Rubbery polymer with low compression set

1. A polymeric composition which is a blend comprising PVC and a rubbery polymer comprising:

(a) from 40 to 80 weight percent butyl acrylate or from 40 to 80 weight percent of a mixture of butyl acrylate and 2-ethylhexyl acrylate containing up to about 40 weight percent 2-ethylhexyl acrylate,

(b) from 1 to 35 weight percent of a member selected from the group consisting of methyl methacrylate, ethyl methacrylate, methyl acrylate, and ethyl acrylate,

(c) from 4 to 30 weight percent acrylonitrile,

(d) from 3 to 25 weight percent styrene, and

(e) from 0.5 to 8 weight percent half ester maleate soap, and

(f) from 0.25 to 4 weight percent of a crosslinking agent selected from the group consisting of allyl methacrylate, glycidyl methacrylate, trimethylolpropanetrimethyl acrylate, and divinylbenzene, wherein the rubbery polymer contains 0.25 to 3 weight percent of allyl methacrylate,

wherein said rubbery polymer is obtainable by process comprising the steps of:

(I) polymerizing monomers (a), (b), (c), (e) and (f) as defined above under emulsion polymerization conditions to produce an elastomeric seed polymer containing latex, allyl methacrylate being necessarily present,

(II) adding additional monomer (c), the monomer (d), and additional monomer (f) as defined above to the elastomeric seed polymer containing latex under emulsion polymerization conditions,

(III) recovering the rubbery polymer from the emulsion containing the rubbery polymer,

wherein an amount of allyl methacrylate added in step (I) is about 0.5 weight percent, based on a total amount of polymerizing monomers (a), (b), (c), (e) and (f) added in step (I).

2. The polymeric composition according to claim 1 , wherein the rubber polymer comprises:

(a) from 50 to 80 weight percent butyl acrylate, or from 50 to 80 weight percent of a mixture of butyl acrylate and 2-ethylhexyl acrylate containing up to about 40 weight percent of 2-ethylhexyl acrylate,

(b) from 1 to 25 weight percent of a member selected from the group consisting of methyl methacrylate, ethyl methacrylate, methyl acrylate and ethyl acrylate,

(c) from 6 to 30 weight percent acrylonitrile,

(d) from 5 to 18 weight percent styrene, and

(e) from 1 to 5 weight percent half ester maleate soap, and

(f) from 0.25 to 4 weight percent of a crosslinking agent selected from the group consisting of allyl methacrylate, glycidyl methacrylate trimethylolpropanetrimethyl acrylate, and divinylbenzene, wherein the rubbery polymer contains 0.25 to 3 weight percent of allyl methacrylate.

3. The polymeric composition according to claim 1 , wherein the rubber polymer comprises:

(a) from 55 weight percent to 75 weight percent butyl acrylate, or a mixture of butyl acrylate and 2-ethylhexyl acrylate containing up to about 40 weight percent of 2-ethylhexyl acrylate,

(b) from 1 weight percent to 20 weight percent of at least one member selected from the group consisting of methyl methacrylate, ethyl methacrylate, methyl acrylate, and ethyl acrylate,

(c) from 10 weight percent to 25 weight percent acrylonitrile,

(d) from 8 weight percent to 14 weight percent styrene,

(e) from 2 weight percent to 4 weight percent of a half ester maleate soap, and

(f) from 0.25 weight percent to 3 weight percent of a crosslinking agent selected from the group consisting of allyl methacrylate, glycidyl methacrylate, trimethylolpropanetrimethyl acrylate, and and divinylbenzene, wherein the rubbery polymer contains 0.25 to 3 weight percent of allyl methacrylate.

4. The polymeric composition according to claim 1 , wherein the crosslinking agent is allyl methacrylate.

5. The polymeric composition according to claim 1 , further comprising an ingredient selected from plasticizers, antioxidants, fillers, colorants, pigments and mixtures thereof.

