Ternary ceramic thermal spraying powder and method of manufacturing thermal sprayed coating using said powder
The invention describes a method for producing ternary and binary ceramic powders and their thermal spraying capable of manufacturing thermal sprayed coatings with superior properties. Powder contain at least 30% by weight ternary ceramic, at least 20% by weight binary molybdenum borides, at least one of the binary borides of Cr, Fe, Ni, W and Co and a maximum of 10% by weight of nano and submicro-sized boron nitride. The primary crystal phase of the manufactured thermal sprayed coatings from these powders is a ternary ceramic, while the secondary phases are binary ceramics. The coatings have extremely high resistance against corrosion of molten metal, extremely thermal shock resistance and superior tribological properties at low and at high temperatures.
1. A thermal spray powder comprising:
20-70% by weight one or more ternary boride ceramics of Metal-Mo—B, Metal-Mo 2 —B 2 , or Metal 2 -Mo 2 —B 2 , where Metal is Ni or Fe;
20-60% by weight one or more binary molybdenum borides; and,
0-50% by weight one or more metal binary borides, where the metals of the one or more metal binary borides are selected from Cr, Fe, and Ni.
2. A thermal spray powder comprising:
20-70% by weight one or more ternary boride ceramics of Metal-Mo—B, Metal-Mo 2 —B 2 , or Metal 2 -Mo 2 —B 2 , where Metal is Ni or Fe;
0-60% by weight one or more binary molybdenum borides; and,
10-50% by weight one or more metal binary borides, where the metals of the one or more metal binary borides are selected from Cr, Fe, and Ni.
3. The thermal spray powder of claim 1 , where the particle size of the one or more ternary boride ceramics, the one or more binary molybdenum borides, and the one or more metal binary borides is at least equal to 0.1 μm and no larger than 10 μm.
4. The thermal spray powder of claim 3 , where the average particle sizes of the powder, in a post-agglomeration and post-sintered state, range between 5 and 125 μm (micrometers).
5. The thermal spray powder of claim 3 , where the average particle sizes of the powder, in a post-agglomeration and post-sintered state, range between 10 and 45 μm (micrometers).
6. The thermal spray powder of claim 1 further comprising: up to 10% by weight of one or more nano and submicro-sized reinforced solid lubricants, the one or more nano and submicro-sized reinforced solid lubricants comprising BN, WS 2 or MoS 2 .
7. The thermal spray powder of claim 6 , wherein the average particle size of the one or more ternary boride ceramics, the one or more binary molybdenum borides, the one or more metal binary borides, and the one or more nano and submicrosized reinforced solid lubricants is at least equal to 0.1 μm and no larger than 10 μm.
8. The thermal spray powder of claim 7 , wherein the average particle sizes of the powder, in a post-agglomeration and post-sintered state, range between 5 and 125 μm (micrometers).
9. The thermal spray powder of claim 7 , wherein the average particle sizes of the powder, in a post-agglomeration and post-sintered state, range between 10 and 45 μm (micrometers).
10. The thermal spray powder of claim 2 , where the particle size of the one or more ternary boride ceramics, the one or more binary molybdenum borides, and the one or more metal binary borides is at least equal to 0.1 μm and no larger than 10 μm.
11. The thermal spray powder of claim 10 , where the average particle sizes of the powder, in a post-agglomeration and post-sintered state, range between 5 and 125 μm (micrometers).
12. The thermal spray powder of claim 10 , where the average particle sizes of the powder, in a post-agglomeration and post-sintered state, range between 10 and 45 μm (micrometers).
13. The thermal spray powder of claim 2 further comprising: up to 10% by weight of one or more nano and submicro-sized reinforced solid lubricants, the one or more nano and submicro-sized reinforced solid lubricants comprising BN, WS 2 or MoS 2 .
14. The thermal spray powder of claim 13 , wherein the average particle size of the one or more ternary boride ceramics, the one or more binary molybdenum borides, the one or more metal binary borides, and the one or more nano and submicrosized reinforced solid lubricants is at least equal to 0.1 μm and no larger than 10 μm.
15. The thermal spray powder of claim 14 , wherein the average particle sizes of the powder, in a post-agglomeration and post-sintered state, range between 5 and 125 μm (micrometers).
16. The thermal spray powder of claim 14 , wherein the average particle sizes of the powder, in a post-agglomeration and post-sintered state, range between 10 and 45 μm (micrometers).