Semiconductor device and method for manufacturing the same
View Patent ↗A semiconductor device in which fluctuation in electric characteristics due to miniaturization is less likely to be caused is provided. The semiconductor device includes an oxide semiconductor film including a first region, a pair of second regions in contact with side surfaces of the first region, and a pair of third regions in contact with side surfaces of the pair of second regions; a gate insulating film provided over the oxide semiconductor film; and a first electrode that is over the gate insulating film and overlaps with the first region. The first region is a CAAC oxide semiconductor region. The pair of second regions and the pair of third regions are each an amorphous oxide semiconductor region containing a dopant. The dopant concentration of the pair of third regions is higher than the dopant concentration of the pair of second regions.
1. A method for manufacturing a semiconductor device comprising the steps of:
forming an oxide semiconductor film over a substrate during heat treatment to the substrate;
forming a gate insulating film over the oxide semiconductor film;
forming a first electrode over the gate insulating film;
forming a first sidewall insulating film and a second sidewall insulating film on side surfaces of the first electrode; and
adding a dopant to the oxide semiconductor film to form a first region, a pair of second regions and a pair of third regions of the oxide semiconductor film,
wherein the first electrode overlaps with the first region,
wherein the first sidewall insulating film overlaps with one of the pair of second regions, and the second sidewall insulating film overlaps with the other of the pair of second regions,
wherein the first region and the pair of second regions are located between the pair of third regions,
wherein the first region is a c-axis aligned crystalline oxide semiconductor region,
wherein each of a crystallinity of the pair of second regions and a crystallinity of the pair of third regions is lower than a crystallinity of the first region, and
wherein a dopant concentration of the pair of third regions is higher than a dopant concentration of the pair of second regions.
2. The method for manufacturing a semiconductor device according to claim 1 ,
wherein the gate insulating film is an oxide insulating film, and
wherein each of the first sidewall insulating film and the second sidewall insulating film is a nitride insulating film.
3. The method for manufacturing a semiconductor device according to claim 1 ,
wherein each of the gate insulating film, the first sidewall insulating film and the second sidewall insulating film is an oxide insulating film.
4. The method for manufacturing a semiconductor device according to claim 1 ,
wherein the pair of second regions and the pair of third regions comprise one or more elements selected from nitrogen, phosphorus, and arsenic as the dopant, and
wherein the dopant concentration of the pair of second regions and the dopant concentration of the pair of third regions are higher than or equal to 5×10 18 atoms/cm 3 and lower than or equal to 1×10 22 atoms/cm 3 .
5. The method for manufacturing a semiconductor device according to claim 1 ,
wherein the pair of second regions and the pair of third regions comprise one or more elements selected from nitrogen, phosphorus, and arsenic as the dopant,
wherein the dopant concentration of the pair of second regions is higher than or equal to 5×10 18 atoms/cm 3 and lower than 5×10 19 atoms/cm 3 , and
wherein the dopant concentration of the pair of third regions is higher than or equal to 5×10 19 atoms/cm 3 and lower than or equal to 1×10 22 atoms/cm 3 .
6. The method for manufacturing a semiconductor device according to claim 1 ,
wherein the oxide semiconductor film comprises two or more elements selected from In, Ga, Sn, and Zn.
7. A method for manufacturing a semiconductor device comprising the steps of:
forming a first oxide semiconductor film over a substrate;
performing first heat treatment to form a first crystalline oxide semiconductor film after forming the first oxide semiconductor film;
forming a second oxide semiconductor film over the first crystalline oxide semiconductor film;
performing second heat treatment to form a second crystalline oxide semiconductor film after forming the second oxide semiconductor film;
forming a gate insulating film over an oxide semiconductor film that comprises the first crystalline oxide semiconductor film and the second crystalline oxide semiconductor film;
forming a first electrode over the gate insulating film;
forming a first sidewall insulating film and a second sidewall insulating film on side surfaces of the first electrode; and
adding a dopant to the oxide semiconductor film to form a first region, a pair of second regions and a pair of third regions of the oxide semiconductor film,
wherein the first electrode overlaps with the first region,
wherein the first sidewall insulating film overlaps with one of the pair of second regions, and the second sidewall insulating film overlaps with the other of the pair of second regions,
wherein the first region and the pair of second regions are located between the pair of third regions,
wherein the first region is a c-axis aligned crystalline oxide semiconductor region,
wherein each of a crystallinity of the pair of second regions and a crystallinity of the pair of third regions is lower than a crystallinity of the first region, and
wherein a dopant concentration of the pair of third regions is higher than a dopant concentration of the pair of second regions.
