Chromium-free paint composition and paint films obtained by coating same
To provide a chromium-free paint composition which can provide paint films which are excellent in terms of corrosion resistance on the edge surfaces, scratched surfaces and worked parts of a pre-coated steel sheet, and the paint films which can be obtained by coating this chromium-free paint composition. A chromium-free paint composition which includes paint film-forming resin (A), anti-rust pigment (B), comprising at least one type of amorphous MgO—V 2 O 5 -based compound, and crosslinking agent (C) which is characterized in that the mass content proportion of the aforementioned anti-rust pigment (B) is from 10 to 80 mass % with respect to the sum of the resin solid fraction mass of the aforementioned paint film-forming resin (A) and the aforementioned crosslinking agent (C), and the overall eluted ion content in a 10% aqueous solution of the aforementioned anti-rust pigment (B) is from 10 ppm to 100 ppm.
1. A chromium-free paint composition comprising a paint film forming resin (A), an anti-rust pigment (B) that comprises at least one amorphous MgO—V 2 O 5 compound, and a crosslinking agent (C), wherein the mass content proportion of the anti-rust pigment (B) is in the range of from 20 to 80 mass % with respect to the sum of the resin solid fraction mass of the paint film-forming resin (A) and the crosslinking agent (C), the mol ratio of magnesium with respect to vanadium is in the range of from 1.7 to 5.0, and wherein the overall eluted ion content in a 10% aqueous solution of the anti-rust pigment (B) is from 10 ppm to 100 ppm and the pH of the 10% aqueous solution is in the range of 9.0 to 11.0, and wherein the amorphous MgO—V 2 O 5 is produced by mixing and reacting magnesium-containing compounds and vanadium-containing compounds in water, drying, and pulverization.
2. The chromium-free paint composition according to claim 1 , wherein the magnesium compound which is a raw material for production of the amorphous MgO—V 2 O 5 compound is at least one magnesium-containing compound selected from the group consisting of magnesium oxide and magnesium carbonate.
3. The chromium-free paint composition according to claim 1 , wherein the vanadium-containing compound which is a raw material for production of the amorphous MgO—V 2 O 5 compound is vanadium pentoxide.
4. The chromium-free paint composition according to claim 1 , wherein the paint film-forming resin (A) is at least one paint film-forming resin selected from the group consisting of hydroxyl group-containing epoxy resins of number average molecular weight from 400 to 10,000 and hydroxyl-group containing polyester resins of number average molecular weight from 500 to 20,000.
5. The chromium-free paint composition according to claim 1 , wherein the crosslinking agent (C) is at least one crosslinking agent selected from the group consisting of blocked polyisocyanate compounds and amino resins, and wherein the solid fraction mass content proportion of the crosslinking agent (C) is from 3 to 60 mass % with respect to the solid fraction mass of the paint film-forming resin (A).
6. A paint film that has been obtained by coating the chromium-free paint composition according to 1.
7. A pre-coated steel sheet comprising a steel sheet and the chromium-free paint composition according to claim 1 coated thereon.
8. A chromium-free paint composition comprising a paint film forming resin (A), an anti-rust pigment (B) that comprises at least one amorphous MgO—V 2 O 5 compound, and a crosslinking agent (C), wherein the mass content proportion of the anti-rust pigment (B) is in the range of from 10 to 80 mass % with respect to the sum of the resin solid fraction mass of the paint film-forming resin (A) and the crosslinking agent (C), and wherein the overall eluted ion content in a 10% aqueous solution of the anti-rust pigment (B) is from 10 ppm to 100 ppm, and wherein anti-rust pigment (B) is used without conjoint use of other anti-rust pigments, and wherein the amorphous MgO—V 2 O 5 is produced by mixing and reacting magnesium-containing compounds and vanadium-containing compounds in water, drying, and pulverization.
9. A chromium-free paint composition comprising a paint film forming resin (A), an anti-rust pigment (B) that comprises at least one amorphous MgO—V 2 O 5 compound, and a crosslinking agent (C), wherein the mass content proportion of the anti-rust pigment (B) is in the range of from 10 to 80 mass % with respect to the sum of the resin solid fraction mass of the paint film-forming resin (A) and the crosslinking agent (C), and wherein the overall eluted ion content in a 10% aqueous solution of the anti-rust pigment (B) is from 10 ppm to 100 ppm, and wherein anti rust pigment (B) the amorphous MgO—V 2 O 5 is produced by mixing and reacting magnesium-containing compounds and vanadium-containing compounds in water, drying, and pulverization.
10. The chromium-free paint composition according to claim 9 , wherein the anti-rust pigment (B) has a mol ratio of magnesium to vanadium of from 1.7 to 5.0.