6. A gasket with a compression set measured at 70° C./22hours inferior to 50% comprised of a polymeric composition according to claim 1 .

7. A polymeric composition, having a compression set at 70° C./22 hours ranging from 45 to 48, which is a blend comprising PVC and a rubbery polymer comprising:

(a) from 40 to 80 weight percent butyl acrylate or from 40 to 80 weight percent of a mixture of butyl acrylate and 2-ethylhexyl acrylate containing up to about 40 weight percent 2-ethylhexyl acrylate,

(b) from 1 to 35 weight percent of a member selected from the group consisting of methyl methacrylate, ethyl methacrylate, methyl acrylate, and ethyl acrylate,

(c) from 4 to 30 weight percent acrylonitrile,

(d) from 3 to 25 weight percent styrene, and

(e) from 0.5 to 8 weight percent half ester maleate soap, and

(f) from 0.25 to 4 weight percent of a crosslinking agent selected from the group consisting of allyl methacrylate, glycidyl methacrylate, trimethylolpropanetrimethyl acrylate, and divinylbenzene, wherein the rubbery polymer contains 0.25 to 3 weight percent of allyl methacrylate,

wherein said rubbery polymer is obtainable by process comprising the steps of:

(I) polymerizing monomers (a), (b), (c), (e) and (f) as defined above under emulsion polymerization conditions to produce an elastomeric seed polymer containing latex, allyl methacrylate being necessarily present,

(II) adding additional monomer (c), the monomer (d), and additional monomer (f) as defined above to the elastomeric seed polymer containing latex under emulsion polymerization conditions,

(III) recovering the rubbery polymer from the emulsion containing the rubbery polymer.

8. The polymeric composition according to claim 7 , wherein the rubber polymer comprises:

(a) from 50 to 80 weight percent butyl acrylate, or from 50 to 80 weight percent of a mixture of butyl acrylate and 2-ethylhexyl acrylate containing up to about 40 weight percent of 2-ethylhexyl acrylate,

(b) from 1 to 25 weight percent of a member selected from the group consisting of methyl methacrylate, ethyl methacrylate, methyl acrylate and ethyl acrylate,

(c) from 6 to 30 weight percent acrylonitrile,

(d) from 5 to 18 weight percent styrene, and

(e) from 1 to 5 weight percent half ester maleate soap, and

(f) from 0.25 to 4 weight percent of a crosslinking agent selected from the group consisting of allyl methacrylate, glycidyl methacrylate, trimethylolpropanetrimethyl acrylate, and divinylbenzene, wherein the rubbery polymer contains 0.25 to 3 weight percent of allyl methacrylate.

9. The polymeric composition according to claim 7 , wherein the rubber polymer comprises:

(a) from 55 weight percent to 75 weight percent butyl acrylate, or a mixture of butyl acrylate and 2-ethylhexyl acrylate containing up to about 40 weight percent of 2-ethylhexyl acrylate,

(b) from 1 weight percent to 20 weight percent of at least one member selected from the group consisting of methyl methacrylate, ethyl methacrylate, methyl acrylate, and ethyl acrylate,

(c) from 10 weight percent to 25 weight percent acrylonitrile,

(d) from 8 weight percent to 14 weight percent styrene,

(e) from 2 weight percent to 4 weight percent of a half ester maleate soap, and

(f) from 0.25 weight percent to 3 weight percent of a crosslinking agent selected from the group consisting of allyl methacrylate, glycidyl methacrylate, trimethylolpropanetrimethyl acrylate, and d divinylbenzene, wherein the rubbery polymer contains 0.25 to 3 weight percent of allyl methacrylate.

10. The polymeric composition according to claim 7 , wherein the crosslinking agent is allyl methacrylate.

11. The polymeric composition according to claim 7 , further comprising an ingredient selected from plasticizers, antioxidants, fillers, colorants, pigments and mixtures thereof.

