Adhesive sheet
An adhesive sheet of the invention includes a substrate and an adhesive composition laminated thereon, the substrate including polyvinyl chloride and a polyester-based plasticizer, wherein the adhesive composition includes two different (meth)acrylate copolymer components (A) and (B) in a mass ratio ranging from 10:90 to 90:10, wherein a content of a cross-linking agent which reacts with functional groups of the component (A) and the component (B) is in a range of 0.5 to 20 mass parts with respect to 100 mass parts of a sum of the component (A) and the component (B), and wherein 10 to 95 mass % of the monomer unit composing the component (A) is 2-ethylhexyl acrylate, and 10 to 95 mass % of the monomer unit composing the component (B) is butyl acrylate.
1. An adhesive sheet for dicing and/or conveying, comprising a substrate and an adhesive composition laminated thereon, the substrate including polyvinyl chloride and a polyester-based plasticizer,
wherein said adhesive composition includes a (meth)acrylate copolymer component (A) with a weight-average molecular weight lower than 350,000 having a functional group-containing monomer unit; and a (meth)acrylate copolymer component (B) with a weight-average molecular weight of 350,000 to 2,000,000 having a functional group-containing monomer unit, in a mass ratio ranging from 10:90 to 90:10, wherein a content of a cross-linking agent which reacts with functional groups of said component (A) and said component (B) is in a range of 0.5 to 20 mass parts with respect to 100 mass parts of a sum of said component (A) and said component (B), and
wherein 10 to 95 mass % of said monomer unit composing said component (A) is 2-ethylhexyl acrylate, and 10 to 95 mass % of said monomer unit composing said component (B) is butyl acrylate.
2. An adhesive sheet of claim 1 , wherein a content of said polyester-based plasticizer in said substrate is 20 to 50 mass parts with respect to 100 mass parts of polyvinyl chloride.
3. An adhesive sheet of claim 1 , wherein said polyester-based plasticizer is an adipic acid-based polyester.
4. An adhesive sheet of claim 1 , wherein glass-transition temperatures of said component (A) and said component (B) are 0° C. or below.