A lithium (Li) ion battery comprising a cathode, a separator, an organic electrolyte, an anode, and a carbon black conductive additive, wherein the carbon black has been heated treated in a CO 2 gas environment at a temperature range of between 875-925 degrees Celsius for a time range of between 50 to 70 minutes to oxidize the carbon black and reduce an electrochemical reactivity of the carbon black towards the organic electrolyte.
1. A method of treating carbon black to reduce an electrochemical reactivity of the carbon black towards an organic electrolyte, comprising:
a. heat the carbon black in a CO 2 gas environment at a temperature range of between 600-1200 degrees Celsius for a time range of between 1 to 120 minutes to oxidize the carbon black surface and reduce the electrochemical reactivity; and
b. measure the carbon black electrochemical reactivity using a cyclic voltammetry technique to determine an electrochemical current in response to an electrochemical polarization in the voltage range of between 2.5 to 5.0 volts versus a Li/Li + reference potential, wherein a treated carbon black produces an electrochemical current in a range of between −0.025 and +0.075 mA/cm 2 in the voltage range of between 2.5 to 4.75 volts.
2. The method of claim 1 , wherein a treated carbon black produces an electrochemical current in a range of between −0.025 and +0.025 mA/cm 2 in the voltage range of between 2.5 to 4.25 volts.
3. The method of claim 1 , wherein the carbon black has been heated treated in the CO 2 gas environment at the temperature of 900 degrees Celsius for the time of 60 minutes.