8. The method for manufacturing a semiconductor device according to claim 7 ,
wherein the gate insulating film is an oxide insulating film, and
wherein each of the first sidewall insulating film and the second sidewall insulating film is a nitride insulating film.
9. The method for manufacturing a semiconductor device according to claim 7 ,
wherein each of the gate insulating film, the first sidewall insulating film and the second sidewall insulating film is an oxide insulating film.
10. The method for manufacturing a semiconductor device according to claim 7 ,
wherein the pair of second regions and the pair of third regions comprise one or more elements selected from nitrogen, phosphorus, and arsenic as the dopant, and
wherein the dopant concentration of the pair of second regions and the dopant concentration of the pair of third regions are higher than or equal to 5×10 18 atoms/cm 3 and lower than or equal to 1×10 22 atoms/cm 3 .
11. The method for manufacturing a semiconductor device according to claim 7 ,
wherein the pair of second regions and the pair of third regions comprise one or more elements selected from nitrogen, phosphorus, and arsenic as the dopant,
wherein the dopant concentration of the pair of second regions is higher than or equal to 5×10 18 atoms/cm 3 and lower than 5×10 19 atoms/cm 3 , and
wherein the dopant concentration of the pair of third regions is higher than or equal to 5×10 19 atoms/cm 3 and lower than or equal to 1×10 22 atoms/cm 3 .
12. The method for manufacturing a semiconductor device according to claim 7 ,
wherein the oxide semiconductor film comprises two or more elements selected from In, Ga, Sn, and Zn.
13. A method for manufacturing a semiconductor device comprising the steps of:
forming an insulating film on a substrate in an atmosphere gas containing oxygen;
forming a first oxide semiconductor film on the insulating film;
performing first heat treatment to form a first crystalline oxide semiconductor film after forming the first oxide semiconductor film;
forming a second oxide semiconductor film over the first crystalline oxide semiconductor film;
performing second heat treatment to form a second crystalline oxide semiconductor film after forming the second oxide semiconductor film;
forming a gate insulating film over an oxide semiconductor film that comprises the first crystalline oxide semiconductor film and the second crystalline oxide semiconductor film;
forming a first electrode over the gate insulating film;
forming a first sidewall insulating film and a second sidewall insulating film on side surfaces of the first electrode; and
adding a dopant to the oxide semiconductor film to form a first region, a pair of second regions and a pair of third regions of the oxide semiconductor film,
wherein the first electrode overlaps with the first region,
wherein the first sidewall insulating film overlaps with one of the pair of second regions, and the second sidewall insulating film overlaps with the other of the pair of second regions,
wherein the first region and the pair of second regions are located between the pair of third regions,
wherein the first region is a c-axis aligned crystalline oxide semiconductor region,
wherein each of a crystallinity of the pair of second regions and a crystallinity of the pair of third regions is lower than a crystallinity of the first region, and
wherein a dopant concentration of the pair of third regions is higher than a dopant concentration of the pair of second regions.
14. The method for manufacturing a semiconductor device according to claim 13 ,
wherein the insulating film is formed by a sputtering method.
15. The method for manufacturing a semiconductor device according to claim 14 ,
wherein the insulating film is formed using a silicon target, a quartz target, an aluminum target, and an aluminum oxide target.
16. The method for manufacturing a semiconductor device according to claim 13 ,
wherein the proportion of oxygen in the atmosphere gas is 6 vol. % or higher.
17. The method for manufacturing a semiconductor device according to claim 1 , wherein each of the first sidewall insulating film and the second sidewall insulating film is on side surfaces of the gate insulating film.