Lithium nickel cobalt manganese oxide positive active material having concentration gradient of nickel, cobalt, and manganese and precursor thereof and preparation methods

1. A precursor of a modified ternary material for a lithium ion battery positive electrode material, wherein the precursor has a composition of the following molecular formula: Ni 1/3 Co 1/3 Mn 1/3 (OH) 2 ;

and consists of three layers, wherein:

an inner layer of the precursor is a first ternary material with a first cobalt content of greater than ⅓ and identical first nickel and first manganese contents, and the molecular formula of said inner layer of the precursor is: (Ni 1/3−x Co 1/3+2x Mn 1/3−x )(OH) 2 , where 0<x <⅓;

an outer layer of the precursor is a second ternary material with a second cobalt content of greater than 0 to ⅓ and equal second nickel and second manganese contents, and the molecular formula of said outer layer of the precursor is: (Ni 0.5−y Co 2y Mn 0.5−y )(OH) 2 , where 0<y<⅙; and

an intermediate layer of the precursor is a concentration-gradient composite material of the first ternary material of the inner layer and the second ternary material of the outer layer of the precursor.

2. A modified ternary material for a lithium ion battery positive electrode material having the precursor of claim 1 .

3. A process for preparing a precursor of a modified ternary material for a lithium ion battery positive electrode material, wherein the particular steps are as follows:

(1) adding a ternary salt solution A of nickel, cobalt and manganese into a reaction kettle at a certain rate, wherein the molar ratio of Ni:Co:Mn =(⅓−x):(⅓+2x):(⅓−x), where 0<x<⅓, carrying out a coprecipitation reaction with an alkali solution to obtain a first solid-liquid mixture, the molecular formula of a first precipitated solid portion of the first solid-liquid mixture being (Ni 1/3−x Co 1/3+2x Mn 1/3−x )(OH) 2 , where 0<x <⅓, so as to form an inner layer part of the precursor;

(2) adjusting a flow rate of the alkali solution during the addition of the ternary salt solution A and during an addition of a ternary salt solution B of nickel, cobalt and manganese to keep a pH value of a solution in the reaction kettle between 10-12;

first, continuing the addition of the ternary salt solution A of nickel, cobalt and manganese into the reaction kettle at a decreasing rate with a decrement of 100-1,000 ml per hour, and at the same time, adding the ternary salt solution B of nickel, cobalt and manganese into the reaction kettle at an increasing rate with a increment of 100-1,000 ml per hour from zero, wherein the molar ratio of the ternary salt solution B is Ni:Co:Mn =(0.5−y):2y:(0.5−y), where 0<y<⅙; so as to form an intermediate layer part of the above precursor which connects the inner layer and an outer layer and has a concentration gradient in the precursor;

(3) when the injection speed of the ternary salt solution A of nickel, cobalt and manganese has decreased to zero, continuing the injection of the ternary salt solution B until a predetermined amount of the ternary salt solution B has been added into the reaction kettle with a constant speed at a certain rate, so as to form the outer layer of the precursor coated outside of the intermediate layer part of the precursor; and

(4) separating a second precipitated solid from a second solid-liquid mixture after the reaction in step (3) is completed by means of centrifugal filtration, washing the same to be neutral, and oven-drying the same at 60° C.-200° C. for 4-10 h; the general molecular formula of the second precipitated solid obtained being (Ni 1/3 Co 1/3 Mn 1/3 )(OH) 2 , and the second precipitated solid being the precursor of the modified ternary material.

