Carbon fiber-reinforced carbon composite and method of manufacturing the same
A plate-shaped carbon fiber-reinforced carbon composite has a longitudinal length-to-widthwise length ratio of more than 1. The carbon fiber-reinforced carbon composite is such that at least two layers that are a first carbon fiber-reinforced carbon composite layer in which carbon fibers are placed in the carbonaceous matrix and are oriented in the longitudinal direction and a second carbon fiber-reinforced carbon composite layer different in the arrangement of the carbon fibers from the first carbon fiber-reinforced carbon composite layer are stacked, the first carbon fiber-reinforced carbon composite layer forms an outermost layer of at least one plate surface, the thickness thereof is 70% or more of the thickness of the carbon fiber-reinforced carbon composite, and the longitudinal bending elastic modulus is 150 GPa or more. The first carbon fiber-reinforced carbon composite layer in which the carbon fibers are aligned in the longitudinal direction is placed only on an outermost layer of one or both of plate surfaces and another site is a carbon fiber-reinforced carbon composite layer different in the arrangement of the carbon fibers from the first carbon fiber-reinforced carbon composite layer; hence, the longitudinal bending elastic modulus is significantly increased and warping, peeling, or cracking during usage and interlayer delamination due to gases produced during manufacture are suppressed.
1. A transfer member comprising a plate-shaped carbon fiber-reinforced carbon composite, wherein the carbon fiber-reinforced carbon composite comprises carbon fibers and a carbonaceous matrix, and has a longitudinal length-to-widthwise length ratio of from 5 to 80,
wherein:
the carbon fiber-reinforced carbon composite comprises at least two stacked carbon fiber-reinforced carbon composite layers comprising (a) at least one carbon fiber-reinforced carbon composite layer in which the carbon fibers are oriented in a longitudinal direction in the carbonaceous matrix, and (b) a carbon fiber-reinforced carbon composite layer which is different in arrangement of the carbon fibers from the at least one carbon fiber-reinforced carbon composite layer (a),
the at least one carbon fiber-reinforced carbon composite layer (a) forms an outermost layer of at least one plate surface of the carbon fiber-reinforced carbon composite,
a total thickness of the layer (a) is 70% or more of a thickness of the carbon fiber-reinforced carbon composite,
the carbon fiber-reinforced carbon composite has a longitudinal bending elastic modulus of 150 GPa or more, and
the at least one carbon fiber-reinforced carbon composite layer (a) has weight of carbon fibers per unit area (FAW) from 5,000 g/m 2 to 15,000 g/m 2 , the carbon fiber-reinforced carbon composite layer (b) has FAW from 400 g/m 2 to 4,000 g/m 2 , and the carbon fiber-reinforced carbon composite has FAW from 5,400 g/m 2 to 19,000 g/m 2 .
2. The transfer member of claim 1 , wherein the carbon fibers in the carbon fiber-reinforced carbon composite layer (b) are oriented in a direction crossing the longitudinal direction.
3. The transfer member of claim 2 , wherein the carbon fibers are pitch-based carbon fibers.
4. The transfer member of claim 1 , wherein the carbon fibers are pitch-based carbon fibers.
5. The transfer member of claim 4 , wherein the carbon fiber-reinforced carbon composite has a volumetric content of the carbon fibers from 40% to 70%.
6. The transfer member of claim 1 , wherein the carbon fiber-reinforced carbon composite has a volumetric content of the carbon fibers from 40% to 70%.
7. The transfer member of claim 1 , wherein the carbon fiber-reinforced carbon composite has a bulk density of 1.65 g/cm 3 or more.
8. The transfer member of claim 1 , wherein the carbon fiber-reinforced carbon composite is manufactured by a method comprising:
stacking a plurality of unidirectional layers in which the carbon fibers are aligned in a fiber axis direction such that alignment directions of the carbon fibers of each layer cross each other to form a laminate,
hot-pressing the laminate to form a carbon fiber-reinforced resin form, and
calcining and carbonizing the carbon fiber-reinforced resin form.
9. The transfer member of claim 8 , wherein the layers have a thermosetting resin content of 15% to 45% by weight.
10. The transfer member of claim 8 , wherein the method for manufacturing the carbon fiber-reinforced carbon composite further comprises a process in which a preform obtained by calcining and carbonizing the carbon fiber-reinforced resin form is subjected to densification treatment comprising operations (1) and (2) conducted at least once:
(1) impregnating the preform with an impregnating material which is at least one selected from the group consisting of coal-tar pitch, petroleum-tar pitch, and resin, and
(2) calcining the preform to carbonize the impregnating material impregnated to the preform.
11. The transfer member of claim 1 , wherein the total thickness of the layer (a) is from 70% to 90% of a thickness of the carbon fiber-reinforced carbon composite.
12. The transfer member of claim 1 , wherein the total thickness of the layer (a) is from 70% to 85% of a thickness of the carbon fiber-reinforced carbon composite.
13. The transfer member of claim 1 , wherein the carbon fiber-reinforced carbon composite has a longitudinal bending elastic modulus of from 150 GPa to 350 GPa.
14. The transfer member of claim 1 , wherein the carbon fiber-reinforced carbon composite has a bulk density of from 1.65g/cm 3 to 1.80 g/cm 3 .
15. The transfer member of claim 1 , wherein the carbon fiber-reinforced carbon composite has a volumetric content of the carbon fibers from 45% to 65%.