High-manganese hot-rolled galvanized steel sheet and manufacturing method thereof
A high-manganese hot-rolled galvanized steel sheet having no surface defects and improved galvanizing and alloying characteristics is manufactured by using a high-manganese hot-rolled steel sheet. Provided are the high-manganese hot-rolled galvanized steel sheet and a method of manufacturing the high-manganese hot-rolled galvanized steel sheet. The high-manganese hot-rolled galvanized steel sheet includes: a hot-rolled steel sheet including 5 wt % to 35 wt % manganese; and a zinc coating layer formed on the hot-rolled steel sheet, wherein an internal oxide layer is formed in an internal region of the hot-rolled steel sheet facing the zinc coating layer.
1. A high-manganese hot-rolled galvanized steel sheet comprising:
a hot-rolled steel sheet comprising 5 wt % to 35 wt % manganese; and
a zinc coating layer formed on the hot-rolled steel sheet,
wherein an internal oxide layer is formed in an internal region of the hot-rolled steel sheet facing the zinc coating layer,
wherein the internal oxide layer has a thickness of 1 μm to 5 μm, and
wherein an interface between the zinc coating layer and the hot-rolled steel sheet includes a Fe—Mn—Al—Zn interfacial inhibition layer.
2. The high-manganese hot-rolled galvanized steel sheet of claim 1 , wherein the hot-rolled steel sheet comprises, by wt %, C: 0.1% to 1.5%, Mn: 5% to 35%, Si: 0.1% to 3%, Al: 0.01% to 6%, Ni: 0.1% to 1.0%, Cr: 0.1% to 0.4%, Sn: 0.01% to 0.2%, Ti: 0.01% to 0.2%, B: 0005% to 0.006%, and the balance of Fe and inevitable impurities.
3. The high-manganese hot-rolled galvanized steel sheet of claim 1 , wherein the zinc coating layer is formed by a hot-dip galvanizing method or a hot-dip galvannealing method.