Lithium ion secondary battery electrode, method of manufacturing the same, and lithium ion secondary battery

1. A lithium ion secondary battery electrode comprising:

a non-fluorinated polymer;

an active material;

a thickener; and

a conductive auxiliary agent,

wherein an elution ratio of the non-fluorinated polymer in an electrolytic solution solvent at 60° C. is equal to or less than 1.0 mass %, and

a swelling ratio of the non-fluorinated polymer in the electrolytic solution solvent at 60° C. is equal to or more than 10 mass % and equal to or less than 50 mass %.

2. The lithium ion secondary battery electrode according to claim 1 ,

wherein a glass transition temperature of the non-fluorinated polymer is equal to or higher than −10° C. and equal to or lower than 30° C.

3. The lithium ion secondary battery electrode according to claim 1 ,

wherein the non-fluorinated polymer contained in the lithium ion secondary battery electrode is formed of latex particles containing the non-fluorinated polymer.

4. The lithium ion secondary battery electrode according to claim 3 ,

wherein a part of the latex particles is attached on a surface of the lithium ion secondary battery electrode.

5. The lithium ion secondary battery electrode according to claim 3 ,

wherein a ratio of an average particle size of the active material to an average particle size of the latex particles is equal to or more than 50 and equal to or less than 200.

6. The lithium ion secondary battery electrode according to claim 1 ,

wherein the non-fluorinated polymer is a polymer obtained by polymerizing an ethylenically unsaturated monomer mixture containing

(a) a carboxyl group-containing unsaturated monomer,

(b) an unsaturated carboxylic acid ester monomer,

(c) an unsaturated monomer other than the (a) and the (b), and

(d) an internal cross-linking agent, and

when a total amount of the ethylenically unsaturated monomer mixture is 100 mass %,

a used amount of the (a) is equal to or more than 0.1 mass % and equal to or less than 10 mass %,

a used amount of the (b) is equal to or more than 20 mass % and equal to or less than 84.8 mass %,

a used amount of the (c) is equal to or more than 15 mass % and equal to or less than 70 mass %, and

a used amount of the (d) is equal to or more than 0.05 mass % and equal to or less than 10 mass %.

7. The lithium ion secondary battery electrode according to claim 1 ,

wherein when a total amount of an active material layer containing the non-fluorinated polymer, the active material, the thickener, and the conductive auxiliary agent is 100 parts by mass,

a content of the non-fluorinated polymer is equal to or more than 0.5 parts by mass and equal to or less than 3.0 parts by mass,

a content of the active material is equal to or more than 93 parts by mass and equal to or less than 98.9 parts by mass,

a content of the thickener is equal to or more than 0.5 parts by mass and equal to or less than 2.0 parts by mass, and

a content of the conductive auxiliary agent is equal to or more than 0.1 parts by mass and equal to or less than 2.0 parts by mass.

8. A method of manufacturing the lithium ion secondary battery electrode according to claim 1 , the method comprising:

a step of mixing the non-fluorinated polymer, the active material, the thickener, and the conductive auxiliary agent with each other to prepare a slurry;

a step of adjusting a pH of the slurry to a range equal to or higher than 3.0 and equal to or lower than 7.0; and

a step of coating the slurry on a current collector and drying the slurry to form the active material layer on the current collector.

9. The method of manufacturing the lithium ion secondary battery electrode according to claim 8 ,

wherein the pH of the slurry is adjusted with an organic acid.

10. The method of manufacturing the lithium ion secondary battery electrode according to claim 9 ,

wherein the organic acid is a polyvalent carboxylic acid.

11. The method of manufacturing the lithium ion secondary battery electrode according to claim 8 ,

wherein after the thickener and the conductive auxiliary agent are mixed with each other to obtain a mixture, the mixture is further mixed with the non-fluorinated polymer and the active material to prepare the slurry.

12. A lithium ion secondary battery which is manufactured using the lithium ion secondary battery electrode according to claim 1 .