12. A gasket with a compression set measured at 70° C./22hours inferior to 50% comprised of a polymeric composition according to claim 7 .

13. A polymeric composition which is a blend comprising PVC and a rubbery polymer comprising:

(a) from 40 to 80 weight percent butyl acrylate or from 40 to 80 weight percent of a mixture of butyl acrylate and 2-ethylhexyl acrylate containing up to about 40 weight percent 2-ethylhexyl acrylate,

(b) from 1 to 35 weight percent of a member selected from the group consisting of methyl methacrylate, ethyl methacrylate, methyl acrylate, and ethyl acrylate,

(c) from 4 to 30 weight percent acrylonitrile,

(d) from 3 to 25 weight percent styrene, and

(e) from 0.5 to 8 weight percent half ester maleate soap, and

(f) from 0.66 to 3.55 weight percent of a crosslinking agent selected from the group consisting of allyl methacrylate, glycidyl methacrylate, trimethylolpropanetrimethyl acrylate, and divinylbenzene, wherein the rubbery polymer contains 0.25 to 3 weight percent of allyl methacrylate,

wherein said rubbery polymer is obtainable by a process comprising the steps of:

(I) polymerizing monomers (a), (b), (c), (e) and (f) as defined above under emulsion polymerization conditions to produce an elastomeric seed polymer containing latex, allyl methacrylate being necessarily present,

(II) adding additional monomer (c), the monomer (d) and additional monomer (f) as defined above to the elastomeric seed polymer containing latex under emulsion polymerization conditions,

(III) recovering the rubbery polymer from the emulsion containing the rubbery polymer.

14. The polymeric composition according to claim 13 , wherein the rubber polymer comprises:

(a) from 50 to 80 weight percent butyl acrylate, or from 50 to 80 weight percent of a mixture of butyl acrylate and 2-ethylhexyl acrylate containing up to about 40 weight percent of 2-ethylhexyl acrylate,

(b) from 1 to 25 weight percent of a member selected from the group consisting of methyl methacrylate, ethyl methacrylate, methyl acrylate and ethyl acrylate,

(c) from 6 to 30 weight percent acrylonitrile,

(d) from 5 to 18 weight percent styrene, and

(e) from 1 to 5 weight percent half ester maleate soap, and

(f) from 0.66 to 3.55 weight percent of a crosslinking agent selected from the group consisting of allyl methacrylate, glycidyl methacrylate, trimethylolpropanetrimethyl acrylate, and divinylbenzene, wherein the rubbery polymer contains 0.25 to 3 weight percent of allyl methacrylate.

15. The polymeric composition according to claim 13 , wherein the rubber polymer comprises:

(a) from 55 weight percent to 75 weight percent butyl acrylate, or a mixture of butyl acrylate and 2-ethylhexyl acrylate containing up to about 40 weight percent of 2-ethylhexyl acrylate,

(b) from 1 weight percent to 20 weight percent of at least one member selected from the group consisting of methyl methacrylate, ethyl methacrylate, methyl acrylate, and ethyl acrylate,

(c) from 10 weight percent to 25 weight percent acrylonitrile,

(d) from 8 weight percent to 14 weight percent styrene,

(e) from 2 weight percent to 4 weight percent of a half ester maleate soap, and

(f) from 0.66 weight percent to 3 weight percent of a crosslinking agent selected from the group consisting of allyl methacrylate, glycidyl methacrylate, trimethylolpropanetrimethyl acrylate, and d divinylbenzene, wherein the rubbery polymer contains 0.25 to 3 weight percent of allyl methacrylate.

16. The polymeric composition according to claim 13 , wherein the crosslinking agent is allyl methacrylate.

17. The polymeric composition according to claim 13 , further comprising an ingredient selected from plasticizers, antioxidants, fillers, colorants, pigments and mixtures thereof.

18. A gasket with a compression set measured at 70° C./22hours inferior to 50% comprised of a polymeric composition according to claim 13 .