Thermal spray material and process for preparing same
A thermal spray material includes granules of an oxyfluoride of yttrium (YOF). The granules may contain a fluoride of yttrium (YF 3 ). The granules preferably have an oxygen content of 0.3 to 13.1 mass %. The granules preferably have a fracture strength of 0.3 MPa or more and less than 10 MPa. Part of yttrium (Y) of the granules may be displaced with at least one rare earth element (Ln) except yttrium, the molar fraction of Ln relative to the sum of Y and Ln being preferably 0.2 or less.
1. A thermal spray material, comprising:
a granule containing an oxyfluoride of yttrium (YOF), wherein
the granule is a granulated material formed by granulating particles containing oxyfluoride of yttrium and having D 50 of about 0.3 to 5 μm as measured using a laser diffraction/scattering particle size distribution analyzer, and the granule has an average particle size of 20 to 200 μm.
2. The thermal spray material according to claim 1 , wherein the granule further contains a fluoride of yttrium (YF 3 ).
3. The thermal spray material according to claim 1 , wherein the granule has a total oxygen content of 0.3% to 13.1% by mass.
4. The thermal spray material according to claim 1 , having a fracture strength of 0.3 MPa or more and less than 10 MPa.
5. The thermal spray material according to claim 1 , wherein part of yttrium (Y) is displaced with at least one rare earth element (Ln) except yttrium, the molar fraction of Ln relative to the sum of Y and Ln being 0.2 or less.
6. The thermal spray material according to claim 1 , wherein the rare earth element (Ln) except yttrium is at least one member selected from the group consisting of samarium (Sm), gadolinium (Gd), dysprosium (Dy), erbium (Er), and Ytterbium (Yb).
7. A process for producing the thermal spray material according to claim 1 , comprising:
step 1, firing fluoride of yttrium (YF 3 ) in an oxygen-containing atmosphere at 750° to 1100° C. to obtain an oxyfluoride of yttrium (YOF);
step 2, grinding the oxyfluoride of yttrium (YOF) obtained in step 1;
step 3, mixing the ground oxyfluoride of yttrium obtained in step 2 with a solvent to prepare a slurry;
step 4, granulating the slurry obtained in step 3 using a spray dryer; and
step 5; firing the granule obtained in step 4 at 300° to 900° C. to obtain granular oxyfluoride of yttrium (YOF).
8. The process according to claim 7 , wherein the fluoride of yttrium (YF 3 ) used in step 1 is obtained by wet synthesis.
9. The process according to claim 7 , wherein the oxygen-containing atmosphere is air.
10. The process according to claim 7 , wherein the oxyfluoride of yttrium (YOF) obtained in step 1 is subjected, either directly or after dry-grinding, to wet-grinding in step 2 to obtain a slurry of the oxyfluoride of yttrium (YOF).
11. The process according to claim 7 , wherein in step 1 the fluoride of yttrium (YF 3 ) is fired to obtain an oxyfluoride of yttrium (YOF) containing yttrium fluoride (YF 3 ).
12. The process according to claim 7 , wherein the fluoride of yttrium (YF 3 ) used in step 1 has part of yttrium (Y) displaced with at least one rare earth element (Ln) except yttrium.
13. The process according to claim 12 , wherein the rare earth element (Ln) except yttrium is at least one member selected from samarium (Sm), gadolinium (Gd), dysprosium (Dy), erbium (Er), and Ytterbium (Yb).
14. The thermal spray material according to claim 2 , wherein the granule has a total oxygen content of 0.3% to 13.1% by mass.
15. The thermal spray material according to claim 2 , having a fracture strength of 0.3 MPa or more and less than 10 MPa.
16. The thermal spray material according to claim 3 , having a fracture strength of 0.3 MPa or more and less than 10 MPa.
17. The thermal spray material according to claim 2 , wherein part of yttrium (Y) is displaced with at least one rare earth element (Ln) except yttrium, the molar fraction of Ln relative to the sum of Y and Ln being 0.2 or less.
18. The thermal spray material according to claim 3 , wherein part of yttrium (Y) is displaced with at least one rare earth element (Ln) except yttrium, the molar fraction of Ln relative to the sum of Y and Ln being 0.2 or less.
19. The thermal spray material according to claim 4 , wherein part of yttrium (Y) is displaced with at least one rare earth element (Ln) except yttrium, the molar fraction of Ln relative to the sum of Y and Ln being 0.2 or less.
20. The thermal spray material according to claim 2 , further comprising at least one rare earth element (Ln) except yttrium, which is at least one member selected from the group consisting of samarium (Sm), gadolinium (Gd), dysprosium (Dy), erbium (Er), and Ytterbium (Yb).
21. The thermal spray material according to claim 2 , wherein an x-ray diffraction pattern of the thermal spray material has a YF3 peak at 28 2θ(o) with an intensity of 2250 cps, said YF3 peak having a YOF shoulder with an intensity of 500 cps.