Structural adhesive sheet specifically for use in a mirror base of an automobile interior rear-view mirror and a method for producing the same
The present invention provides a structural adhesive sheet specifically for use in a mirror base of an automobile interior rear-view mirror and a method for producing the same, said structural adhesive sheet comprises in parts by weight of 20-100 parts of a nitrile-butadiene rubber, 10-70 parts of a partially cured polysulfide adhesive, 5-40 parts of a bisphenol A type epoxy resin, 0.1-2.5 parts of a crosslinking agent, 0.2-2.5 parts of a softening agent, 3-20 parts of a curing agent, 1-10 parts of an accelerator, 20-100 parts of an inorganic filler, and 0.1-3.0 parts of a silane coupling agent. The structural adhesive sheet of the present invention is obtained by subjecting the above-mentioned components to a compounding process and an extrusion film forming process. The advantages of said structural adhesive sheet include good film-forming property, and simple curing process, while having high structural strength, good toughness, and excellent heat-resistance and cold-resistance after cured.
1. A structural adhesive sheet specifically for use in the mirror base of an automobile interior rear-view mirror, wherein said structural adhesive sheet comprises in parts by weight of 20˜100 parts of a nitrile-butadiene rubber, 10˜70 parts of a partially cured polysulfide adhesive, 5˜40 parts of a bisphenol A epoxy resin, 0.1˜2.5 parts of a crosslinking agent, 0.2˜2.5 parts of a softening agent, 3˜20 parts of a curing agent, 1˜10 parts of an accelerator, 20˜100 parts of an inorganic filler, 0.1˜3.0 parts of a silane coupling agent, and 0˜60 parts of a modified epoxy resin, wherein said partially cured polysulfide adhesive is a curing agent-deficient two-component polysulfide adhesive.
2. The structural adhesive sheet specifically for use in the mirror base of an automobile interior rear-view mirror according to claim 1 , wherein said modified epoxy resin is one or two of a polyurethane-modified epoxy resin and a butyronitrile-modified epoxy resin.
3. The structural adhesive sheet specifically for use in the mirror base of an automobile interior rear-view mirror according to claim 1 , wherein said softening agent is one or two of stearic acid and glycerin.
4. The structural adhesive sheet specifically for use in the mirror base of an automobile interior rear-view mirror according to claim 1 , wherein said curing agent is one or two of dicyandiamide curing agent and a modified dicyandiamide curing agent.
5. The structural adhesive sheet specifically for use in the mirror base of an automobile interior rear-view mirror according to claim 1 , wherein said accelerator is one or two of an imidazole epoxy resin accelerator and a urea epoxy resin accelerator.
6. The structural adhesive sheet specifically for use in the mirror base of an automobile interior rear-view mirror according to claim 1 , wherein said crosslinking agent is one or two of sulfur powder and zinc oxide.
7. The structural adhesive sheet specifically for use in the mirror base of an automobile interior rear-view mirror according to claim 1 , wherein said inorganic filler is one or more of aluminum oxide powder, nanometer sized calcium carbonate, fumed silica, and carbon black.
8. The structural adhesive sheet specifically for use in the mirror base of an automobile interior rear-view mirror according to claim 1 , wherein said silane coupling agent is one or two of γ-glycidoxypropyl trimethoxy silane and γ-thiopropyl trimethoxy silane.
9. A method for producing the structural adhesive sheet specifically for use in the mirror base of an automobile interior rear-view mirror according to any one of the preceding claims, which comprises the steps of:
(1) adding in proportions a nitrile-butadiene rubber, an epoxy resin, a crosslinking agent and a softening agent into a kneader, and subjecting them to stirring at medium speed for 50˜200 min for thorough mixing, meanwhile the rubber temperature is controlled and maintained less than 80° C.;
(2) adding an inorganic filler into the kneader, and subjecting it to stirring at low speed for 50˜100 min, meanwhile the rubber temperature is controlled and maintained less than 80° C.;
(3) adding a curing agent, an accelerator and a silane coupling agent into the kneader, and subjecting them to stirring at low speed for 60˜100 min, meanwhile the rubber temperature is controlled and maintained less than 50° C. for thorough mixing to obtain the desired structural adhesive; and
(4) using a continuous extrusion film forming machine, the structural adhesive obtained in step (3) is made into a adhesive sheet having a uniform thickness and a smooth surface, which is then formed into a roll by die cutting.
10. The method according to claim 9 , wherein 20˜100 parts of a nitrile-butadiene rubber, 10˜70 parts of a partially cured polysulfide adhesive, 5˜40 parts of a bisphenol A epoxy resin, 0.1˜2.5 parts of a crosslinking agent, 0.2˜2.5 parts of a softening agent, 3˜20 parts of a curing agent, 1˜10 parts of an accelerator, 20˜100 parts of an inorganic filler and 0.1˜3.0 parts of a silane coupling agent are used in said method, and the amount is expressed in parts by weight.
11. The method according to claim 9 , which further comprises adding 0˜60 parts by weight of a modified epoxy resin in step (1).