Method for improving the wear resistance of dyed surgical instruments
The present invention relates to a method for improving the wear resistance of dyed surgical instruments having a vacuum-resistant material as the main body which, over the course of a vacuum coating step, is coated with a thin layer of titanium, and the coated surface is subjected to anodic oxidation. The method is characterized in that, over the course of the vacuum coating step, prior to coating with the layer of titanium, at least parts of the main body are coated with a layer of hard material which improves the wear protection.
1. Method for improving the wear resistance of dyed surgical instruments having a vacuum-resistant material as a main body which is coated with a titanium layer, characterized in that, over the course of a vacuum coating step, prior to coating with the layer of titanium, at least parts of the main body are coated with a layer of hard material which improves the wear protection.
2. Method according to claim 1 , characterized in that production of a titanium oxide layer on the main body comprises a vapor deposition from a vapor phase in a vacuum coating facility, wherein in the course of the deposition either the titanium oxide layer is deposited on the main body by means of sputtered or vaporized titanium with the aid of oxygen as reactive gas or in the course of the vapor deposition the titanium layer is deposited on the main body and subjected to anodic oxidation to convert the titanium layer to the titanium oxide layer.
3. Method according to claim 2 , characterized in that the nitride and/or oxide is formed with titanium and/or chromium.
4. Method according to claim 1 , characterized in that the layer of hard material is formed by means of a nitride and/or oxide of at least one metal and/or of at least one alloy.
5. Method according to claim 1 , characterized in that the layer of hard material can be formed by means of a chromium nitride layer.
6. Method according to claim 1 , characterized in that the layer of hard material is formed by means of a titanium nitride layer.
7. Method according to claim 1 , characterized in that the layer of hard material is deposited with a thickness of at least 1.5 μm and maximum 20 μm.
8. Method according to claim 1 , characterized in that in the case of a deposited titanium layer, the layer is deposited with a thickness of at least 1 μm.
9. Method according to claim 1 , characterized in that to improve the adhesion of the layer of hard material onto the main body, a bonding layer is provided between the main body and the layer of hard material.
10. Method according to claim 1 , characterized in that the layer of hard material is deposited as a gradient layer and thus a gradual transition to a titanium oxide layer or to the titanium layer is achieved.
11. Method according to claim 1 , characterized in that the layer of hard material is deposited with a thickness of at least 2 μm and a maximum of 5 μm.
12. Method according to claim 1 , characterized in that in the case of a deposited titanium layer, the layer is deposited with a thickness of at least 2 μm and a maximum of 10 μm.
13. Method according to claim 1 , characterized in that in the case of a deposited titanium layer, the layer is deposited with a thickness of at least 2 μm and a maximum of 10 μm directly onto the layer of hard material.
14. Method according to claim 1 , characterized in that to improve the adhesion of the layer of hard material onto the main body, a bonding layer of chromium is provided between the main body and the layer of hard material.
15. Method according to claim 1 , characterized in that production of a titanium oxide layer on the main body comprises a vapor deposition from a vapor phase in a vacuum coating facility, wherein in the course of the vapor deposition the titanium oxide layer is formed by depositing titanium oxide on the main body by means of sputtered or vaporized titanium with the aid of oxygen as reactive gas.
16. Surgical instrument with a main body and a titanium oxide coating, characterized in that a layer of hard material is provided between the main body and the titanium oxide coating on the main body.
17. Surgical instrument according to claim 16 , characterized in that the layer of hard material has a thickness between 2 μm and 10 μm.
18. Surgical instrument according to claim 16 , characterized in that the layer of hard material comprises titanium nitride and/or chromium nitride.
19. Surgical instrument according to claim 16 , characterized in that between the main body and the layer of hard material, a bonding layer is provided.
20. Surgical instrument according to claim 16 , characterized in that the layer of hard material is deposited as a gradient layer and thus a gradual transition to the titanium oxide layer is achieved.
21. Surgical instrument according to claim 16 , characterized in that between the main body and the layer of hard material, a bonding layer of chromium is provided.