Cement composition based on calcium aluminate cement
The present invention relates to a current composition for cementing oil or gas wells. The composition comprises calcium aluminate cement in which the proportion of HC 2 0 3 is at least 50% by weight, dispersant, microsilica, mineral particles, water and optionally a retarder.
1. A cement composition for cementing oil and gas wells comprising:
35-50% by weight of dry components of calcium aluminate cement in which the proportion of Al 2 O 3 is at least 50% by weight,
dispersant,
20-25% by weight of dry components of microsilica,
5-30% by weight of dry components of mineral particles selected from the group consisting of silica flour and alumina,
water, and
optionally a retarder.
2. The cement composition as claimed in claim 1 , in which the dispersant is selected from the group consisting of sodium phosphate salts.
3. The cement composition as claimed in claim 2 , in which the dispersant is selected from the group consisting of sodium hexa metaphosphate (SHMP), sodium tripolyphosphate (STPP), sodium trimetaphosphate (STMP) and combinations thereof.
4. The cement composition as claimed in claim 1 , in which the dispersant is present at a concentration in the range 0.05-0.4% by weight of the dry components.
5. The cement composition as claimed in claim 4 , in which the dispersant is present at a concentration in the range 0.2-0.5% by weight of the dry components.
6. The cement composition as claimed in claim 1 , in which the retarder is selected from the group consisting of hydroxycarboxilic acids.
7. The cement composition as claimed in claim 6 , wherein the hydroxycarboxilic acids is selected from the group consisting of citric, tartaric, gluconic acids and their salts, boric acid and its salt, sodium chloride, sodium nitrate, ethylenediamine, tetraacetic disodium salt, potassium sulfate and potassium chloride.
8. The cement composition as claimed in claim 7 , in which the retarder is citric acid.
9. The cement composition as claimed in claim 1 , in which the retarder is present in the range 0-1% by weight of the dry components.
10. The cement composition as claimed in claim 9 , in which the retarder is present in the range 0.001-1% by weight of the dry composition.
11. The cement composition as claimed in claim 1 , in which the composition further comprises hollow microspheres.
12. The cement composition as claimed in claim 11 , in which the hollow microspheres are glass microspheres or cenospheres.
13. The cement composition as claimed in claim 11 , in which the hollow microspheres are present in the range 0-30%, by weight of the dry components.
14. The cement composition as claimed in claim 1 , in which the composition further comprises fiber.
15. The cement composition as claimed in claim 14 , in which the fiber is selected from the group consisting plastics and cellulose.
16. The cement composition as claimed in claim 15 , in which the plastic fiber is selected from the group consisting of polypropylene, polyvinyl acetate and polyethylene.
17. The cement composition as claimed in claim 14 , in which the fiber is present in the range 0-5% by weight of the dry components.
18. The cement composition as claimed in claim 1 , in which the composition further comprises weighting agents.
19. The cement composition as claimed in claim 18 , in which the weighting agents are selected from the group consisting of barite, hematite, siderite, dolomite, manganomanganic oxide, ilmenite and calcium carbonate.
20. The cement composition as claimed in claim 18 , in which the weighting agent is present in the range 0-70% by weight of the dry components.
21. The cement composition as claimed in claim 1 , in which the composition further comprises an elastomeric powder.
22. The cement composition as claimed in claim 21 , in which the elastomeric powder is selected from the group consisting of rubber powder and surface modified pre-crosslinked copolymer of butadiene-acrylonitrite partitioned with calcium carbonate.
23. The cement composition as claimed in claim 21 , in which the elastomeric powder is present in the range 0-6% by weight of the dry components.
24. The cement composition as claimed in claim 11 , in which the hollow microspheres are present in the range 15-25% by weight of the dry components.
25. The cement composition as claimed in claim 14 , in which the fiber is present in the range 1-3% by weight of the dry components.
26. The cement composition as claimed in claim 18 , in which the weighting agent is present in the range 0-5% by weight of the dry components.
27. The cement composition as claimed in claim 21 , in which the elastomeric powder is present in the range 0.15-0.3% by weight of the dry components.