Biodegradable, magnesium-containing bone screws, methods for their preparation and medical applications therefor
The invention relates to a biodegradable, magnesium-containing bone screw for implanting into a patient body for use in medical applications, such as, orthopedic, craniofacial and cardiovascular surgery. The bone screw has a head, shaft and tip. The thickness of the head is greater than the thickness of conventional bone screws. The shaft includes both a non-threaded and a threaded portion. The tip is non-threaded and pointed, such as, conical in shape. The composition of the bone screws provide for improved biodegradability and biocompatibility, and the features of the structure of the bone screws facilitate guidance and placement during implantation as well as reduce the potential for mechanical failures.
1. A biodegradable bone screw, comprising:
a magnesium-based alloy;
a cylindrical head having a first diameter, comprising:
a circular top, planar surface;
a circular bottom, planar surface; and
a thickness extending between the circular top and circular bottom, planar surfaces;
a non-threaded, conical, pointed tip; and
a cylindrical, non-tapered shaft having a circumference, comprising:
a first end having a circular, planar surface coupled to the circular bottom, planar surface of the head such that the shaft extends straight outwardly from the bottom, planar surface of the head;
a vertical length extending along a surface of the shaft from the first end to the non-threaded, conical, pointed tip;
a second diameter smaller than the first diameter of the cylindrical head;
a transition point;
a continuous non-threaded portion along an entire portion of the vertical length of the shaft extending from the bottom, planar surface of the head to the transition point,
wherein the second diameter is continuous from the bottom, planar surface of the head to the transition point; and
a circumferentially continuous threaded portion consisting of continuous threads disposed about the circumference along an entire portion of the vertical length of the shaft extending from the transition point to the non-threaded, conical, pointed tip.
2. The bone screw of claim 1 , wherein the circular top, planar surface of the head has an indentation diametrically formed therein, the indentation having a length and height that is suitable to accommodate a driver mechanism for rotating and guiding the bone screw.
3. The bone screw of claim 2 , wherein the length of the indentation extends along an entire or nearly entire diameter of the head.
4. The bone screw of claim 1 , wherein the non-threaded portion of the length of the shaft is less than the threaded portion of the length of the shaft.
5. The bone screw of claim 1 , wherein said magnesium-based alloy comprises at least one element selected from the group consisting of iron, zirconium, manganese, calcium, yttrium and zinc, optionally one or more elements selected from the group consisting of aluminum, silver, cerium and strontium, and a remainder of magnesium.
6. The bone screw of claim 1 , wherein the thickness of the cylindrical head is from about 0.96 mm to about 1.04 mm, and wherein the first diameter is from about 1.92 mm to about 2.08 mm.
7. The bone screw of claim 1 , wherein the first diameter is two times the thickness.
8. The bone screw of claim 6 , wherein the first diameter is two times the thickness.
9. The bone screw of claim 1 , wherein the magnesium-based alloy comprises:
from about 0.5 to about 4.0 weight percent yttrium;
from greater than 0 to about 1.0 weight percent calcium;
from about 0.25 to about 1.0 weight percent zirconium; and
a remainder of magnesium.
10. The bone screw of claim 1 , where the magnesium-based alloy comprises:
from about 1.0 to about 6.0 weight percent zinc;
from greater than 0 to about 1.0 weight percent zirconium; and
a remainder of magnesium.
11. The bone screw of claim 9 , wherein the magnesium-based alloy further comprises one or more elements selected from the group consisting of silver, cerium and strontium.