magnesium oxide and other oxides.
10. The method of claim 9 , wherein said forming the insoluble and stable glass is done at a temperature comprised between 1000° C. and 1200° C.
11. The method of claim 9 , comprising reducing glass-forming elements to a very fine state smaller than 60 mesh and intimately mixing them with arsenious oxide, manganese dioxide and calcium hydroxide, and starting a heating cycle.
12. The method of claim 9 , comprising using recycled glass reduced to a very fine state smaller than 60 mesh.
13. A glass composition, comprising from 50 to 75% silica; from 0.5 to 3% Al 2 O 3 ; from 1 to 15% MnO; from 5 to 15% CaO; from 1 to 20% As 2 O 5 and from 8 to 14% Na 2 O, less than four percent of iron oxides, magnesium oxide and other oxides.