Conductive paste used for solar cell electrodes
View Patent ↗The present invention is directed to a conductive paste used for solar cell electrodes comprising, (i) 60 wt % to 95 wt % of a conductive powder, based on the total weight of the conductive paste, (ii) 0.1 wt % to 10 wt % of a lead-tellurium-oxide powder, based on the total weight of the conductive paste, comprising 20 wt % to 60 wt % of PbO and 20 wt % to 60 wt % of TeO 2 , based on the total weight of the lead-tellurium-oxide powder, (iii) 3 wt % to 38 wt % of an organic medium, based on the total weight of the conductive paste, and (iv) 0.01 wt % to 5.0 wt % of lithium oxide powder selected from the group consisting of LiMnO 3 , Li 2 WO 4 , Li 2 CO 3 , Li 2 TiO 3 , Li 4 Ti 5 O 12 , Li 2 MoO 4 and a mixture thereof, based on the total weight of the conductive paste.
1. A conductive paste used for solar cell electrodes comprising,
(i) 60 wt % to 95 wt % of a conductive powder, based on the total weight of the conductive paste,
(ii) 0.1 wt % to 10 wt % of a lead-tellurium-oxide powder, based on the total weight of the conductive paste, comprising 20 wt % to 60 wt % of PbO and 20 wt % to 60 wt % of TeO 2 , based on the total weight of the lead-tellurium-oxide powder,
(iii) 3 wt % to 38 wt % of an organic medium, based on the total weight of the conductive paste,
(iv) 0.01 wt % to 5.0 wt % of lithium oxide powder selected from the group consisting of LiMnO 3 , Li 2 WO 4 , Li 2 TiO 3 , Li 4 Ti 5 O 12 , Li 2 MoO 4 and a mixture thereof, based on the total weight of the conductive paste.
2. The conductive paste of claim 1 , wherein the conductive paste further comprising a bismuth-based glass frit comprising no less than 50 wt % of Bi 2 O 3 , based on the total weight of the bismuth-based glass frit.
3. The conductive paste of claim 2 , wherein the bismuth-based glass frit has a weight percentage of 0.01 wt % to 1.0 wt %, based on the total weight of the conductive paste.
4. The conductive paste of claim 2 , wherein the bismuth-based glass frit further comprises ZnO, B 2 O 3 or a mixture thereof.
5. The conductive paste of claim 1 , further comprising a metal resinate selected from the group consisting of lead resinate, barium resinate, calcium resinate, bismuth resinate, manganese resinate and a mixture thereof.
6. The conductive paste of claim 1 , further comprising a metal oxide powder selected from the group consisting of cobalt(II) oxide, zinc oxide, magnesium oxide, chromium oxide, copper(II) oxide, Iron(III) oxide and a mixture thereof.
7. The conductive paste of claim 1 , wherein the mean particle size (D50) of the lithium oxide powder is 0.1 μm to 5.0 μm.
8. The conductive paste of claim 1 , wherein the specific surface area (SPA) of the lithium oxide powder is in the range of 10000 to 150000 cm 2 /cm 3 .