Oxygen-enriched Ti-6AI-4V alloy and process for manufacture
A titanium alloy comprising an elevated level of oxygen is disclosed. The alloy may have 5.5 to 6.75 weight percent of aluminum, 3.5 to 4.5 weight percent of vanadium, 0.21 to 0.30 weight percent of oxygen, and up to 0.40% of weight percent of iron. The alloy may also have a minimum ultimate tensile strength of 130,000 psi, a minimum tensile yield strength of 120,000 psi, and a minimum ductility of 10% elongation. Also disclosed is a method for manufacturing components having the aforementioned alloy.
1. A titanium alloy, comprising:
5.5 to 6.75 weight percent of aluminum, 3.5 to 4.5 weight percent of vanadium, up to 0.40 weight percent of iron, and 0.21 to 0.30 weight percent of oxygen, and having a minimum ultimate tensile strength of at least about 130,000 psi, a minimum tensile yield strength of at least about 120,000 psi, a minimum ductility of at least about 10% elongation, and wherein a microstructure of the titanium alloy includes an average grain size of at least 8 microns.
2. The titanium alloy of claim 1 , wherein the microstructure includes a plurality of voids totaling about 2% by volume.
3. The titanium alloy of claim 1 , wherein the titanium alloy has a minimum density of at least about 98% of theoretical density.
4. A titanium alloy material consisting essentially of:
titanium;
about 5.50 to about 6.75 weight percent of aluminum;
about 3.50 to about 4.50 weight percent of vanadium;
less than about 0.40 weight percent of iron; and
greater than about 0.21 weight percent of oxygen,
wherein the titanium alloy has a minimum ultimate tensile strength of at least about 130,000 psi, a minimum tensile yield strength of at least about 120,000 psi, a minimum ductility of at least about 10% elongation, and wherein an average grain size of the titanium alloy is at least about 8 microns.
5. The titanium alloy of claim 4 , wherein the titanium alloy includes a plurality of voids totaling less than about 2% by volume.
6. The titanium alloy of claim 4 , wherein the titanium alloy has a minimum density of at least about 98% of theoretical density.