One coat painting composition for high gloss and coating method thereof
Disclosed is a one coat painting composition comprising a base including a polyester resin in an amount of about 15 to 45 wt %, a first acrylic resin in an amount of about 15 to 25 wt %, and a second acrylic resin in an amount of about 35 to 65 wt % and a coating method thereof. The composition makes it possible to maintain and improve a high gloss finish of a high gloss injection molded substrate through a single primary coating on the substrate and satisfies environment resistant properties of exterior parts, such as adhesiveness, weather resistance, and scratch resistance, and, thus, is widely suitable for use on exterior plastic parts of automobiles.
1. A one coat painting composition for providing a high gloss finish comprising:
100 parts by weight of a base;
about 1.0 to 1.5 parts by weight of a reaction catalyst;
about 0.1 to 1.0 part by weight of a wetting additive;
about 1.0 to 1.5 parts by weight of photostabilizer; and
a solvent;
wherein the base comprises about 15 to 45 wt % of a polyester resin, about 15 to 25 wt % of a first acrylic resin, and about 35 to 65 wt % a second acrylic resin, wherein the amounts of polyester resin, the first acrylic resin, and the second acrylic resin total 100 wt % of the base.
2. The one coat painting composition of claim 1 wherein:
the reaction catalyst is a urethane reaction catalyst;
the wetting additive is a polyester siloxane-based wetting additive; and
the photostabilizer is a UV absorber.
3. The one coat painting composition of claim 1 , wherein the polyester resin has a weight-average molecular weight of about 3000 to about 10000, a hydroxyl group content of about 2 to 4 mol %, and a solid content of 80 wt % with respect to the total weight of the polyester resin.
4. The one coat painting composition of claim 1 , wherein the polyester resin is produced through a condensation reaction between an alcohol compound and an acid; wherein the alcohol compound is at least one of diethylene glycol and methylpropanediol; and wherein the acid is at one of adipic acid and isophthalic acid.
5. The one coat painting composition of claim 1 , wherein the first acrylic resin has a weight-average molecular weight of about 6000 to about 15000, an acid value of about 2 to 6 mg KOH/g, a hydroxyl group content of about 1 to 5 mol %, a glass transition temperature of about 20 to 30° C., and a solid content of about 60 wt % or more based on total weight of the first acrylic resin.
6. The one coat painting composition of claim 1 , wherein the second acrylic resin has a weight-average molecular weight of about 6000 to 15000, an acid value of about 0.5 to 2 mg KOH/g, a hydroxyl group content of about 0.2 to 2 mol %, a glass transition temperature of 70 to 80° C., and a solid content of 40 wt % or more based on total weight of the second acrylic resin.
7. A coating method comprising: adding a curing agent to the one coat painting composition of claim 1 to form a curable painting composition; applying the curable painting composition to a substrate; and curing the applied curable painting composition.
8. The coating method of claim 7 , wherein the reaction catalyst is a urethane reaction catalyst comprising a hydroxyl group as a main component, and the curing agent is a hexamethylene diisocyanate trimer-based agent.
9. The coating method of claim 8 , wherein the curing agent is present in an amount such that a ratio of the curing agent to hydroxyl group is about 1:2 to 1:4 wt %.