Laminated ceramic capacitor and producing method for laminated ceramic capacitor
A laminated ceramic capacitor having high electrostatic capacitance and excellent lifetime characteristics, even when in a high electric field intensity employs a dielectric ceramic including crystal grains and crystal grain boundaries which contains, as its main constituent, a perovskite-type compound including Ba, Ca, and Ti, and further contains Mg, R (Y, La, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, and/or Yb), and Zr, such that when the laminated body is dissolved, the contents in terms of parts by mol are Ca: 3 to 15 parts by mol, Mg: 0.01 to 0.09 parts by mol, R: 2.5 to 8.4 parts by mol, and Zr: 0.05 to 3.0 parts by mol with respect to 100 parts by mol of Ti, and there is Ca at least at the centers of the crystal grains.
1. A laminated ceramic capacitor comprising:
a laminated body comprising dielectric ceramic layers including crystal grains and crystal grain boundaries and internal electrode layers; and
external electrodes disposed on a surface of the laminated body electrically connecting to internal electrode layers,
wherein the laminated body has a composition comprising, as its main constituent, a perovskite-type compound including Ba, Ca, and Ti, and further containing Mg, R (in which R is at least one member selected from the group consisting of Y, La, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, and Yb), and Zr, and
the contents of the respective elements in terms of parts by mol are
Ca: 3 parts by mol or more and 15 parts by mol or less,
Mg: 0.01 parts by mol or more and 0.09 parts by mol or less,
R: 2.5 parts by mol or more and 8.4 parts by mol or less, and
Zr: 0.05 parts by mol or more and 3.0 parts by mol or less
with respect to 100 parts by mol of Ti, and
there is Ca at least at the centers of crystal grains.
2. A laminated ceramic capacitor according to claim 1 , wherein said contents of the respective elements in terms of parts by mol are when the laminated body is dissolved in a solvent therefor.
3. The laminated ceramic capacitor according to claim 2 , wherein the R content is 5.7 parts by mol or more and 8.4 parts by mol or less with respect to 100 parts by mol of Ti.
4. The laminated ceramic capacitor according to claim 3 , wherein the Mg content is at least 0.05 parts by mol and the Zr content is 0.5 parts by mol or more and 2.9 parts by mol or less, with respect to 100 parts by mol of Ti.
5. The laminated ceramic capacitor according to claim 4 , further containing Mn, V, and Si,
wherein the contents of the respective elements in terms of parts by mol are
Mn: 0.1 parts by mol or more and 1.0 part by mol or less,
V: 0.05 parts by mol or more and 0.5 parts by mol or less, and
Si: 0.5 parts by mol or more and 2.5 parts by mol or less
with respect to 100 parts by mol of Ti.
6. The laminated ceramic capacitor according to claim 1 , wherein the R content is 5.7 parts by mol or more and 8.4 parts by mol or less with respect to 100 parts by mol of Ti.
7. The laminated ceramic capacitor according to claim 6 , further containing Mn, V, and Si,
wherein the Contents of the respective elements in terms of parts by mol are
Mn: 0.1 parts by mol or more and 1.0 part by mol or less,
V: 0.05 parts by mol or more and 0.5 parts by mol or less, and
Si: 0.5 parts by mol or more and 2.5 parts by mol or less
with respect to 100 parts by mol of Ti.
8. The laminated ceramic capacitor according to claim 1 , further containing Mn, V, and Si,
wherein the contents of the respective elements in terms of parts by mol are
Mn: 0.1 parts by mol or more and 1.0 part by mol or less,
V: 0.05 parts by mol or more and 0.5 parts by mol or less, and
Si: 0.5 parts by mol or more and 2.5 parts by mol or less
with respect to 100 parts by mol of Ti.
9. The laminated ceramic capacitor according to claim 1 , wherein the Mg content is at least 0.05 parts by mol and the Zr content is 0.5 parts by mol or more and 2.9 parts by mol or less, with respect to 100 parts by mol of Ti.
10. A method for producing a laminated ceramic capacitor comprising
providing a slurry comprising a main constituent powder containing, as its main constituent, a perovskite-type compound including Ba, Ca, and Ti, a Mg compound, a R compound in which R is at least one member selected from the group consisting of Y, La, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, and Yb, and a Zr compound;
obtaining ceramic green sheets from the ceramic slurry;
stacking ceramic green sheets and internal electrode layers to obtain an unfired laminated body; and
firing the unfired laminated body to obtain a laminated body,
wherein the contents of the respective elements in terms of parts by mol are
Ca: 3 parts by mol or more and 15 parts by mol or less,
Mg: 0.01 parts by mol or more and 0.09 parts by mol or less,
R: 2.5 parts by mol or more and 8.4 parts by mol or less, and
Zr: 0.05 parts by mol or more and 3.0 parts by mol or less
with respect to 100 parts by mol of Ti.
11. The method for producing a laminated ceramic capacitor according to claim 10 , wherein the R content in the slurry is 5.7 parts by mol or more and 8.4 parts by mol or less with respect to 100 parts by mol of Ti.
12. The method of producing a laminated ceramic capacitor according to claim 11 , wherein the Mg content in the slurry is at least 0.05 parts by mol and the Zr content in the slurry is 0.5 parts by mol or more and 2.9 parts by mol or less, with respect to 100 parts by mol of Ti.
13. The method for producing a laminated ceramic capacitor according to claim 12 , wherein the slurry further contains Mn, V, and Si,
wherein the contents of the respective elements in terms of parts by mol are
Mn: 0.1 parts by mol or more and 1.0 part by mol or less,
V: 0.05 parts by mol or more and 0.5 parts by mol or less, and
Si: 0.5 parts by mol or more and 2.5 parts by mol or less
with respect to 100 parts by mol of Ti.
14. The method for producing a laminated ceramic capacitor according to claim 13 , wherein the slurry further contains Mn, V, and Si,
wherein the contents of the respective elements in terms of parts by mol are
Mn: 0.1 parts by mol or more and 1.0 part by mol or less,
V: 0.05 parts by mol or more and 0.5 parts by mol or less, and
Si: 0.5 parts by mol or more and 2.5 parts by mol or less
with respect to 100 parts by mol of Ti.
15. The method for producing a laminated ceramic capacitor according to claim 12 , wherein the slurry further contains Mn, V, and Si,
wherein the contents of the respective elements in terms of parts by mol are
Mn: 0.1 parts by mol or more and 1.0 part by mol or less,
V: 0.05 parts by mol or more and 0.5 parts by mol or less, and
Si: 0.5 parts by mol or more and 2.5 parts by mol or less
with respect to 100 parts by mol of Ti.
16. The method for producing a laminated ceramic capacitor according to claim 11 , wherein the slurry further contains Mn, V, and Si,
wherein the contents of the respective elements in terms of parts by mol are
Mn: 0.1 parts by mol or more and 1.0 part by mol or less,
V: 0.05 parts by mol or more and 0.5 parts by mol or less, and
Si: 0.5 parts by mol or more and 2.5 parts by mol or less with respect to 100 parts by mol of Ti.
17. The method for producing a laminated ceramic capacitor according to claim 10 , wherein the slurry further contains Mn, V, and Si,
wherein the contents of the respective elements in terms of parts by mol are
Mn: 0.1 parts by mol or more and 1.0 part by mol or less,
V: 0.05 parts by mol or more and 0.5 parts by mol or less, and
Si: 0.5 parts by mol or more and 2.5 parts by mol or less
with respect to 100 parts by mol of Ti.