Filter material
Provided is a filter material which can enhance the particle holding capacity of a filter while keeping the particle capture efficiency thereof and which thus ensures a prolonged filter life. The present invention pertains to a filter material comprising a spun lace nonwoven fabric which contains a thermoplastic synthetic filament nonwoven fabric as the intermediate layer.
1. A filter material for vehicle fuel, comprising a spun lace nonwoven fabric which contains a thermoplastics synthetic filament nonwoven fabric as an intermediate layer,
wherein the thermoplastic synthetic filament nonwoven fabric as the intermediate layer is treated with a hydrophilic agent and is a spunbond nonwoven fabric having a fiber diameter of 5 to 30 μm and a basis weight of 20 to 160 g/m 2 , and a layer on one side of the spunbond nonwoven fabric is composed of staple fibers with a fiber diameter of 2 to 15 μm and a basis weight of 30 to 100 g/m 2 , while a layer on a second side is composed of staple fibers with a fiber diameter of 7 to 25 μm and a basis weight of 50 to 200 g/m 2 ,
wherein the fiber diameter of the staple fibers used in the layer on the one side is smaller than the fiber diameter of the staple fibers used in the layer on the second side, and
wherein the spun lace nonwoven fabric is a nonwoven fabric having the staple fibers formed into a web and the fibers tangled with the spunbond nonwoven fabric, by a high-pressure water jet of a high-pressure columnar stream.
2. A filter material according to claim 1 , wherein the staple fibers having a fiber diameter of 2 to 15 μm and a basis weight of 30 to 100 g/m 2 have an aspect ratio (L/D) of between 200 and 4000 wherein their fiber length is L and fiber diameter is D, and the staple fibers having a fiber diameter of 7 to 25 μm and a basis weight of 50 to 200 g/m 2 also have an aspect ratio (L/D) of between 200 and 4000 wherein their fiber length is L and fiber diameter is D.
3. A filter material according to claim 1 , which is further layered with a spunbond nonwoven fabric that has been pretreated with a water jet, as a pretreatment layer.
4. A filter material according to any one of claim 1 , 2 or 3 , which is capable of capturing at least 90% of particles of 30 μm and greater, and which has a filter life of at least 30 minutes as measured by a method pursuant to JIS-B-8356-8.
5. A filter material according to any one of claim 1 , 2 or 3 , which is capable of capturing at least 90% of particles of 20 μm and greater, and which has a filter life of at least 25 minutes as measured by a method pursuant to JIS-B-8356-8.
6. A filter material according to any one of claim 1 , 2 or 3 , which is capable of capturing at least 90% of particles of 10 μm and greater, and which has a filter life of at least 20 minutes as measured by a method pursuant to JIS-B-8356-8.
7. A filter material having a monofilament woven fabric with a fiber diameter of 30 μm to 170 μm layered on the one side of a filter material according to any one of claim 1 , 2 or 3 .
8. A filter for vehicle fuel, obtained by heat sealing edge perimeters on the second side of a filter material according to any one of claim 1 , 2 or 3 to produce a pouch form.
9. A filter for vehicle fuel formed by heat sealing edge perimeters of a filter material having a monofilament woven fabric with a fiber diameter of 30 μm to 170 μm layered on the one side of a filter material according to any one of claim 1 , 2 and or 3 , to form a pouch form.