Process for the mineralization of carbon dioxide
A process for the mineralization of carbon dioxide to form a magnesium carbonate compound, which process includes contacting the carbon dioxide, in the free form, or in the form of an alkali metal carbonate or bicarbonate, with an alkali metal magnesium silicate to produce the magnesium carbonate compound.
1. A process for the mineralization of carbon dioxide to form a magnesium carbonate compound, which comprises preparing an alkali metal magnesium silicate by reacting, in the solid state and at 500-1100° C., an alkali metal carbonate compound which compound is an alkali metal carbonate, an alkali metal bicarbonate or a mixture thereof, with a magnesium silicate, wherein the molar ratio of alkali metal carbonate compound to magnesium silicate is from 2:1 to 1:2, wherein the alkali metal carbonate compound in the molar ratio is expressed as alkali metal oxide of the formula R 2 O, in which R represents an alkali metal, and wherein the magnesium silicate in the molar ratio is expressed as silicon dioxide of the formula SiO 2 , which reaction produces an alkali metal magnesium silicate, and contacting the carbon dioxide, in the free form or in the form of an alkali metal bicarbonate or carbonate, with an alkali metal magnesium silicate to produce the magnesium carbonate compound.
2. A process according to claim 1 in which the carbon dioxide is in the free form in a gas comprising carbon dioxide.
3. A process according to claim 1 in which the carbon dioxide is in the form of an alkali metal carbonate or bicarbonate formed by contacting a gas comprising carbon dioxide with an alkali metal hydroxide or an alkali metal carbonate.
4. A process according to claim 1 in which the reaction is effected at a temperature of 800 to 950° C.
5. A process according to claim 1 in which the magnesium silicate is of the general formula m(MgO).SiO 2 .xH 2 O wherein m is from 0.5 to 3 and x is from zero to 2.