Hydrophilic member and hydrophilic product using the same

1. A method for manufacturing a hydrophilic member, comprising:

mixing at least one kind of particles selected from the group consisting of tungsten oxide particles each having a crystal structure and tungsten oxide composite particles each having a crystal structure, with an aqueous dispersion medium including at least one selected from the group consisting of water and alcohol, to obtain a dispersion liquid containing the particles and the aqueous dispersion medium, the crystal structure of the particles including a mixture of monoclinic crystal and triclinic crystal of tungsten trioxide;

applying the dispersion liquid on a surface of a substrate; and

drying the dispersion liquid applied on the surface of the substrate, without firing after drying, to form a dried film containing the particles and having a surface of which an arithmetic mean roughness Ra with a reference length of 100 μm is from 1 nm to 1000 nm,

wherein the particles in the dried film exist on the surface of the substrate in a state that a crystal direction is not oriented, and

wherein the dried film exhibits hydrophilicity independently of light based on the particles in the dried film, and a contact angle with water of the dried film stored for a month in a dark place and tested without light irradiation is 10° or less.

2. The method according to claim 1 ,

wherein a mean particle diameter of the particles is in a range of from 1 nm to 200 nm.

3. The method according to claim 1 ,

wherein a BET specific surface area of the particles is in a range of 4.1 m 2 /g to 820 m 2 /g.

4. The method according to claim 1 ,

wherein the dried film is formed by drying the dispersion liquid at a temperature of 200° C. or less.

5. The method according to claim 1 ,

wherein the tungsten oxide composite includes a transition metal element in a range of from 0.001 mass % to 50 mass %.

6. The method according to claim 1 ,

wherein the tungsten oxide composite includes at least one metal element selected from the group consisting of titanium, zirconium, manganese, iron, palladium, platinum, copper, silver, zirconium, aluminum, and cerium in a range of from 0.001 mass % to 50 mass %.

7. The method according to claim 1 ,

wherein the crystal structure further includes rhombic crystal of tungsten trioxide.

8. The method according to claim 1 , further comprising:

fabricating the particles by sublimating a metal tungsten powder, a tungsten compound powder, or a tungsten compound solution in an oxygen atmosphere.

9. The method according to claim 8 ,

wherein the metal tungsten powder, the tungsten compound powder, or the tungsten compound solution is sublimated by an inductively coupled plasma process in the oxygen atmosphere.

10. The method according to claim 8 , further comprising:

heat-treating the particles obtained by sublimating at a temperature of 200° C. to 1000° C. for 10 minutes to 5 hours.

11. A method for manufacturing a hydrophilic member, comprising:

mixing at least one kind of particles selected from the group consisting of tungsten oxide particles each having a crystal structure and tungsten oxide composite particles each having a crystal structure, with an aqueous dispersion medium including at least one selected from the group consisting of water and alcohol, to obtain a dispersion liquid containing the particles and the aqueous dispersion medium, the crystal structure of the particles including a mixture of monoclinic crystal and triclinic crystal of tungsten trioxide;

mixing the dispersion liquid with an inorganic binder or an organic binder to obtain a coating material containing the particles, the aqueous dispersion medium, and the binder;

applying the coating material on a surface of a substrate; and

drying the coating material applied on the surface of the substrate, without firing after drying, to form a dried film containing the particles and having a surface of which an arithmetic mean roughness Ra with a reference length of 100 μm is from 1 nm to 1000 nm,

wherein the particles in the dried film exist on the surface of the substrate in a state that a crystal direction is not oriented, and

wherein the dried film exhibits hydrophilicity independently of light based on the particles in the dried film, and a contact angle with water of the dried film stored for a month in a dark place and tested without light irradiation is 10° or less.

12. The method according to claim 11 ,

wherein the coating material contains the inorganic binder, and

wherein the inorganic binder includes at least one selected from the group consisting of silica, colloidal silica, alumina, zirconia, zinc oxide, silicon compound, phosphate, water glass, glass frit, gypsum, and lime.

13. The method according to claim 11 ,

wherein a mean particle diameter of the particles is in a range of from 1 nm to 200 nm.

14. The method according to claim 11 ,

wherein a BET specific surface area of the particles is in a range of 4.1 m 2 /g to 820 m 2 /g.

15. The method according to claim 11 ,

wherein the dried film is formed by drying the coating material at a temperature of 200° C. or less.

16. The method according to claim 11 ,

wherein the tungsten oxide composite includes a transition metal element in a range of from 0.001 mass % to 50 mass %.

17. The method according to claim 11 ,

wherein the crystal structure further includes rhombic crystal of tungsten trioxide.

18. The method according to claim 11 , further comprising:

fabricating the particles by sublimating a metal tungsten powder, a tungsten compound powder, or a tungsten compound solution in an oxygen atmosphere.

19. The method according to claim 18 ,

wherein the metal tungsten powder, the tungsten compound powder, or the tungsten compound solution is sublimated by an inductively coupled plasma process in the oxygen atmosphere.

20. The method according to claim 18 , further comprising:

heat-treating the particles obtained by sublimating at a temperature of 200° C. to 1000° C. for 10 minutes to 5 hours.