Method of producing electrocast belt
Disclosed is a method for producing an electrocast belt which method ensures long-term use of an electrocasting bath and which method enables provision of an electrocast belt having a required product quality even when an electrocasting bath that has been used in electrolysis with a large cumulative amount of electricity. The method includes a first step of producing an electrocast belt having a required product quality in an electrocasting bath of a specific composition until a predetermined period of time has elapsed; a second step of subsequently producing an electrocast belt in the same electrocasting bath; and a third step of polishing a surface of the electrocast belt produced from the second step so that the electrocast belt produced from the third step has a product quality equivalent to that of the electrocast belt produced from the first step.
1. An electrocast belt production method by use of an electrocasting bath, the method comprising:
a first step of producing a first set of electrocast belts having a required product quality without polishing a surface of any of the first set of electrocast belts in an electrocasting bath of a specific composition,
wherein, in the first step, the first set of electrocast belts are produced without polishing a surface thereof, using an electrocasting bath which has been used in electrolysis with a cumulative amount of electricity of 0 kAh or more and less than 1,500 kAh, until the electrocasting bath has been used for a predetermined period whereby a produced electrocast belt fails to have the required product quality, and
a second step of producing a second set of electrocast belts in the electrocasting bath which has been used for the predetermined period in the first step,
wherein, in the second step, each of the electrocast belts of the second set of electrocast belts are produced with polishing a surface thereof, using the electrocasting bath which has been used in electrolysis in the first step with a cumulative amount of electricity of at least 1,500 kAh, so that each of the electrocast belts produced in the second step has the required product quality.
2. The electrocast belt production method according to claim 1 , wherein each electrocast belt has at least one metal layer made of a metal selected from nickel and a nickel alloy.
3. The electrocast belt production method according to claim 1 , wherein the polishing is physical polishing.
4. The electrocast belt production method according to claim 2 , wherein the polishing is physical polishing.
5. The electrocast belt production method according to claim 1 , wherein the polishing is chemical polishing.
6. The electrocast belt production method according to claim 2 , wherein the polishing is chemical polishing.
7. The electrocast belt production method according to claim 1 , wherein the polishing is electro-polishing.
8. The electrocast belt production method according to claim 2 , wherein the polishing is electro-polishing.
9. The electrocast belt production method according to claim 1 , wherein,
during the first step, the electrocasting bath has a cumulative amount of electricity less than a first amount of cumulative electricity, and
during the second step, the electrocasting bath has a cumulative amount of electricity greater than the first amount of cumulative electricity and less than a maximum amount of cumulative electricity.
10. The electrocast belt production method according to claim 1 , wherein, during the second step, the electrocasting bath, which has been used in electrolysis in the first step, has a cumulative amount of electricity of 1,500 kAh to 6,000 kAh.