Method of preparing a coating composition comprising submicron calcium carbonate
Coating composition providing gloss and opacity on application, having a pigment volume concentration of from 5% up to the critical pigment volume concentration and characterised in that comprises at least one ground natural calcium carbonate having a volume median diameter of between 0.05 and 0.3 μm, and at least one pigment having a refractive index of greater than or equal to 2.5.
1. A process for preparing a glossing and opacifying coating composition comprising:
mixing, with glossing and opacifying coating composition components, at least one submicron ground natural calcium carbonate (SMGCC) having a volume median particle diameter d 50 of 0.05 to 0.3 μm and a d 98 of less than or equal to 0.6 μm, and titanium dioxide, at a titanium dioxide:SMGCC weight ratio from 75:25 to 98:2, to obtain a glossing and opacifying coating composition having a pigment volume concentration (PVC) of from 5% up to a critical pigment volume concentration (CPVC),
and wherein the glossing and opacifying coating composition, applied to a contrast card to form a layer having a thickness of 150 μm or 300 μm, has a gloss that is within ±3% of the gloss of the same composition and thickness in which the SMGCC is fully replaced with the titanium dioxide, when gloss is measured either at a 60° or an 85° incident angle according to DIN 67530.
2. The process according to claim 1 , wherein the SMGCC is provided in the form of an aqueous suspension or dispersion.
3. The process according to claim 1 , wherein the glossing and opacifying coating composition components comprises at least one resin.
4. The process according to claim 3 , wherein the resin is a latex and/or acrylate-based binder.
5. The process according to claim 4 , wherein the acrylate-based binder is in the form of an aqueous emulsion.
6. The process according to claim 1 , wherein the glossing and opacifying coating composition has a PVC of from 10 to 30 vol.-%.
7. The process according to claim 1 , wherein the glossing and opacifying coating composition has a PVC of from 15 to 25 vol.-%.
8. The process according to claim 1 , wherein the glossing and opacifying coating composition has a PVC of from 17 to 21 vol.-%.
9. The process according to claim 1 , wherein the SMGCC has a volume median diameter d 50 of 0.08 to 0.3 μm.
10. The process according to claim 1 , wherein the SMGCC has a volume median diameter d 50 of 0.1 to 0.2 μm.
11. The process according to claim 1 , wherein the SMGCC has a d 98 /d 50 of greater than 3.
12. The process according to claim 1 , wherein the SMGCC has a d 98 of less than or equal to 0.4 μm.
13. The process according to claim 1 , wherein the titanium dioxide:SMGCC weight ratio is from 75:25 to 90:10.
14. The process according to claim 1 , wherein the titanium dioxide:SMGCC weight ratio is from 80:20 to 85:15.
15. The process according to claim 1 , wherein the glossing and opacifying coating composition components are selected from the group consisting of one or more of a resin, a binder, a pigment, a defoamer, a levelling agent, a flatting agent, a preservative, an optical brightener, a light stabilizer, a reheological additive, a thickener, a dispersant, a solvent, a filler, an anti-settling agent, a surfactant, a metal, and a UV absorber.