Addition curable self-adhesive silicone rubber composition
An addition curable self-adhesive silicone rubber composition is provided. This silicone rubber composition comprises (A) 100 parts by weight of an organopolysiloxane containing at least 2 alkenyl groups bonded to silicon atoms per molecule, (B) 0.05 to 10 parts by weight of an organosilicon compound containing 1 to 100 silicon atoms which has at least 1 phenylene skeleton per molecule, and which has at least 1 hydrogen atom bonded to a silicon atom, (C) 0 to 30 parts by weight of an organohydrogenpolysiloxane containing at least 2 hydrogen atoms bonded to silicon atoms per molecule, and containing no phenylene skeleton in the molecule, (D) 0.001 to 0.1 part by weight of a triazole compound, and (E) a catalytic amount of a platinum catalyst. This silicone rubber composition is capable of forming a cured article having good adhesion to various organic resins.
1. An addition curable self-adhesive silicone rubber composition comprising
(A) 100 parts by weight of an organopolysiloxane containing at least 2 alkenyl groups bonded to silicon atoms per molecule,
(B) 0.05 to 10 parts by weight of an organosilicon compound containing 1 to 100 silicon atoms which has at least 1 phenylene skeleton per molecule, and which has at least 1 hydrogen atom bonded to a silicon atom per molecule, but free of an alicyclic epoxy radical,
(C) 0 to 30 parts by weight of an organohydrogenpolysiloxane containing at least 2 hydrogen atoms bonded to silicon atoms per molecule, and containing no phenylene skeleton in the molecule,
(D) 0.001 to 0.1 part by weight of a triazole compound,
(E) a catalytic amount of a platinum catalyst, and
(G) an acetylene alcohol compound or an acetylene alcohol compound having its alcoholic hydroxy group modified with a silane or a siloxane at an amount of 0.001 to 1 part by weight in relation to 100 parts by weight of the component (A).
2. The addition curable self-adhesive silicone rubber composition according to claim 1 further comprising
(F) a reinforcement silica fine powder at an amount of 5 to 100 parts by weight in relation to 100 parts by weight of the component (A).
3. The addition curable self-adhesive silicone rubber composition according to claim 1 wherein content of the component (C) is 0.1 to 30 parts by weight in relation to 100 parts by weight of the component (A).
4. The addition curable self-adhesive silicone rubber composition according to claim 1 wherein a molar ratio of the total amount of the SiH functional group in the component (B) and the component (C) to the amount of the alkenyl group in the component (A) (SiH/alkenyl) is 0.8 to 5.0.
5. The addition curable self-adhesive silicone rubber composition according to claim 1 wherein the 10% curing time T10 (at 110° C. for 3 minutes) is 10 seconds≦T10≦60 seconds, and η 12 /η 0 ≦2 when shear viscosity 0.9 s −1 at 25° C. after storing at 25° C. for 10 minutes after mixing the components (A) to (E) is η 0 , and shear viscosity 0.9 s −1 at 25° C. after storing at 25° C. for 12 hours after mixing the components (A) to (E) is η 12 .
6. The addition curable self-adhesive silicone rubber composition according to claim 1 wherein the composition is the one for adhesion to a thermoplastic resin selected from acrylonitrile-butadiene-styrene (ABS) resin, polycarbonate (PC) resin, polyurethane (PU) resin, styrene resin, polyethylene (PE) resin, polypropylene (PP) resin, acrylic resin, polyethylene terephthalate (PET) resin, polybuthylene terephthalate (PBT) resin, polyphenylene oxide (PPO) resin, polyphenylene sulfide (PPS) resin, polysulfone resin, nylon (PA) resin, aromatic polyamide (aromatic PA) resin, polyimide (PI) resin, and liquid crystal resin.