Process of preparing a siloxane copolymer
A process for preparing a cyclic siloxane copolymer, a water repellent composition and the use for treating porous substrates like concrete, especially reinforced concrete.
1. Process for improving the water repellency of a substrate by treating it with an emulsion having a Volatile Organic Content according to ASTM 5095 below 50 g/I which includes water, at least one surfactant, and a siloxane copolymer obtained by the process of
Reacting
(i) 1-octene
(ii) a cyclic siloxane having the formula:
wherein R is methyl; and c is between 4 and 6, and where the molar ratio alkene:cyclic siloxane is ≧1.5,
in the presence of a platinum catalyst so as to form a cyclic copolymer having the formula:
where R′ is octyl, a is less than 3 and b is equal to or greater than 2, a+b=c;
Removing the unreacted alkene and volatile cyclic siloxanes from the reaction mixture;
wherein the substrate comprises at least one of regular concrete, high strength concrete, stamped concrete, high performance concrete, self consolidating concrete, shotcrete, cellular concrete, lightweight aerated concrete, variable density concrete, foamed concrete, lightweight or ultra-lightweight concrete, rapid strength concrete, pre-stressed concrete or reinforced concrete for use in pavements, highways/roadways, bridges/overpasses, parking structures, stadiums, precast structures, tilt up structures, drainage pipes, tunnels or reservoir structures, concrete masonry units, concrete blocks, split faced blocks, natural stone or bricks for use on building facades or foundations.
2. A process of utilizing an emulsion having a Volatile Organic Content according to ASTM 5095 below 50 g/I which includes water, at least one surfactant, and a siloxane copolymer obtained by the process of
Reacting
(i) 1-octene
(ii) a cyclic siloxane having the formula:
wherein R is methyl; and c is between 4 and 6, and where the molar ration alkene:cyclic siloxane is ≧1.5,
in the presence of a platinum catalyst so as to form a cyclic copolymer having the formula:
where R′ is octyl, a is less than 3 and b is equal to or greater than 2, a+b=c;
Removing the unreacted alkene and volatile cyclic siloxanes from the reaction mixture; to improve water repellency of substrates by applying the emulsion to the finished substrate wherein the substrate comprises at least one of regular concrete, high strength concrete, stamped concrete, high performance concrete, self consolidating concrete, shotcrete, cellular concrete, lightweight aerated concrete, variable density concrete, foamed concrete, lightweight or ultra-lightweight concrete, rapid strength concrete, pre-stressed concrete or reinforced concrete for use in pavements, highways/roadways, bridges/overpasses, parking structures, stadiums, precast structures, tilt up structures, drainage pipes, tunnels or reservoir structures, concrete masonry units, concrete blocks, split faced blocks, natural stone or bricks for use on building facades or foundations.
3. A process for improving the water repellency of a substrate by treating it with a water repellent composition, having a Volatile Organic Content according to ASTM 5095 below 50 g/I, comprising an emulsion which includes water, at least one surfactant, and a siloxane copolymer obtained by the process of
A) reacting
i) a 1-alkene containing from 8 to 12 carbon atoms
ii) a cyclic siloxane having the formula:
wherein R is an alkyl radical having 1 to 3 carbon atoms; c is equal to or higher than 4, and where the molar ration alkene:cyclic siloxanes is ≧1, in the presence of a platinum catalyst so as to form a cyclic copolymer having the formula:
where R′ is an alkyl group having from 8 to 12 carbon atoms and a+b=c;
B) removing the unreacted alkene and volatile cyclic siloxanes from the reaction mixture;
wherein the substrate comprises at least one of regular concrete, high strength concrete, stamped concrete, high performance concrete, self consolidating concrete, shotcrete, cellular concrete, lightweight aerated concrete, variable density concrete, foamed concrete, lightweight or ultra-lightweight concrete, rapid strength concrete, pre-stressed concrete or reinforced concrete for use in pavements, highways/roadways, bridges/overpasses, parking structures, stadiums, precast structures, tilt up structures, drainage pipes, tunnels or reservoir structures, concrete masonry units, concrete blocks, split faced blocks, natural stone or bricks for use on building facades or foundations.
4. The process according to claim 3 in which the alkene is 1-octene, 1-dodecene or 1-isooctene.
5. The process according to claim 3 in which the molar ratio alkene:cyclic siloxane is ≧1.5.
6. The process according to claim 3 in which a mixture of cyclic siloxanes is used with c being comprised between 4 and 6.
7. The process according to claim 3 in which a is less than 3 and b is equal to or greater than 2.
8. A process of utilizing the siloxane copolymer obtained by the process of
A) reacting
i) a 1-alkene containing from 8 to 12 carbon atoms
ii) a cyclic siloxane having the formula:
wherein R is an alkyl radical having 1 to 3 carbon atoms; c is equal to or higher than 4, and where the molar ratio alkene: cyclic siloxanes is ≧1, in the presence of a platinum catalyst so as to form a cyclic copolymer having the formula:
where R′ is an alkyl group having from 8 to 12 carbon atoms and a+b=c;
B) removing the unreacted alkene and volatile cyclic siloxanes from the reaction mixture;
in a water repellent composition comprising an emulsion which includes water, at least one surfactant and the siloxane copolymer and having a Volatile Organic Content according to ASTM 5095 below 50 g/I, to improve water repellency of a finished substrate by applying the composition to the substrate, wherein the substrate comprises at least one of regular concrete, high strength concrete, stamped concrete, high performance concrete, self consolidating concrete, shotcrete, cellular concrete, lightweight aerated concrete, variable density concrete, foamed concrete, lightweight or ultra-lightweight concrete, rapid strength concrete, pre-stressed concrete or reinforced concrete for use in pavements, highways/roadways, bridges/overpasses, parking structures, stadiums, precast structures, tilt up structures, drainage pipes, tunnels or reservoir structures, concrete masonry units, concrete blocks, split faced blocks, natural stone or bricks for use on building facades or foundations.