Titanium oxide-containing aluminum oxide particles based on corundum melted in an electric arc furnace from calcined alumina, and a method for the production thereof
Titanium oxide-containing aluminum oxide particles are based on corundum melted in an electric arc furnace from calcined alumina. The particles may have an aluminum oxide content of less than 97.0% by weight, a titanium oxide content ranging from 1.3% by weight to 1.8% by weight, and a zirconium oxide content of ranging from 0.02% by weight to 0.1% by weight. The aluminum oxide particles may have an arithmetic mean compactness of less than 0.8.
1. Titanium oxide-containing aluminium oxide particles based on corundum melted in an electric arc furnace from calcined alumina, the aluminium oxide particles comprising:
Al 2 O 3 greater than 97.0% by weight,
Fe 2 O 3 0.05% by weight to 0.2% by weight,
SiO 2 0.1% by weight to 0.5% by weight,
TiO 2 1.3% by weight to 1.8% by weight,
ZrO 2 0.02% by weight to 0.1% by weight,
Na 2 O 0.05% by weight to 2.0% by weight, and
other oxides less than 0.2% by weight,
in each case based on the total weight of the melted corundum, characterized in that the ratio of the sum of the percentages by weight of Fe 2 O 3 , SiO 2 , and ZrO 2 to the percentage by weight of Na 2 O is less than 10.
2. The aluminum oxide particles according to claim 1 , characterized in that the aluminum oxide particles encompass an arithmetic mean compactness of less than 0.8, wherein compactness is solidity (S), which is determined via image analyzing software and which is defined as a ratio of actual particle surface (A) to convex particle surface (B).
3. A method for producing at least one of abrasives and fireproof materials, the method comprising:
providing the aluminum oxide particles of claim 1 ; and
forming at least one of the abrasives and the fireproof materials comprising the aluminum oxide containing particles.
4. A method for producing at least one of abrasives and fireproof materials, the method comprising:
providing the aluminum oxide particles of claim 2 ; and
forming at least one of the abrasives and the fireproof materials comprising the aluminum oxide containing particles.
5. A method for producing titanium oxide-containing aluminum oxide particles based on corundum melted in an electric arc furnace from alumina, comprising:
melting a mixture of Al 2 O 3 , TiO 2 , SiO 2 , and Fe 2 O 3 containing raw materials in the presence of iron filings and charcoal in the electric light arc furnace,
cooling the melted mixture to obtain a solid block, which consists substantially of corundum, and
comminuting and processing of the corundum block into defined particle size distributions, wherein raw materials, which contain small quantities of contaminations, are thereby used as raw materials, wherein the raw materials are selected from the group consisting of calcined alumina, rutile, ilmenite, and iron ore in such quantities that titanium oxide-containing aluminum oxide particles comprise the chemical composition
Al 2 O 3 less than 97.0% by weight,
Fe 2 O 3 0.05% by weight to 0.2% by weight,
SiO 2 0.1% by weight to 0.5% by weight,
TiO 2 1.3% by weight to 1.8% by weight,
ZrO 2 0.02% by weight to 0.1% by weight,
Na 2 O 0.05% by weight 2.0% by weight, and
other oxides less than 0.2% by weight,
and an arithmetic mean compactness of less than 0.8 are formed, wherein compactness is solidity (S), which is determined via image analyzing software and which is defined as a ratio of actual particle surface (A) to convex particle surface (B).