CMAS resistant thermal barrier coatings
The present application provides Calcia-Magnesia-Alumina-Silica (CMAS) (or molten silicate) resistant thermal barrier coatings (TBC). The coatings include elongate growth domains of non-equiaxed, randomly arranged overlapping grains or splats. The elongate growth domains include overlapping individual, randomly distributed splats of tough and soft phases. In some embodiments, the elongate growth domains are formed via air plasma spray. In some embodiments, the tough phases are at least partially stabilized zirconia and/or hafnia compositions, and the soft phases are CMAS (or molten silicate) reactive or resistant compositions. Within each elongate growth domain, the mixture of the tough and soft phases act together to limit penetration of CMAS and also provide sufficient domain toughness to minimize cracking forces produced during crystallization of infiltrated CMAS. The soft phases may react with the CMAS and increase its melting point, increase its viscosity, and reduce the destabilization of the tough phases.
1. A thermal barrier; coating comprising:
a plurality of elongate material growth domains defined between domain boundaries,
wherein the domains have an intra-domain density of at least about 75%, and comprise individual, randomly distributed splats of tough and soft phases stacked throughout the growth domains, and
wherein the tough phases are at least one of partially stabilized zirconia compositions and partially stabilized hafnia compositions, and the soft phases are at least one of CMAS reactive compositions and CMAS resistant compositions, wherein at least about 75% of the splats of the domains include a width to length aspect ratio of greater than or equal to about 3:1.
2. The thermal harrier coating of claim 1 , wherein the widths of the splats are oriented within the range of about 45 degrees to about 90 degrees with respect to at least one of the direction in which tough and soft phases are stacked and the thickness of the thermal barrier coating.
3. The thermal barrier coating of claim 1 , wherein the domains have a substantially isotropic crystallographic orientation.
4. The thermal barrier coating of claim 1 , wherein the tough phases are at least partially stabilized zirconia compositions that are stabilized by at least one of yttria, magnesia, calcia, ceria, lanthana, neodymia, europia, gadolinia, erbia, dysprosia, ytterbia, scandia, sainaria and lutetia.
5. The thermal barrier coating of claim 1 , wherein the tough phases are at least partially stabilized hafnia that are stabilized by at least one of yttria, magnesia, calcia, ceria, lanthana, neodymia, europia, gadolinia, erhia, dysprosia, ytterbia, scandia, samaria and Iutetia.
6. The thermal barrier coating of claim 1 , wherein the tough phases are 7YSZ and the soft phases are Y203.
7. The thermal barrier coating of claim 1 , wherein the domains have a thickness in the range from about 5 micrometers to about 150 micrometers.
8. The thermal barrier coating of claim 1 , wherein the domains include at least about 75% non-equiaxed grains.
9. The thermal tinnier coating of claim 1 , wherein at least 50% of material present in the domains comprises at least partially melted and solidified particles.
10. The thermal barrier coating of claim 1 , further comprising a plurality of domain boundaries between the domains, wherein a density of the domain boundaries is less than about 25%.
11. The thermal barrier coating of claim 10 , wherein the domain boundaries extend for at least about 50% of a thickness of the coating.
12. The thermal barrier coating of claim 1 , wherein the soft phases are molten silicate resistant compositions.
13. The thermal barrier coating of claim 12 , wherein the soft phases are oxides selected from the group consisting of hafnia, yttria, ytterbia, zirconia, lanthana, ceria and alumina.
14. The thermal barrier coating of claim 12 , wherein the soft phases are at least one of gadolinia and zirconia with a cubic crystal structure.
15. The thermal harrier coating of claim 12 , wherein the soft phases are at least one material with a cubic pyrochlore structure.
16. The thermal barrier coating of claim 12 , wherein the soft phases are selected from the group consisting of:
at least one of zirconia, hafnia and titania, which are stabilized with a rare earth material;
at least one oxide of aluminum, calcium, magnesium, silicon, tantalum, titanium, cerium, praseodymium, neodymium, promethium, samarium, europium, terbium, dysprosium, holmium, erbium, thulium, yttrium, ytterbium, lutetium, scandium, indium, hafnium, gadolinium and mixtures thereof;
at least one sodium containing compound selected from the group consisting of sodium oxide, sodium silicate, sodium titanate and mixtures thereof;
at least one garnet;
at least one titanate mixed with at least one oxide;
at least one metal carbide;
at least one metal nitride;
at least one metal silicide; and
3-70 mol % gadolinia, balance hafina.
17. An article for use at elevated temperatures, comprising:
a substrate; and
a thermal bailer coating according to claim 1 disposed on the substrate.