Method for the production of a refractory filter
A method for the production of closed edge filters suitable for filtering molten metal and filters made by such a method. The method comprises: providing a reticulated foam substrate having at least one first surface for forming a side face of the filter and two opposed second surfaces for forming the through-flow faces of the filter; applying a liquid comprising an organic coating component to the first surface; solidifying the organic coating component to form a filter precursor having a volatilizable coating on the first surface; impregnating the filter precursor with a slurry comprising particles of a refractory material, a binder and a liquid carrier; and drying and firing the impregnated filter precursor to form the filter having a closed edge.
1. A refractory foam filter comprising a three-dimensional network of strands of refractory material and having at least one side face and two opposed through-flow faces, the at least one side face having a unitary closed edge, wherein the closed edge comprises cavities enclosed within the edge and the filter is capable of withstanding temperatures above 500° C., and wherein substantially all of the cavities enclosed within the edge are located along a line which is substantially parallel to the edge of the filter.
2. The filter according to claim 1 , wherein the unitary closed edge has a thickness of less than 1 mm.
3. The filter according to claim 1 , in which the cavities are significantly longer in a direction parallel to the side face than they are wide in a direction perpendicular to the side face.
4. The filter of claim 1 , in which the unitary closed edge has a thickness of less than 0.5 mm.
5. The filter of claim 1 , wherein the ratio of the thickness of the unitary closed edge to the thickness of the strands is from 0.5 to 2.