Conjugated gold nanoparticles
The present invention relates to methods, compositions, and kits for generating conjugated gold nanoparticles. In certain embodiments, the present invention provides methods of generating unsaturated conjugated gold nanoparticles by mixing naked gold nanoparticles with a first type of attachment molecules at a molar ratio such that the attachment molecules attach to the naked gold particles at a density level below the saturation level of the naked gold particles (e.g., at a saturation level of 1-99%). In some embodiments, a second type of attachment molecules (e.g., with the opposite charge as the first type of attachment molecules) are mixed with the unsaturated conjugated gold nanoparticles to generate double-conjugated gold nanoparticles (e.g., that are zwitterionic).
1. A method for making conjugated gold nanoparticles comprising:
a) providing:
i) naked gold nanoparticles, wherein each of said naked gold nanoparticles has an gold surface, and wherein at least 90% of said gold surface is exposed and not attached to any molecules, and
ii) first type of attachment molecules having the formula R1-polymer-R2, wherein R1 is a moiety having affinity for said gold surface of said naked gold nanoparticles, and wherein R2 is a functional group that allows attachment to other chemicals, and/or comprises a targeting ligand, and
iii) second type of attachment molecules having the formula R3-polymer-R4, wherein R3 is a moiety having affinity for said gold surface, and wherein R4 is a functional group that allows attachment to other chemicals, and/or comprises a targeting ligand, and
wherein either: A) said first type of attachment molecules possess a positive charge and said second type of attachment molecules possess a negative charge, or B) said first type of attachment molecules posses a negative charge and said second type of attachment molecules posses a positive charge;
b) mixing said first type of attachment molecules with said naked gold nanoparticles in a first molar ratio of said first type of attachment molecules to said naked gold nanoparticles such that said first type of attachment molecules attach to said naked gold nanoparticles at a density level below the saturation level for said naked gold nanoparticles thereby generating unsaturated conjugated gold nanoparticles; and
c) mixing said second type of attachment molecules with said unsaturated conjugated gold nanoparticles in a second molar ratio of said second type of attachment molecules to said unsaturated conjugated gold particles such that said second type of attachment molecules attach to said unsaturated conjugated gold nanoparticles thereby generating double-conjugated gold nanoparticles, and
wherein said double-conjugated gold nanoparticles posses a ratio of negative to positive attachment molecules of 900/100 to 700/300.
2. The method of claim 1 , further comprising providing a third type of attachment molecules having the formula R5-polymer-R6, wherein R5 is a moiety having affinity for said gold surface of said double-conjugated gold nanoparticles, and wherein R6 is a functional group that allows attachment to other chemicals, and/or comprises a targeting ligand, and step d) mixing said third type of attachment molecules with said double-conjugated gold nanoparticles in a third molar ratio of said third type of attachment molecules to said double-conjugated gold particles such that said third type of attachment molecules attach to said double-conjugated gold nanoparticles thereby generated third-conjugated gold nanoparticles.
3. The method of claim 1 , wherein said R1 is the same or different on each of said first type of attachment molecules and is selected from the group consisting of: a thiol group, an amine group, a phosphine group, and a disulfide group.
4. The method of claim 1 , wherein said R3 is the same or different on each of said second type of attachment molecules and is selected from the group consisting of: a thiol group, an amine group, a phosphine group, and a disulfide group.
5. The method of claim 1 , wherein said polymer in said first type of attachment molecules comprises polyethylene glycol.
6. The method of claim 1 , wherein said polymer in said first type of attachment molecules is selected from the group consisting of: polyethyleneglycol (PEG), polyacrylamide, polydecylmethacrylate, polystyrene, dendrimer molecule, polycaprolactone (PCL), polylactic acid (PLA), poly(lactic-co-glycolic acid) (PLGA), polyglycolic acid (PGA), polyhydroxybutyrate (PHB), and the said polymer has degree of polymerization in the range from 1 unit to 100 units.
7. The method of claim 1 , wherein said polymer in said second type of attachment molecules comprises polyethylene glycol.
8. The method of claim 1 , wherein said polymer in said second type of attachment molecules is selected from the group consisting of: polyethyleneglycol (PEG), polyacrylamide, polydecylmethacrylate, polystyrene, dendrimer molecule, polycaprolactone (PCL), polylactic acid (PLA), poly(lactic-co-glycolic acid) (PLGA), polyglycolic acid (PGA), polyhydroxybutyrate (PHB), and the said polymer has degree of polymerization in the range from 1 unit to 100 units.
9. The method of claim 1 , wherein said R2 is selected from the group consisting of COOH, —OCH3, and —NH2.
10. The method of claim 1 , wherein said R4 is selected from the group consisting of COOH, —OCH3, and —NH2.
11. The method claim 1 , wherein at least 93% of said gold surface of each of said naked gold nanoparticles is exposed and not attached to any molecules.
12. The method of claim 1 , wherein said naked gold nanoparticles are in a colloidal suspension.
13. The method of claim 1 , wherein said naked gold nanoparticles are pulse laser ablation generated naked gold nanoparticles.