4. A process for preparing a modified ternary material for a lithium ion battery positive electrode material, wherein the modified ternary material includes a precursor that has a composition of the following molecular formula: Ni 1/3 Co 1/3 Mn 1/3 (OH) 2 ;

and consists of three layers, wherein:

an inner layer of the precursor is a first ternary material with a first cobalt content of greater than ⅓ and identical first nickel and first manganese contents, and the molecular formula of said inner layer of the precursor is: (Ni 1/3−x Co 1/3+2x Mn 1/3−x )(OH) 2 , where 0<x<⅓;

an outer layer of the precursor is a second ternary material with a second cobalt content of 0 to ⅓ and equal second nickel and second manganese contents, and the molecular formula of said outer layer of the precursor is: (Ni 0.5−y Co 2y Mn 0.5−y )(OH) 2 , where 0<y<⅙; and

an intermediate layer of the precursor is a concentration-gradient composite material of the first ternary material and the second ternary material of the inner layer and the outer layer of the precursor, and wherein the modified ternary material is prepared by crushing the precursor obtained by the preparation process for a precursor of claim 3 , then mixing the same with a lithium source and calcining, wherein mixing the powder of said precursor with the lithium source and calcining at 300° C.-1,200° C. for 8-30 h forms the modified ternary material.

5. The process for preparing a modified ternary material according to claim 4 , wherein said lithium source is lithium carbonate or lithium hydroxide.

6. A process for preparing a modified ternary material wherein the particular steps are as follows:

first, obtaining a precursor of a modified ternary material with a general molecular formula of (Ni 1/3 Co 1/3 Mn 1/3 )(OH) 2 and having three layers, wherein:

an inner layer of the precursor is a first ternary material with a first cobalt content of greater than ⅓ and identical first nickel and first manganese contents, and the molecular formula of said inner layer of the precursor is: (Ni 1/3−x Co 1/3+2x Mn 1/3−x )(OH) 2 , where 0<x<⅓;

an outer layer of the precursor is a second ternary material with a second cobalt content of 0 to ⅓ and equal second nickel and second manganese contents, and the molecular formula of said outer layer of the precursor is: (Ni 0.5 −y Co 2y Mn 0.5−y )(OH) 2 , where 0<y<⅙; and

an intermediate layer of the precursor is a concentration-gradient composite material of the first ternary material and the second ternary material of the of the inner layer and the outer layer of the precursor and wherein the modified ternary material is prepared by crushing the precursor obtained by the preparation process for a precursor of claim 3 , then mixing the same with a lithium source and calcining, wherein mixing the powder of said precursor with the lithium source and calcining at 300° C.-1,200° C. for 8-30 h forms the modified ternary material; and

wherein the mixing the precursor with the lithium source is at a molar ratio of 1:1 to 1:1.2, wherein the calcining is a multi-stage calcination in a muffle furnace, with the calcination temperature of 300° C.-1,200° C. and the calcination time of 8-30 h, and after the multi-stage calcination, cooling, crushing and sieving to obtain the modified ternary material, wherein said lithium source is lithium carbonate or lithium hydroxide.

7. A process for preparing a modified ternary material for a lithium ion battery positive electrode material, wherein the modified ternary material includes a precursor that has a composition of the following molecular formula: Ni 1/3 Co 1/3 Mn 1/3 (OH) 2 ;

and consists of three layers, wherein:

an inner layer of the precursor is a first ternary material with a first cobalt content of greater than ⅓ and identical first nickel and first manganese contents, and the molecular formula of said inner layer of the precursor is: (Ni 1/3−x Co 1/3+2x Mn 1/3−x )(OH) 2 , where 0<x<⅓;

an outer layer of the precursor is a second ternary material with a second cobalt content of 0 to ⅓ and equal second nickel and second manganese contents, and the molecular formula of said outer layer of the precursor is: (Ni 0.5−y Co 2y Mn 0.5−y )(OH) 2 , where 0<y<⅙; and

an intermediate layer of the precursor is a concentration-gradient composite material of the first ternary material and the second ternary material of the inner layer and the outer layer of the precursor, and wherein the modified ternary material is prepared by crushing the precursor, then mixing the same with a lithium source and calcining, wherein mixing the powder of said precursor with the lithium source and calcining at 300° C.-1,200° C. for 8-30 h forms the modified ternary material.