Phosphonate flame-retardant polyester artificial hair and method of preparing same
A flame-retardant polyester artificial hair filaments is provided which comprises: (A) 100 parts by weight of a thermoplastic polyester resin; (B) 10-30 parts by weight of a polymeric phosphorus-based flame retardant; (C) 0.1-3 parts by weight of a chain extender; and (D) 0.5-3 parts by weight of sodium antimonate. The polymeric phosphorus-based flame retardant (B) may be a flame retardant having a repeat unit of formula 1 and a weight-average molecular weight ranging from 80,000 to 150,000. The flame-retardant polyester artificial hair filaments can be prepared by: extruding a composition comprising a mixture of a polyester resin, a polymeric phosphorus-based flame retardant, a chain extender and sodium antimonate to form a pellet; drying the pellet to a water content of 500 ppm or less; melt-spinning the dried pellet to prepare a undrawn yarn; drawing the undrawn yarn at a draw ratio of 2-5; and heat-treating the drawn yarn in a heat treatment device heated to a temperature of 150˜280° C.
1. A flame-retardant polyester artificial hair filaments, which comprises:
(A) 100 parts by weight of a thermoplastic polyester resin;
(B) 10-30 parts by weight of a polymeric phosphorus-based flame retardant, wherein the polymeric phosphorus-based flame retardant is a flame retardant having a repeat unit of the following Formula 1 and a weight-average molecular weight ranging from 80,000 to 150,000:
wherein Ar is an aromatic group, each X is, independently, a C 1-20 alkyl, a C 2-20 alkene, a C 2-20 alkyne, a C 5-20 cycloalkyl, or a C 6-20 aryl, and n is an integer ranging from 1 to 100;
(C) 0.1-3 parts by weight of a chain extender; and
(D) 0.5-3 parts by weight of sodium antimonate.
2. The flame-retardant polyester artificial hair filaments of claim 1 in which said polyester resin (A) is selected from the group consisting of polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polypropylene terephthalate (PPT), polycyclohexanedimethanol terephthalate (PCT), and polynaphthalene terephthalate (PEN).
3. The flame-retardant polyester artificial hair filaments of claim 1 in which said sodium antimonate (D) is a compound having an average particle diameter of 0.1-1.0 μm and is represented by Formula 3: Na 2 SbO 3 •nH 2 O.
4. The flame-retardant polyester artificial hair filaments of claim 1 which further comprise an inorganic quencher, a thermal stabilizer, a light stabilizer, a UV stabilizer, a fluorescent agent, an antioxidant, an antistatic agent, a pigment, a dye, a plasticizer, a lubricant, a flame retardant, a flame retardant aid, or an inorganic filler.
5. The flame-retardant polyester artificial hair filaments of claim 1 which has a fineness of 40-100 denier.
6. A wig prepared with the flame-retardant polyester artificial hair filaments of claim 1 .
7. A method of flame-retardant polyester artificial hair filaments, which comprises:
extruding a composition comprising a mixture of a polyester resin, a polymeric phosphorus-based flame retardant, a chain extender and sodium antimonate to form pellets, wherein the polymeric phosphorus-based flame retardant is a flame retardant having a repeat unit of the following Formula 1 and a weight-average molecular weight ranging from 80,000 to 150,000:
wherein Ar is an aromatic group, each X is, independently, a C 1-20 alkyl, a C 2-20 alkene, a C 2-20 alkyne, a C 5-20 cycloalkyl, or a C 6-20 aryl, and n is an integer ranging from 1 to 100;
drying the pellets to a water content of 500 ppm or less;
melt-spinning the dried pellets to prepare undrawn yarn;
drawing the undrawn yarn at a draw ratio of 2-5; and
heat-treating the drawn yarn in a heat treatment device heated to a temperature of 150˜280° C.
8. A flame-retardant polyester artificial hair filaments, which comprises:
(A) 100 parts by weight of a thermoplastic polyester resin;
(B) 10-30 parts by weight of a polymeric phosphorus-based flame retardant;
(C) 0.1-3 parts by weight of a chain extender, wherein the chain extender is a compound of Formula 2, which contains an epoxy group and comprises a copolymer based on styrene, acrylate or methacrylate:
wherein each of R 1 to R 5 are each, independently, hydrogen or an alkyl group, R 6 is an alkyl group, and x, y and z are each, independently, an integer ranging from 1 to 20; and
(D) 0.5-3 parts by weight of sodium antimonate.
9. The flame-retardant polyester artificial hair filaments of claim 8 in which said polyester resin (A) is selected from the group consisting of polyethylene terephthalate (PET), polybutylene terephthalate (PBT), polypropylene terephthalate (PPT), polycyclohexanedimethanol terephthalate (PCT), and polynaphthalene terephthalate (PEN).
10. The flame-retardant polyester artificial hair filaments of claim 8 in which said sodium antimonate (D) is a compound having an average particle diameter of 0.1-1.0 μm and is represented by Formula 3: Na 2 SbO 3 •nH 2 O.
11. The flame-retardant polyester artificial hair filaments of claim 8 which further comprise an inorganic quencher, a thermal stabilizer, a light stabilizer, a UV stabilizer, a fluorescent agent, an antioxidant, an antistatic agent, a pigment, a dye, a plasticizer, a lubricant, a flame retardant, a flame retardant aid, or an inorganic filler.
12. The flame-retardant polyester artificial hair filaments of claim 8 which has a fineness of 40-100 denier.
13. A wig prepared with the flame-retardant polyester artificial hair filaments of claim 8 .