Lithium metal doped electrodes for lithium-ion rechargeable chemistry
An embodiment of the invention combines the superior performance of a polyvinylidene difluoride (PVDF) or polyethyleneoxide (POE) binder, the strong binding force of a styrene-butadiene (SBR) binder, and a source of lithium ions in the form of solid lithium metal powder (SLMP) to form an electrode system that has improved performance as compared to PVDF/SBR binder based electrodes. This invention will provide a new way to achieve improved results at a much reduced cost.
1. A composition of matter comprising:
a styrene-butadiene rubber (SBR) polymer binder;
polymer coated active material particles; and
a stabilized lithium metal powder.
2. A method of preparing a composition of matter comprising a styrene-butadiene rubber (SBR) polymer binder, polymer coated active material particles, and stabilized lithium metal powder comprising:
providing the polymer coated active material particles and the stabilized lithium metal powder;
mixing the polymer coated active material particles and stabilized lithium metal powder in a SBR polymer binder solution; and
evaporating the solution to form the composition of matter.
3. The method of claim 2 , wherein the solution comprises an organic solvent.
4. The method of claim 3 , wherein the organic solvent comprises toluene.
5. The composition of matter of claim 1 wherein the active material particles comprise one or more anode materials.
6. The composition of matter of claim 5 wherein the anode materials comprise at least one of graphite, silicon, or tin.
7. The composition of matter of claim 1 wherein the active material particles comprise one or more cathode materials.
8. The composition of matter of claim 7 wherein the cathode materials comprise at least one of LiCoO 2 , LiMnO 2 , LiFePO 4 , MnO 2 , or nickel manganese cobalt.
9. The composition of matter of claim 1 wherein the polymer coating comprises one or more of polyvinylidene difluoride or polyethyleneoxide.
10. The composition of matter of claim 1 wherein the polymer coating comprises polyvinylidene difluoride (PVDF) and the active material particles comprise graphite.
11. The composition of matter of claim 10 wherein the PVDF ranges from approximately 10-0.0001% by weight of the graphite.
12. The composition of matter of claim 10 wherein the PVDF ranges from approximately 0.75-3% by weight of the graphite.
13. The composition of matter of claim 10 wherein the PVDF is approximately 1% by weight of the graphite.
14. The method of claim 2 further comprising adding a conductive additive to the polymer coated active material particles, stabilized lithium metal powder and SBR polymer binder solution prior to evaporating the solution.
15. The method of claim 14 wherein the conductive additive comprises one or more of acetylene black or carbon fiber.
16. A composition of matter comprising:
a non-polyvinylidene difluoride (PVDF) binder comprising styrene-butadiene rubber (SBR) polymer; and
PVDF coated graphite particles, wherein the SBR polymer and PVDF are unmixed.
17. The composition of matter of claim 16 , wherein the PVDF coated graphite particles do not operate as the binder.
18. The composition of matter of claim 16 , further comprising stabilized lithium metal powder.