Methods of joining metallic protective layers
View Patent ↗In various embodiments, protective layers are bonded to a steel layer, overlapped, and at least partially covered by a layer of unmelted metal powder produced by cold spray.
1. A method of joining protective cladding layers over an underlying steel layer without the use of batten strips, the method comprising:
bonding a first protective layer to an underlying steel layer at an interface between the first protective layer and the steel layer;
bonding a second protective layer to the steel layer at an interface between the second protective layer and the steel layer, the steel layer underlying the second protective layer;
disposing a portion of the first protective layer over a portion of the second protective layer, thereby forming a region of overlap; and
thereafter, and without otherwise bonding the first protective layer to the second protective layer in the region of overlap, cold spraying a metal powder over and in contact with the first and second protective layers in the region of overlap to form a layer of unmelted metal powder that directly connects the first and second protective layers.
2. The method of claim 1 , wherein the first and second protective layers each comprise at least one of tantalum, niobium, titanium, zirconium, molybdenum, or tungsten.
3. The method of claim 1 , wherein the first and second protective layers are not welded together before cold spraying the metal powder.
4. The method of claim 1 , wherein the first and second protective layers are substantially resistant to at least one of acid or corrosion.
5. The method of claim 1 , wherein the steel layer underlies substantially all of the first and second protective layers.
6. The method of claim 1 , wherein after cold spraying the layer of unmelted metal powder is substantially free of oxygen.
7. The method of claim 1 , wherein each of the first and second protective layers is bonded directly to the steel layer.
8. The method of claim 7 , wherein bonding both of the first and second protective layers to the steel layer comprises at least one of diffusion bonding or explosive bonding.
9. The method of claim 1 , wherein at least one of the first or second protective layers is bonded to the steel layer via a structural adhesive, a low-temperature brazing material, or a low-temperature solder.
10. The method of claim 9 , wherein the at least one of the first or second protective layers is bonded to the steel layer via a structural adhesive having a decomposition temperature less than approximately 300° C.
11. The method of claim 9 , wherein the at least one of the first or second protective layers is bonded to the steel layer via a low-temperature solder having a melting point less than approximately 400° C.
12. The method of claim 1 , wherein bonding the second protective layer to the underlying steel layer comprises cold spraying the second protective layer over the steel layer.
13. The method of claim 1 , wherein a thickness of at least one of the first or second protective layers ranges between approximately 0.005 inches and approximately 0.02 inches.
14. The method of claim 1 , wherein a thickness of at least one of the first or second protective layers ranges between approximately 0.005 inches and approximately 0.01 inches.
15. The method of claim 1 , wherein the layer of unmelted metal powder comprises elongated particles having a random crystallographic orientation.
16. The method of claim 1 , wherein the layer of unmelted metal powder has a density greater than approximately 95%.
17. The method of claim 16 , wherein the layer of unmelted metal powder has a density greater than approximately 97.5%.
18. The method of claim 1 , further comprising annealing the layer of unmelted metal powder for at least one of relieving mechanical stress or improving interparticle bond strength.
19. The method of claim 18 , wherein the annealing recrystallizes at least a portion of the layer of unmelted metal powder.
20. The method of claim 18 , wherein the annealing is performed at a temperature greater than approximately 1150° C.
21. The method of claim 1 , wherein the steel layer comprises stainless steel.
22. The method of claim 1 , wherein after cold spraying the layer of unmelted metal powder and the first and second protective layers are substantially free of impurities diffused therein from the steel layer.
23. The method of claim 1 , further comprising, prior to forming the region of overlap, joining two steel members to form the underlying steel layer, thereby forming a joint, wherein the region of overlap is disposed proximate the joint.
24. The method of claim 23 , wherein joining the two steel members comprises welding.